PC/PBT GF30 vs PC/PBT PCR
Polymer · PC/PBT grade comparison
PC/PBT GF30 and PC/PBT PCR are two grades of the same polymer grade, PC/PBT: GF30 (30 % glass-fiber reinforced) versus PCR (post-consumer-recycled content grade). The chemistry is identical, so every difference below comes from the condition. PC/PBT GF30 is the stronger of the two: yield strength 52 MPa (7.54 ksi) against 49 MPa (7.11 ksi) for PC/PBT PCR, about 6% more; tensile strength follows at 115 MPa (16.7 ksi) vs 50 MPa (7.25 ksi). In exchange, PC/PBT PCR is the more ductile: elongation 80% versus 3.5% for PC/PBT GF30. PC/PBT PCR is lighter (1.21 g/cm³ vs 1.44 g/cm³ for PC/PBT GF30) and PC/PBT GF30 is stiffer (8 GPa vs 2.1 GPa). On the shop floor, PC/PBT PCR machines more easily (good vs fair).
PC/PBT GF30Choose it when strength drives the design, or when the part sees heat.
PC/PBT PCRChoose it when the part is bent, formed or impact-loaded, or when weight is the constraint.
PC/PBT GF30 vs PC/PBT PCR: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Flexural Strength
Flexural Modulus
Izod Impact, Notched
Hardness, Shore D
Hardness, Rockwell R
Same in both: Poisson's Ratio 0.4
Physical
Density and transition temperatures.
Density
Same in both: Melting Temperature (Tm) 222°C432 °F · Glass Transition (Tg) 130°C266 °F · Water Absorption (24 h) 0.12% · Water Absorption (Saturation) 0.4%
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Heat Deflection Temp. @ 0.45 MPa
Heat Deflection Temp. @ 1.8 MPa
Vicat Softening Point (B50)
Same in both: Specific Heat Capacity 1,400 J/kg·K0.33 BTU/lb·°F · Min Service Temperature -40°C-40 °F · Limiting Oxygen Index 24% · Max Service Temperature (short-term) 130°C266 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Resistivity 1×10¹³ Ω·m3.94×10²⁰ µΩ·in · Dielectric Strength 26 kV/mm660 V/mil · Dielectric Constant (1 MHz) 3.1 · Dissipation Factor (1 MHz) 0.012 · Volume Resistivity 1×10¹⁵ Ω·cm · Surface Resistivity 1×10¹⁵ Ω · Comparative Tracking Index (CTI) 275 V
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: UV / Weathering Resistance 55 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Mold Shrinkage
Melt Flow Rate
Same in both: Polishability 55 / 100 · Processing Melt Temperature (typ.) 260°C500 °F · Mold Temperature (typ.) 70°C158 °F
Sustainability
Primary-production footprint per kilogram.
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Energy (primary production) 95 MJ/kg40,843 BTU/lb · Embodied Water 250 L/kg30 gal/lb
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
PC/PBT GF30 vs PC/PBT PCR — frequently asked
Is PC/PBT GF30 stronger than PC/PBT PCR?
Yes. PC/PBT GF30 has a typical yield strength of 52 MPa (7.54 ksi) against 49 MPa (7.11 ksi) for PC/PBT PCR — about 6% more. Tensile strength is 115 MPa (16.7 ksi) vs 50 MPa (7.25 ksi).
Which grade does FabDigit quote by default, GF30 or PCR?
Specify the condition in the material field or the drawing note; FabDigit prices the quote for the state you call out.
Which is easier to machine, PC/PBT GF30 or PC/PBT PCR?
PC/PBT PCR. Its machinability rates good (62/100) against fair (42/100) for PC/PBT GF30.