Melamine Foam UF
Grade
UF = cleaning-sponge (ultra-fine cell) grade
Fine-cell, slightly denser foam whose hard resin struts act as a micro-abrasive for water-only cleaning.
Values for the UF condition
Other Melamine Foam grades and fills
Melamine Foam is listed in 5 conditions; see the grade overview at Melamine Foam.
Compare all 5 grades and fillsHide
| Grade · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness |
|---|---|---|---|---|---|
Graphite-enhanced grade | Choose for the most demanding transport fire tests and slightly lower conductivity, where dark colour is acceptable. | 0.01 | 0.12 | 15 | — |
Solution heat treated (unstable) | Use where the foam surface stays visible (studio panels, ceiling baffles) and grey is unacceptable. | 0.01 | 0.12 | 15 | — |
Hydrophobic-treated grade | Silicone/fluoro-impregnated version for HVAC ducts and outdoor enclosures where condensation or splash water is present. | 0.01 | 0.12 | 14 | — |
UFThis page Cleaning-sponge (ultra-fine cell) grade | Fine-cell, slightly denser foam whose hard resin struts act as a micro-abrasive for water-only cleaning. | 0.01 | 0.15 | 12 | — |
Compressed / densified melamine foam | Heat-compressed block for firestop gaskets, high-temperature seals and thin high-strength insulation layers. | 0.04 | 0.4 | 10 | — |
What is Melamine Foam UF?
Melamine Foam UF is Melamine Foam in the UF grade — fine-cell, slightly denser foam whose hard resin struts act as a micro-abrasive for water-only cleaning. Melamine Foam UF has a tensile strength of 0.15 MPa (0.0218 ksi), weaker than 97% of polymer grades. Elongation at break is 12% and the elastic modulus is 6×10⁻⁴ GPa (8.7×10⁻⁵ Msi).
Advantages
- Easy to machine — 88/100, better than 92% of polymer grades
- High service temperature — 150°C (302 °F), better than 79% of polymer grades
Limitations
- Low stiffness — 6×10⁻⁴ GPa (8.7×10⁻⁵ Msi), worse than 98% of polymer grades
- Poor heat conductor — 0.04 W/m·K (0.0208 BTU/hr·ft·°F), worse than 92% of polymer grades
- Degrades in UV without stabilisers — 25/100, worse than 76% of polymer grades
Melamine Foam UF properties
Typical room-temperature values for Melamine Foam UF; 17 are specific to this condition. Other listed values are Melamine Foam reference data and may not represent this condition. Bars are the position among polymer grades.
Mechanical6
Melamine Foam UF has a tensile strength of 0.15 MPa (0.0218 ksi), weaker than 97% of polymer grades. Elongation at break is 12% and the elastic modulus is 6×10⁻⁴ GPa (8.7×10⁻⁵ Msi).
Thermal7
Melamine Foam UF is rated for continuous service to 150°C (302 °F). It conducts heat at 0.04 W/m·K (0.0208 BTU/hr·ft·°F), worse than 92% of polymer grades.
Electrical2
Chemical & Environmental2
UV resistance is poor.
Sustainability3
Producing a kilogram of Melamine Foam UF takes about 100 MJ of energy and emits 5 kg of CO₂ — less than 61% of polymer grades. Typical recycled content is 0%.
Manufacturability2
Melamine Foam UF's machinability is excellent (88/100, better than 92% of polymer grades); formability poor (30/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with Melamine Foam UF
Is Melamine Foam easy to machine?
Cut with band knife, oscillating blade, die or waterjet; hot-wire does not work (thermoset) and routing generates friable dust — use extraction.
Can Melamine Foam be welded?
Not weldable; assemble with spray contact adhesive, hot-melt web or mechanical clips/facings.
Can Melamine Foam be formed, bent or molded?
Sheets are die-cut or CNC contour-cut from bun stock; only the thermoformable grades can be steam/heat compression-moulded into 3-D shapes.
What surface finishes work on Melamine Foam?
Usually left raw or laminated with glass tissue, aluminium foil, PU film or acoustic fabric; heavy paint/coating closes the cells and destroys sound absorption.
Melamine Foam chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| emulsifier / sulfonate surfactantresidual foaming aid | 0.5 – 2.5 | 1.5 |
| blowing agent residue (C5 hydrocarbon)largely driven off after curing | 0 – 0.5 | 0.2 |
| graphiteonly in graphite-enhanced (G+) variant | 0 – 3 | 0 |
| melamine-formaldehyde resin (crosslinkedmelamine:formaldehyde molar ratio typically 1:3, fully cured thermoset | ≥ 96 (balance) | — |
Melamine Foam UF — frequently asked
What is Melamine Foam UF used for?
Melamine Foam UF is typically used for acoustic absorption panels, fire-retardant insulation, transportation NVH treatment and abrasive cleaning sponges. In short: inherently flame-retardant acoustic foam; 180 °C open-cell foam; non-structural, friable surface.
What is the tensile strength of Melamine Foam UF?
Melamine Foam UF has a typical tensile strength of 0.15 MPa (0.0218 ksi) — weaker than 97% of polymer grades. Strength varies by condition: see the 5 listed tempers.
Is Melamine Foam UF easy to machine?
Yes — machinability is rated excellent (88/100, better than 92% of polymer grades). Cut with band knife, oscillating blade, die or waterjet; hot-wire does not work (thermoset) and routing generates friable dust — use extraction.
Can Melamine Foam UF be welded?
Not weldable; assemble with spray contact adhesive, hot-melt web or mechanical clips/facings.
What surface finishes work on Melamine Foam UF?
Usually left raw or laminated with glass tissue, aluminium foil, PU film or acoustic fabric; heavy paint/coating closes the cells and destroys sound absorption.
Can Melamine Foam UF be formed, bent or molded?
Sheets are die-cut or CNC contour-cut from bun stock; only the thermoformable grades can be steam/heat compression-moulded into 3-D shapes.
What is the maximum service temperature of Melamine Foam UF?
Melamine Foam UF is rated for continuous use to about 150°C (302 °F), and briefly to 250°C. Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Sources
- Basotect melamine resin foam product brochure and grade data (G, G+, W, TG, UL, UF) — BASF (2022)
- UL 94 Tests for Flammability of Plastic Materials (HF-1 horizontal foam test) — UL Solutions (2020)
- DIN 4102-1 / EN 13501-1 building material fire classification — DIN / CEN (2019)
- EN ISO 1798 / ISO 3386 flexible cellular polymeric materials — tensile and compression stress-strain — ISO (2018)
- Cellular Solids: Structure and Properties (open-cell foam mechanics) — Cambridge University Press (1997)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.