Steel 18CrNiMo7-6 Cold Drawn
Supply condition
EN 18CrNiMo7-6
Small-diameter bright bar with tight tolerance for pinion shafts and automatic-lathe work.
Values for the Cold Drawn condition
Other 18CrNiMo7-6 tempers and conditions
18CrNiMo7-6 is listed in 9 conditions; see the grade overview at 18CrNiMo7-6.
- Spheroidized (+AC)
- Annealed
- Heat Treated (+TH)
- High Shearability (+S)
- Hot Rolled
- Normalized
- Cold Drawn
- Q&T 28-32 HRC
- Carburized 58-62 HRC
Compare all 9 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
Spheroidize Annealed | EN 10084 soft-annealed condition with globular carbides, giving the lowest hardness and the best cold formability for extrusion, upsetting and heavy machining before carburizing. | 360 | 590 | 22 | 175 HB | 8 % IACS |
AnnealedDefault soft (spheroidize/sub-critical) annealed bar, ≤229 HB | Standard delivery condition for machining of gear blanks before carburizing. | 370 | 640 | 20 | 200 HB | — |
Heat Treated to Hardness Range | EN 10084 delivery condition treated to a controlled Brinell band (~179–229 HB) so bar and forging stock machines predictably before carburizing. | 450 | 700 | 17 | 205 HB | 8 % IACS |
Treated for High Shearability | EN 10084 condition softened only enough to cap hardness (~≤255 HB) so bar can be cold-sheared into blanks without cracking the shear tooling. | 500 | 780 | 15 | 21 HRC | 8 % IACS |
untreated bar or forging | Mill delivery for stock that will be normalized or annealed by the gear maker. | 500 | 800 | 14 | 23 HRC | 7.8 % IACS |
+N, 870–900 °C air cooled | Uniform fine-grained structure for forgings prior to machining and carburizing. | 550 | 850 | 15 | 24 HRC | 7.8 % IACS |
Cold DrawnThis page +C, annealed then cold drawn bright bar | Small-diameter bright bar with tight tolerance for pinion shafts and automatic-lathe work. | 600 | 750 | 10 | 21 HRC | 7.8 % IACS |
Quenched and higher-temperature tempered core condition | Choose when the part is used as a through-hardened shaft rather than a carburized gear. | 800 | 980 | 14 | 30 HRC | — |
Carburized & Hardened | Final service condition for heavy-duty gears: hard wear-resistant case with compressive residual stress over a tough core. | 950 | 1,250 | 9 | 60 HRC | — |
What is 18CrNiMo7-6 Cold Drawn?
18CrNiMo7-6 Cold Drawn is 18CrNiMo7-6 supplied in the Cold Drawn condition — small-diameter bright bar with tight tolerance for pinion shafts and automatic-lathe work. 18CrNiMo7-6 Cold Drawn has a yield strength of 600 MPa (87 ksi) and a tensile strength of 750 MPa (109 ksi) — stronger than 77% of steel grades. Elongation at break is 10% and the elastic modulus is 210 GPa (30.5 Msi). 18CrNiMo7-6 Cold Drawn has a density of 7.85 g/cm³ (0.284 lb/in³), heavier than 56% of steel grades. It melts at 1,425°C (2,597 °F). Annealed is the default condition FabDigit quotes; Cold Drawn is available on request or by drawing note.
Advantages
- Polishes to a fine finish — 65/100, better than 78% of steel grades
- High strength — 600 MPa (87 ksi), better than 77% of steel grades
Limitations
- Limited ductility — 10%, worse than 91% of steel grades
- Limited service temperature — 300°C (572 °F), worse than 78% of steel grades
18CrNiMo7-6 Cold Drawn properties
Typical room-temperature values for 18CrNiMo7-6 Cold Drawn; 23 are specific to this condition. Other listed values are 18CrNiMo7-6 reference data and may not represent this condition. Bars are the position among steel grades.
Physical3
18CrNiMo7-6 Cold Drawn has a density of 7.85 g/cm³ (0.284 lb/in³), heavier than 56% of steel grades. It melts at 1,425°C (2,597 °F).
Mechanical15
18CrNiMo7-6 Cold Drawn has a yield strength of 600 MPa (87 ksi) and a tensile strength of 750 MPa (109 ksi) — stronger than 77% of steel grades. Elongation at break is 10% and the elastic modulus is 210 GPa (30.5 Msi).
Thermal6
18CrNiMo7-6 Cold Drawn is rated for continuous service to 300°C (572 °F). It conducts heat at 40 W/m·K (23.1 BTU/hr·ft·°F), worse than 64% of steel grades. Thermal expansion is 11.5 µm/m·K (6.39 µin/in·°F).
Electrical3
18CrNiMo7-6 Cold Drawn conducts electricity at 7.8 % IACS, worse than 57% of steel grades.
Chemical & Environmental2
Corrosion resistance is not recommended (12/100), worse than 53% of steel grades.
Sustainability4
Producing a kilogram of 18CrNiMo7-6 Cold Drawn takes about 32 MJ of energy and emits 2.3 kg of CO₂ — more than 70% of steel grades. Typical recycled content is 35%.
Manufacturability8
18CrNiMo7-6 Cold Drawn's machinability is good (60/100, better than 83% of steel grades); weldability fair (42/100); formability poor (30/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with 18CrNiMo7-6 Cold Drawn
Is 18CrNiMo7-6 easy to machine?
Machine all gear geometry in the soft-annealed state (≈55% of 1212); after carburizing only grinding, honing or hard skiving with CBN is practical.
Can 18CrNiMo7-6 be welded?
Weldable only with care — preheat 200–250 °C, low-hydrogen consumables and immediate stress relief; never weld carburized surfaces.
Can 18CrNiMo7-6 be formed, bent or molded?
Hot forge at 1050–1150 °C then normalize; cold forming limited to annealed small-section bar with generous radii.
What surface finishes work on 18CrNiMo7-6?
Not anodizable — use phosphating, black oxide, oil or Zn-Ni plating (bake to avoid hydrogen embrittlement); shot peening of tooth roots markedly raises bending fatigue life.
18CrNiMo7-6 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| C | 0.15 – 0.21 | 0.18 |
| Si | ≤ 0.4 | 0.25 |
| Mn | 0.5 – 0.9 | 0.7 |
| P | ≤ 0.03 | — |
| Smax; low-S (≤0.015) variants used for wind-turbine gears | ≤ 0.04 | — |
| Cr | 1.5 – 1.8 | 1.65 |
| Mo | 0.25 – 0.35 | 0.3 |
| Ni | 1.4 – 1.7 | 1.55 |
| Fe | balance | — |
18CrNiMo7-6 Cold Drawn — frequently asked
What is 18CrNiMo7-6 Cold Drawn used for?
18CrNiMo7-6 Cold Drawn is typically used for wind-turbine gearbox gears, heavy industrial spur and helical gears, drive shafts and pinion shafts, planet carriers and planetary pinions, marine and rail gearbox components and bevel and hypoid gears. In short: premium gear-steel bar.
What is the yield strength of 18CrNiMo7-6 Cold Drawn?
18CrNiMo7-6 Cold Drawn has a typical yield strength of 600 MPa (87 ksi) and a tensile strength of 750 MPa (109 ksi) — stronger than 77% of steel grades. Strength varies by condition: see the 9 listed tempers.
Is 18CrNiMo7-6 Cold Drawn easy to machine?
Reasonably — machinability is rated good (60/100, better than 83% of steel grades). Machine all gear geometry in the soft-annealed state (≈55% of 1212); after carburizing only grinding, honing or hard skiving with CBN is practical.
Can 18CrNiMo7-6 Cold Drawn be welded?
With care — weldability is rated fair (42/100). Weldable only with care — preheat 200–250 °C, low-hydrogen consumables and immediate stress relief; never weld carburized surfaces.
What surface finishes work on 18CrNiMo7-6 Cold Drawn?
Not anodizable — use phosphating, black oxide, oil or Zn-Ni plating (bake to avoid hydrogen embrittlement); shot peening of tooth roots markedly raises bending fatigue life.
Can 18CrNiMo7-6 Cold Drawn be formed, bent or molded?
Hot forge at 1050–1150 °C then normalize; cold forming limited to annealed small-section bar with generous radii.
What is the maximum service temperature of 18CrNiMo7-6 Cold Drawn?
18CrNiMo7-6 Cold Drawn is rated for continuous use to about 300°C (572 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Can FabDigit make parts in 18CrNiMo7-6 Cold Drawn?
Yes — 18CrNiMo7-6 Cold Drawn is available for CNC machining and sheet metal with instant online pricing. Upload a STEP file to get a price and a DFM check.
Sources
- EN 10084 — Case hardening steels: technical delivery conditions — CEN (2008)
- EN 10263-4 / EN ISO 683-3 case-hardening steel designations — CEN/ISO (2018)
- 18CrNiMo7-6 (1.6587) gear steel data sheet — Ovako / Böhler / Dörrenberg (2022)
- ASM Handbook Vol.1 — Properties and Selection: Irons, Steels — ASM International (1990)
- ASM Handbook Vol.4 — Heat Treating (carburizing of gear steels) — ASM International (1991)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.