PC/PBT GF30
Reinforced grade
GF30 = 30 % glass-fiber reinforced
Highest stiffness and heat resistance of the family; use for load-bearing housings and under-hood brackets.
Values for the GF30 condition
Other PC/PBT grades and fills
PC/PBT is listed in 7 conditions; see the grade overview at PC/PBT.
Compare all 7 grades and fillsHide
| Grade · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness |
|---|---|---|---|---|---|
Impact-modified / high-impact grade | Pick when ductile failure is required down to -30/-40 °C, e.g. bumper systems and rocker panels. | 46 | 47 | 150 | 72 Shore D |
Post-consumer-recycled content grade | Use when 20–50 % PCR content is required by an OEM sustainability spec; slightly lower and more variable impact. | 49 | 50 | 80 | 75 Shore D |
Heat-stabilized grade | Antioxidant/heat-stabilizer package for prolonged service near 110–120 °C (e.g. paint-bake or lamp-adjacent parts). | 54 | 55 | 100 | 76 Shore D |
Mineral / talc filled | Choose for isotropic shrinkage and low CTE on large painted exterior panels without fiber read-through. | 56 | 57 | 25 | 80 Shore D |
Flame-retardant, UL 94 V-0 | Select for enclosures and E&E parts requiring V-0 at 1.5 mm; some loss of ductility and heat resistance. | 56 | 57 | 55 | 78 Shore D |
15 % glass-fiber reinforced | Mid stiffness/low warpage compromise for painted structural trim and brackets. | — | 85 | 6 | — |
GF30This page 30 % glass-fiber reinforced | Highest stiffness and heat resistance of the family; use for load-bearing housings and under-hood brackets. | — | 115 | 3.5 | — |
What is PC/PBT GF30?
PC/PBT GF30 is PC/PBT in the GF30 grade — highest stiffness and heat resistance of the family; use for load-bearing housings and under-hood brackets. PC/PBT GF30 has a yield strength of 52 MPa (7.54 ksi) and a tensile strength of 115 MPa (16.7 ksi) — stronger than 56% of polymer grades. Elongation at break is 3.5% and the elastic modulus is 8 GPa (1.16 Msi). PC/PBT GF30 has a density of 1.44 g/cm³ (0.052 lb/in³), heavier than 85% of polymer grades. Its glass-transition temperature is 130°C (266 °F).
Advantages
- Low, predictable mold shrinkage — 0.25%, better than 93% of polymer grades
- Stiff — 8 GPa (1.16 Msi), better than 91% of polymer grades
- Conducts heat well — 0.28 W/m·K (0.162 BTU/hr·ft·°F), better than 79% of polymer grades
- Good UV / weathering resistance — 55/100, better than 77% of polymer grades
Limitations
- Heavy — 1.44 g/cm³ (0.052 lb/in³), worse than 85% of polymer grades
- Difficult to machine — 42/100, worse than 80% of polymer grades
- Limited ductility — 3.5%, worse than 79% of polymer grades
PC/PBT GF30 properties
Typical room-temperature values for PC/PBT GF30; 14 are specific to this condition. Other listed values are PC/PBT reference data and may not represent this condition. Bars are the position among polymer grades.
Physical5
PC/PBT GF30 has a density of 1.44 g/cm³ (0.052 lb/in³), heavier than 85% of polymer grades. Its glass-transition temperature is 130°C (266 °F).
Mechanical11
PC/PBT GF30 has a yield strength of 52 MPa (7.54 ksi) and a tensile strength of 115 MPa (16.7 ksi) — stronger than 56% of polymer grades. Elongation at break is 3.5% and the elastic modulus is 8 GPa (1.16 Msi).
Thermal11
PC/PBT GF30 is rated for continuous service to 120°C (248 °F). It conducts heat at 0.28 W/m·K (0.162 BTU/hr·ft·°F), better than 79% of polymer grades. Thermal expansion is 28 µm/m·K (15.6 µin/in·°F).
Electrical7
PC/PBT GF30 is an electrical insulator with a dielectric strength of 26 kV/mm (660.4 V/mil) and a resistivity of 1×10¹³ Ω·m.
Chemical & Environmental3
Corrosion resistance is very good (80/100), worse than 52% of polymer grades. UV resistance is good.
Sustainability4
Producing a kilogram of PC/PBT GF30 takes about 95 MJ of energy and emits 5.5 kg of CO₂ — less than 70% of polymer grades. Typical recycled content is 10%.
Manufacturability7
PC/PBT GF30's machinability is fair (42/100, worse than 80% of polymer grades); weldability very good (70/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with PC/PBT GF30
Is PC/PBT easy to machine?
Machines like tough PC: sharp positive-rake carbide tools, high speed / moderate feed, air or mist cooling; avoid stress-inducing dry drilling and anneal (~110 °C) before solvent contact.
Can PC/PBT be welded?
Joins well by ultrasonic, laser, hot-plate and vibration welding; adhesive bonding with polyurethane/epoxy after abrasion or flame/plasma treatment — avoid solvent cements that stress-crack the PC phase.
Can PC/PBT be formed, bent or molded?
Injection mold at 245–275 °C melt / 50–90 °C tool with pellets dried to <0.02 % moisture (2–4 h at 100–120 °C) to prevent hydrolytic splay and loss of impact; shrinkage 0.5–1.0 % unfilled.
What surface finishes work on PC/PBT?
Excellent for painting — accepts 1K/2K automotive basecoat-clearcoat with adhesion promoter; can be laser-marked, hot-stamped, in-mold decorated or vacuum metallized, but is opaque and not suitable for optical polishing.
PC/PBT chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| polycarbonate (PC)bisphenol-A polycarbonate matrix phase | 45 – 75 | 60 |
| poly(butylene terephthalate) (PBT)semi-crystalline phase, provides chemical/weather resistance | 20 – 50 | 32 |
| impact modifier (MBS/core-shell acrylic low-temperature toughness | 3 – 12 | 6 |
| compatibilizer / transesterification catphosphite/epoxy stabilizers, antioxidants, mold release | 0.3 – 2 | 1 |
PC/PBT GF30 — frequently asked
What is PC/PBT GF30 used for?
PC/PBT GF30 is typically used for automotive body panels, bumper components, electrical enclosures and chemical-resistant housings. In short: paintable exterior PC blend; better chemical resistance than PC; tough at low temperature.
What is the yield strength of PC/PBT GF30?
PC/PBT GF30 has a typical yield strength of 52 MPa (7.54 ksi) and a tensile strength of 115 MPa (16.7 ksi) — stronger than 56% of polymer grades. Strength varies by condition: see the 7 listed tempers.
Is PC/PBT GF30 easy to machine?
Not especially — machinability is rated fair (42/100, worse than 80% of polymer grades). Machines like tough PC: sharp positive-rake carbide tools, high speed / moderate feed, air or mist cooling; avoid stress-inducing dry drilling and anneal (~110 °C) before solvent contact.
Can PC/PBT GF30 be welded?
Yes — weldability is rated very good (70/100). Joins well by ultrasonic, laser, hot-plate and vibration welding; adhesive bonding with polyurethane/epoxy after abrasion or flame/plasma treatment — avoid solvent cements that stress-crack the PC phase.
What surface finishes work on PC/PBT GF30?
Excellent for painting — accepts 1K/2K automotive basecoat-clearcoat with adhesion promoter; can be laser-marked, hot-stamped, in-mold decorated or vacuum metallized, but is opaque and not suitable for optical polishing.
Can PC/PBT GF30 be formed, bent or molded?
Injection mold at 245–275 °C melt / 50–90 °C tool with pellets dried to <0.02 % moisture (2–4 h at 100–120 °C) to prevent hydrolytic splay and loss of impact; shrinkage 0.5–1.0 % unfilled.
What is the maximum service temperature of PC/PBT GF30?
PC/PBT GF30 is rated for continuous use to about 120°C (248 °F), and briefly to 130°C. Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Sources
- ASTM D5927 — Standard Specification for Thermoplastic Polyester (TPES) Injection Molding and Extrusion Materials — ASTM International (2018)
- ISO 7391 — Polycarbonate (PC) moulding and extrusion materials — ISO (2006)
- Xenoy PC/PBT resin product datasheets and processing guide — SABIC Specialties (2023)
- Makroblend PC+PBT grade datasheets — Covestro (2023)
- CAMPUS plastics database — PC+PBT blends (ISO 10350 datasets) — CWFG / CAMPUS consortium (2024)
- Engineered Materials Handbook Vol. 2: Engineering Plastics — ASM International (1988)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.