Steel 18CrNiMo7-6 Heat Treated (+TH)
Heat-treated state
EN 18CrNiMo7-6
Heat Treated (+TH) = heat Treated to Hardness Range
EN 10084 delivery condition treated to a controlled Brinell band (~179–229 HB) so bar and forging stock machines predictably before carburizing.
Values for the Heat Treated (+TH) condition
Other 18CrNiMo7-6 tempers and conditions
18CrNiMo7-6 is listed in 9 conditions; see the grade overview at 18CrNiMo7-6.
- Spheroidized (+AC)
- Annealed
- Heat Treated (+TH)
- High Shearability (+S)
- Hot Rolled
- Normalized
- Cold Drawn
- Q&T 28-32 HRC
- Carburized 58-62 HRC
Compare all 9 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
Spheroidize Annealed | EN 10084 soft-annealed condition with globular carbides, giving the lowest hardness and the best cold formability for extrusion, upsetting and heavy machining before carburizing. | 360 | 590 | 22 | 175 HB | 8 % IACS |
AnnealedDefault soft (spheroidize/sub-critical) annealed bar, ≤229 HB | Standard delivery condition for machining of gear blanks before carburizing. | 370 | 640 | 20 | 200 HB | — |
Heat Treated (+TH)This page Heat Treated to Hardness Range | EN 10084 delivery condition treated to a controlled Brinell band (~179–229 HB) so bar and forging stock machines predictably before carburizing. | 450 | 700 | 17 | 205 HB | 8 % IACS |
Treated for High Shearability | EN 10084 condition softened only enough to cap hardness (~≤255 HB) so bar can be cold-sheared into blanks without cracking the shear tooling. | 500 | 780 | 15 | 21 HRC | 8 % IACS |
untreated bar or forging | Mill delivery for stock that will be normalized or annealed by the gear maker. | 500 | 800 | 14 | 23 HRC | 7.8 % IACS |
+N, 870–900 °C air cooled | Uniform fine-grained structure for forgings prior to machining and carburizing. | 550 | 850 | 15 | 24 HRC | 7.8 % IACS |
+C, annealed then cold drawn bright bar | Small-diameter bright bar with tight tolerance for pinion shafts and automatic-lathe work. | 600 | 750 | 10 | 21 HRC | 7.8 % IACS |
Quenched and higher-temperature tempered core condition | Choose when the part is used as a through-hardened shaft rather than a carburized gear. | 800 | 980 | 14 | 30 HRC | — |
Carburized & Hardened | Final service condition for heavy-duty gears: hard wear-resistant case with compressive residual stress over a tough core. | 950 | 1,250 | 9 | 60 HRC | — |
What is 18CrNiMo7-6 Heat Treated (+TH)?
18CrNiMo7-6 Heat Treated (+TH) is 18CrNiMo7-6 heat treated to Heat Treated (+TH) — eN 10084 delivery condition treated to a controlled Brinell band (~179–229 HB) so bar and forging stock machines predictably before carburizing. 18CrNiMo7-6 Heat Treated (+TH) has a yield strength of 450 MPa (65.3 ksi) and a tensile strength of 700 MPa (102 ksi) — stronger than 52% of steel grades. Elongation at break is 17% and the elastic modulus is 210 GPa (30.5 Msi). 18CrNiMo7-6 Heat Treated (+TH) has a density of 7.85 g/cm³ (0.284 lb/in³), heavier than 56% of steel grades. It melts at 1,430°C (2,606 °F). Annealed is the default condition FabDigit quotes; Heat Treated (+TH) is available on request or by drawing note.
Advantages
- Polishes to a fine finish — 65/100, better than 78% of steel grades
Limitations
- Limited service temperature — 300°C (572 °F), worse than 78% of steel grades
- Poor heat conductor — 34 W/m·K (19.6 BTU/hr·ft·°F), worse than 77% of steel grades
18CrNiMo7-6 Heat Treated (+TH) properties
Typical room-temperature values for 18CrNiMo7-6 Heat Treated (+TH); 39 are specific to this condition. Other listed values are 18CrNiMo7-6 reference data and may not represent this condition. Bars are the position among steel grades.
Physical3
18CrNiMo7-6 Heat Treated (+TH) has a density of 7.85 g/cm³ (0.284 lb/in³), heavier than 56% of steel grades. It melts at 1,430°C (2,606 °F).
Mechanical15
18CrNiMo7-6 Heat Treated (+TH) has a yield strength of 450 MPa (65.3 ksi) and a tensile strength of 700 MPa (102 ksi) — stronger than 52% of steel grades. Elongation at break is 17% and the elastic modulus is 210 GPa (30.5 Msi).
Thermal6
18CrNiMo7-6 Heat Treated (+TH) is rated for continuous service to 300°C (572 °F). It conducts heat at 34 W/m·K (19.6 BTU/hr·ft·°F), worse than 77% of steel grades. Thermal expansion is 11.9 µm/m·K (6.61 µin/in·°F).
Electrical3
18CrNiMo7-6 Heat Treated (+TH) conducts electricity at 8 % IACS, better than 55% of steel grades.
Chemical & Environmental2
Corrosion resistance is not recommended (12/100), worse than 53% of steel grades.
Sustainability4
Producing a kilogram of 18CrNiMo7-6 Heat Treated (+TH) takes about 34 MJ of energy and emits 2.3 kg of CO₂ — more than 82% of steel grades. Typical recycled content is 30%.
Manufacturability8
18CrNiMo7-6 Heat Treated (+TH)'s machinability is fair (52/100, better than 52% of steel grades); weldability fair (45/100); formability fair (45/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with 18CrNiMo7-6 Heat Treated (+TH)
Is 18CrNiMo7-6 easy to machine?
Machine all gear geometry in the soft-annealed state (≈55% of 1212); after carburizing only grinding, honing or hard skiving with CBN is practical.
Can 18CrNiMo7-6 be welded?
Weldable only with care — preheat 200–250 °C, low-hydrogen consumables and immediate stress relief; never weld carburized surfaces.
Can 18CrNiMo7-6 be formed, bent or molded?
Hot forge at 1050–1150 °C then normalize; cold forming limited to annealed small-section bar with generous radii.
What surface finishes work on 18CrNiMo7-6?
Not anodizable — use phosphating, black oxide, oil or Zn-Ni plating (bake to avoid hydrogen embrittlement); shot peening of tooth roots markedly raises bending fatigue life.
18CrNiMo7-6 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| C | 0.15 – 0.21 | 0.18 |
| Si | ≤ 0.4 | 0.25 |
| Mn | 0.5 – 0.9 | 0.7 |
| P | ≤ 0.03 | |
| Smax; low-S (≤0.015) variants used for wind-turbine gears | ≤ 0.04 | |
| Cr | 1.5 – 1.8 | 1.65 |
| Mo | 0.25 – 0.35 | 0.3 |
| Ni | 1.4 – 1.7 | 1.55 |
| Fe | balance |
18CrNiMo7-6 Heat Treated (+TH) — frequently asked
What is 18CrNiMo7-6 Heat Treated (+TH) used for?
18CrNiMo7-6 Heat Treated (+TH) is typically used for wind-turbine gearbox gears, heavy industrial spur and helical gears, drive shafts and pinion shafts, planet carriers and planetary pinions, marine and rail gearbox components and bevel and hypoid gears. In short: premium gear-steel bar.
What is the yield strength of 18CrNiMo7-6 Heat Treated (+TH)?
18CrNiMo7-6 Heat Treated (+TH) has a typical yield strength of 450 MPa (65.3 ksi) and a tensile strength of 700 MPa (102 ksi) — stronger than 52% of steel grades. Strength varies by condition: see the 9 listed tempers.
Is 18CrNiMo7-6 Heat Treated (+TH) easy to machine?
Reasonably — machinability is rated fair (52/100, better than 52% of steel grades). Machine all gear geometry in the soft-annealed state (≈55% of 1212); after carburizing only grinding, honing or hard skiving with CBN is practical.
Can 18CrNiMo7-6 Heat Treated (+TH) be welded?
With care — weldability is rated fair (45/100). Weldable only with care — preheat 200–250 °C, low-hydrogen consumables and immediate stress relief; never weld carburized surfaces.
What surface finishes work on 18CrNiMo7-6 Heat Treated (+TH)?
Not anodizable — use phosphating, black oxide, oil or Zn-Ni plating (bake to avoid hydrogen embrittlement); shot peening of tooth roots markedly raises bending fatigue life.
Can 18CrNiMo7-6 Heat Treated (+TH) be formed, bent or molded?
Hot forge at 1050–1150 °C then normalize; cold forming limited to annealed small-section bar with generous radii.
What is the maximum service temperature of 18CrNiMo7-6 Heat Treated (+TH)?
18CrNiMo7-6 Heat Treated (+TH) is rated for continuous use to about 300°C (572 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Can FabDigit make parts in 18CrNiMo7-6 Heat Treated (+TH)?
Yes — 18CrNiMo7-6 Heat Treated (+TH) is available for CNC machining and sheet metal with instant online pricing. Upload a STEP file to get a price and a DFM check.
Sources
- EN 10084 — Case hardening steels: technical delivery conditions — CEN (2008)
- EN 10263-4 / EN ISO 683-3 case-hardening steel designations — CEN/ISO (2018)
- 18CrNiMo7-6 (1.6587) gear steel data sheet — Ovako / Böhler / Dörrenberg (2022)
- ASM Handbook Vol.1 — Properties and Selection: Irons, Steels — ASM International (1990)
- ASM Handbook Vol.4 — Heat Treating (carburizing of gear steels) — ASM International (1991)