Vespel SP-21 SP-211
Reinforced grade
SP-211 = 15% graphite + 10% PTFE, lowest friction
Use for dry-running, low-speed start/stop seals and sliding parts needing the lowest static and dynamic friction; the 10 % PTFE cuts tensile strength to 44 MPa and service temperature to 260 °C.
Values for the SP-211 condition
Other Vespel SP-21 grades and fills
Vespel SP-21 is listed in 5 conditions; see the grade overview at Vespel SP-21.
Compare all 5 grades and fillsHide
| Grade · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness |
|---|---|---|---|---|---|
SP-211This page 15% graphite + 10% PTFE, lowest friction | Use for dry-running, low-speed start/stop seals and sliding parts needing the lowest static and dynamic friction; the 10 % PTFE cuts tensile strength to 44 MPa and service temperature to 260 °C. | — | 44 | 3.5 | 85 Shore D |
40% graphite filled, maximum dimensional stability | Pick for heavily loaded hot bearings and seal rings that need low thermal expansion and 1.5 W/m·K conduction; the 40 % graphite loading drops tensile strength to 52 MPa and machinability to 50. | — | 52 | 3 | 90 Shore D |
15% MoS2 filled, vacuum / dry-environment grade | Select for sliding parts in vacuum, dry nitrogen or moisture-free atmospheres where graphite loses lubricity; the 15 % MoS₂ filler holds 288 °C service at 55 MPa tensile strength. | — | 55 | 4 | 87 Shore D |
SP-21Default 15% graphite filled | Default pick for high-temperature bearings, seals and washers needing low friction, high PV capability, 0.87 W/m·K heat removal and the dimensional stability given by 15 % graphite. | — | 65 | 4.5 | — |
Unfilled base polyimide | Choose the unfilled base polyimide for non-rubbing parts needing maximum toughness (86 MPa, 7.5 % elongation) or electrical insulation; thermal conductivity falls to 0.35 W/m·K. | — | 86 | 7.5 | — |
What is Vespel SP-21 SP-211?
Vespel SP-21 SP-211 is Vespel SP-21 in the SP-211 grade — use for dry-running, low-speed start/stop seals and sliding parts needing the lowest static and dynamic friction; the 10 % PTFE cuts tensile strength to 44 MPa and service temperature to 260 °C. Vespel SP-21 SP-211 has a tensile strength of 44 MPa (6.38 ksi), weaker than 53% of polymer grades. Elongation at break is 3.5% and the elastic modulus is 2.8 GPa (0.406 Msi). Vespel SP-21 SP-211 has a density of 1.55 g/cm³ (0.056 lb/in³), heavier than 91% of polymer grades. Its glass-transition temperature is 360°C (680 °F). SP-21 is the default condition FabDigit quotes; SP-211 is available on request or by drawing note.
Advantages
- Conducts heat well — 0.66 W/m·K (0.381 BTU/hr·ft·°F), better than 99% of polymer grades
- High service temperature — 260°C (500 °F), better than 97% of polymer grades
- Good UV / weathering resistance — 70/100, better than 83% of polymer grades
Limitations
- High embodied carbon — 15 kg CO₂/kg, worse than 96% of polymer grades
- Heavy — 1.55 g/cm³ (0.056 lb/in³), worse than 91% of polymer grades
- Difficult to weld — 5/100, worse than 89% of polymer grades
- Limited formability — 10/100, worse than 87% of polymer grades
- Limited ductility — 3.5%, worse than 79% of polymer grades
Vespel SP-21 SP-211 properties
Typical room-temperature values for Vespel SP-21 SP-211; 21 are specific to this condition. Other listed values are Vespel SP-21 reference data and may not represent this condition. Bars are the position among polymer grades.
Physical4
Vespel SP-21 SP-211 has a density of 1.55 g/cm³ (0.056 lb/in³), heavier than 91% of polymer grades. Its glass-transition temperature is 360°C (680 °F).
Mechanical10
Vespel SP-21 SP-211 has a tensile strength of 44 MPa (6.38 ksi), weaker than 53% of polymer grades. Elongation at break is 3.5% and the elastic modulus is 2.8 GPa (0.406 Msi).
Thermal9
Vespel SP-21 SP-211 is rated for continuous service to 260°C (500 °F). It conducts heat at 0.66 W/m·K (0.381 BTU/hr·ft·°F), better than 99% of polymer grades. Thermal expansion is 52 µm/m·K (28.9 µin/in·°F).
Chemical & Environmental3
Corrosion resistance is excellent (87/100), better than 72% of polymer grades. UV resistance is very good.
Sustainability3
Producing a kilogram of Vespel SP-21 SP-211 takes about 290 MJ of energy and emits 15 kg of CO₂ — more than 95% of polymer grades. Typical recycled content is 0%.
Manufacturability4
Vespel SP-21 SP-211's machinability is good (62/100, better than 60% of polymer grades); weldability not recommended (5/100); formability not recommended (10/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with Vespel SP-21 SP-211
Is Vespel SP-21 easy to machine?
Cut dry at high speed with light feeds using sharp carbide or PCD; the graphite filler is abrasive to tooling. Skip coolant to avoid moisture pickup, and dry parts in an inert atmosphere after machining if needed.
Can Vespel SP-21 be welded?
This thermoset polyimide cannot be melt-welded. Assemble with high-temperature epoxy or polyimide adhesives, or with mechanical fasteners.
Can Vespel SP-21 be formed, bent or molded?
Parts are direct-formed from powder, or isostatically pressed and sintered at high temperature into blanks, then machined to size. Injection moulding and extrusion are not possible.
What surface finishes work on Vespel SP-21?
Fine grinding and lapping give high-quality sealing faces. Plating and anodizing are not applicable; dry per DuPont's recommendation before assembly and allow for moisture-related swelling.
Vespel SP-21 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| graphitesolid lubricant filler, wt% | 14 – 16 | 15 |
| polyimide (PMDA/ODA) matrixthermoset aromatic polyimide, non-melting | ≥ 83 (balance) | — |
Vespel SP-21 SP-211 — frequently asked
What is Vespel SP-21 SP-211 used for?
Vespel SP-21 SP-211 is typically used for turbine engine seal rings, high-temperature bearings and bushings in jet engines. In short: graphite-filled Vespel; 288 °C continuous service; triple SP-1 conductivity.
What is the tensile strength of Vespel SP-21 SP-211?
Vespel SP-21 SP-211 has a typical tensile strength of 44 MPa (6.38 ksi) — weaker than 53% of polymer grades. Strength varies by condition: see the 5 listed tempers.
Is Vespel SP-21 SP-211 easy to machine?
Reasonably — machinability is rated good (62/100, better than 60% of polymer grades). Cut dry at high speed with light feeds using sharp carbide or PCD; the graphite filler is abrasive to tooling. Skip coolant to avoid moisture pickup, and dry parts in an inert atmosphere after machining if needed.
Can Vespel SP-21 SP-211 be welded?
Not readily — weldability is rated not recommended (5/100). This thermoset polyimide cannot be melt-welded. Assemble with high-temperature epoxy or polyimide adhesives, or with mechanical fasteners.
What surface finishes work on Vespel SP-21 SP-211?
Fine grinding and lapping give high-quality sealing faces. Plating and anodizing are not applicable; dry per DuPont's recommendation before assembly and allow for moisture-related swelling.
Can Vespel SP-21 SP-211 be formed, bent or molded?
Parts are direct-formed from powder, or isostatically pressed and sintered at high temperature into blanks, then machined to size. Injection moulding and extrusion are not possible.
What is the maximum service temperature of Vespel SP-21 SP-211?
Vespel SP-21 SP-211 is rated for continuous use to about 260°C (500 °F), and briefly to 482°C. Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Sources
- Vespel SP Polyimide Parts and Shapes — Design Handbook & Property Data — DuPont (2021)
- Vespel SP-21 / SP-211 / SP-22 grade data sheets — DuPont (Rogers Corporation Vespel business) (2023)
- MatWeb polyimide (graphite-filled) typical property listings — MatWeb LLC (2024)
- Engineering Plastics — Engineered Materials Handbook Vol. 2 (polyimides) — ASM International (1988)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.