Steel 16MnCrS5 Normalized
Heat-treated state
EN 16MnCrS5
Use to homogenize forgings and give a uniform ferrite–pearlite structure for consistent machining and later carburizing.
Values for the Normalized condition
Other 16MnCrS5 tempers and conditions
16MnCrS5 is listed in 11 conditions; see the grade overview at 16MnCrS5.
Compare all 11 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
Spheroidize annealed | Sub-critical spheroidizing anneal giving globular carbides in ferrite for maximum cold-formability of this resulfurized case-hardening steel. | 330 | 520 | 24 | 152 HB | 44 W/m·K |
soft/spheroidize annealed | Best condition for deep cold forming, cold extrusion and heavy machining before carburizing. | 350 | 560 | 25 | 165 HB | 8.4 % IACS |
Treated for cold shearability | Delivery condition per EN 10084 when bar/coil must be cold sheared or cropped into blanks. | 370 | 580 | 23 | 170 HB | 8.2 % IACS |
Treated to a specified hardness range | Ordered when a narrow incoming hardness band is needed for automated machining lines. | 390 | 600 | 21 | 175 HB | 8.2 % IACS |
NormalizedThis page normalized, ferrite-pearlite | Use to homogenize forgings and give a uniform ferrite–pearlite structure for consistent machining and later carburizing. | 400 | 620 | 22 | 175 HB | 8.2 % IACS |
HRDefault Hot rolled | Standard stock condition for bar and billet that will be machined and then carburized. | 420 | 640 | 20 | 180 HB | — |
Spheroidized and Cold Drawn | Spheroidize-annealed bar finished by cold drawing: close tolerances and bright surface with moderate strain hardening, still suitable for cold heading and later case hardening. | 520 | 640 | 11 | 190 HB | 44 W/m·K |
Cold rolled | Choose for thin strip and stamped blanks needing tight thickness and good surface before carburizing. | 550 | 700 | 12 | 17 HRC | 8.2 % IACS |
Cold drawn | Pick for turned/CNC parts made from bright bar where dimensional accuracy and chip control matter most. | 600 | 760 | 10 | 225 HB | — |
Quenched and tempered | Core-property condition after case hardening (~880 °C quench, 180–200 °C temper) — pick when core strength must be specified. | 650 | 930 | 11 | 30 HRC | — |
carburized, quenched and tempered (58–62 HRC case) | Final service condition for gears and shafts: hard wear-resistant case with a tough core; specify case depth (typically 0.3–1.5 mm). | 750 | 1,100 | 9 | 60 HRC | — |
What is 16MnCrS5 Normalized?
16MnCrS5 Normalized is 16MnCrS5 heat treated to Normalized — use to homogenize forgings and give a uniform ferrite–pearlite structure for consistent machining and later carburizing. 16MnCrS5 Normalized has a yield strength of 400 MPa (58 ksi) and a tensile strength of 620 MPa (89.9 ksi) — weaker than 60% of steel grades. Elongation at break is 22% and the elastic modulus is 210 GPa (30.5 Msi). 16MnCrS5 Normalized has a density of 7.85 g/cm³ (0.284 lb/in³), heavier than 56% of steel grades. It melts at 1,420°C (2,588 °F). HR is the default condition FabDigit quotes; Normalized is available on request or by drawing note.
Advantages
- Forms and bends easily — 62/100, better than 78% of steel grades
Limitations
- Limited service temperature — 180°C (356 °F), worse than 98% of steel grades
16MnCrS5 Normalized properties
Typical room-temperature values for 16MnCrS5 Normalized; 22 are specific to this condition. Other listed values are 16MnCrS5 reference data and may not represent this condition. Bars are the position among steel grades.
Physical3
16MnCrS5 Normalized has a density of 7.85 g/cm³ (0.284 lb/in³), heavier than 56% of steel grades. It melts at 1,420°C (2,588 °F).
Mechanical14
16MnCrS5 Normalized has a yield strength of 400 MPa (58 ksi) and a tensile strength of 620 MPa (89.9 ksi) — weaker than 60% of steel grades. Elongation at break is 22% and the elastic modulus is 210 GPa (30.5 Msi).
Thermal6
16MnCrS5 Normalized is rated for continuous service to 180°C (356 °F). It conducts heat at 44 W/m·K (25.4 BTU/hr·ft·°F), better than 57% of steel grades. Thermal expansion is 11.5 µm/m·K (6.39 µin/in·°F).
Electrical2
16MnCrS5 Normalized has an electrical resistivity of 2.1×10⁻⁷ Ω·m.
Chemical & Environmental3
Corrosion resistance is not recommended (11/100), worse than 73% of steel grades.
Sustainability4
Producing a kilogram of 16MnCrS5 Normalized takes about 30 MJ of energy and emits 2.1 kg of CO₂ — more than 56% of steel grades. Typical recycled content is 30%.
Manufacturability7
16MnCrS5 Normalized's machinability is good (59/100, better than 80% of steel grades); weldability fair (45/100); formability good (62/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with 16MnCrS5 Normalized
Is 16MnCrS5 easy to machine?
Machines well in +A/+CD condition — the 0.02–0.04 % S gives short chips and ~10–15 % better tool life than 16MnCr5; carbide, 120–200 m/min turning, machine before carburizing.
Can 16MnCrS5 be welded?
Weldable with preheat 150–250 °C, low-hydrogen consumables and post-weld stress relief; sulfur raises hot-cracking risk, so avoid welding carburized surfaces entirely.
Can 16MnCrS5 be formed, bent or molded?
Cold heading, extrusion and shearing done in +A or +S condition; hot forge 1100–1150 °C down to 850 °C then normalize or anneal before machining.
What surface finishes work on 16MnCrS5?
Not anodizable; protect with oil, Mn/zinc phosphate, black oxide or zinc-nickel plating (bake to avoid H-embrittlement), and grind/hone carburized surfaces after heat treatment.
16MnCrS5 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| C | 0.14 – 0.19 | 0.16 |
| Si | ≤ 0.4 | 0.25 |
| Mn | 1 – 1.3 | 1.15 |
| P | ≤ 0.03 | 0.02 |
| Sdeliberate sulfur addition for machinability | 0.02 – 0.04 | 0.03 |
| Cr | 0.8 – 1.1 | 0.95 |
| Fe | balance |
16MnCrS5 Normalized — frequently asked
What is 16MnCrS5 Normalized used for?
16MnCrS5 Normalized is typically used for gears, shafts and pins. In short: carburizing Cr-Mn-S bar.
What is the yield strength of 16MnCrS5 Normalized?
16MnCrS5 Normalized has a typical yield strength of 400 MPa (58 ksi) and a tensile strength of 620 MPa (89.9 ksi) — weaker than 60% of steel grades. Strength varies by condition: see the 11 listed tempers.
Is 16MnCrS5 Normalized easy to machine?
Reasonably — machinability is rated good (59/100, better than 80% of steel grades). Machines well in +A/+CD condition — the 0.02–0.04 % S gives short chips and ~10–15 % better tool life than 16MnCr5; carbide, 120–200 m/min turning, machine before carburizing.
Can 16MnCrS5 Normalized be welded?
With care — weldability is rated fair (45/100). Weldable with preheat 150–250 °C, low-hydrogen consumables and post-weld stress relief; sulfur raises hot-cracking risk, so avoid welding carburized surfaces entirely.
What surface finishes work on 16MnCrS5 Normalized?
Not anodizable; protect with oil, Mn/zinc phosphate, black oxide or zinc-nickel plating (bake to avoid H-embrittlement), and grind/hone carburized surfaces after heat treatment.
Can 16MnCrS5 Normalized be formed, bent or molded?
Cold heading, extrusion and shearing done in +A or +S condition; hot forge 1100–1150 °C down to 850 °C then normalize or anneal before machining.
What is the maximum service temperature of 16MnCrS5 Normalized?
16MnCrS5 Normalized is rated for continuous use to about 180°C (356 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between 16MnCrS5-HR and 16MnCrS5-CD?
HR is the default condition — standard stock condition for bar and billet that will be machined and then carburized. CD: pick for turned/CNC parts made from bright bar where dimensional accuracy and chip control matter most. Yield strength is 420 MPa in HR versus 600 MPa in CD.
Can FabDigit make parts in 16MnCrS5 Normalized?
Yes — 16MnCrS5 Normalized is available for CNC machining; every part is priced by an engineer rather than instantly. Upload a STEP file to get a price and a DFM check.
Sources
- EN 10084 — Case hardening steels: technical delivery conditions — CEN (2008)
- EN 10277 — Bright steel products: technical delivery conditions — CEN (2018)
- ASM Handbook Vol.1 — Properties and Selection: Irons, Steels and High-Performance Alloys — ASM International (1990)
- ASM Handbook Vol.4A — Steel Heat Treating Fundamentals and Processes (carburizing) — ASM International (2013)
- Case-hardening steel 16MnCr5 / 16MnCrS5 (1.7131 / 1.7139) datasheet — European long-products mills (e.g. Ovako / Saarstahl / Deutsche Edelstahlwerke) (2022)
- GB/T 3077 (comparison grades 20CrMn/20CrMnTi) — SAC (2015)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.