Steel SK5 Annealed
Temper
JIS SK5
Softest, most machinable and most formable condition; the standard delivery state for tool-steel bar prior to hardening.
Values for the Annealed condition
Other SK5 tempers and conditions
SK5 is listed in 6 conditions; see the grade overview at SK5.
- Annealed
- HR
- CR
- Normalized
- BT
- Q&T
Compare all 6 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
AnnealedThis page spheroidize/full annealed (≤ 217 HB) | Softest, most machinable and most formable condition; the standard delivery state for tool-steel bar prior to hardening. | 380 | 640 | 20 | 185 HB | — |
HRDefault Hot rolled | Cheapest starting stock for parts that will be re-annealed, machined or hardened afterwards. | 400 | 710 | 12 | 200 HB | — |
Cold rolled | Pick for blanking, stamping and forming operations followed by hardening; good gauge tolerance and surface. | 430 | 720 | 10 | 210 HB | — |
austenitized ~900 °C, air cooled (fine pearlite) | Use to refine grain and homogenize forgings/hot-rolled stock before hardening, or where medium strength without quenching is enough. | 525 | 1,010 | 11 | 31 HRC | — |
Blue-tempered / hardened-and-tempered spring strip, 44–50 HRC | Ready-to-use spring/shim strip: high elastic limit with enough toughness to bend and coil without re-heat-treating. | 1,350 | 1,550 | 4 | 47 HRC | — |
Quenched and tempered | Working condition for cutting edges, saw teeth, scrapers and wear plates where maximum hardness matters more than toughness. | 1,650 | 2,000 | 2 | 60 HRC | — |
What is SK5 Annealed?
SK5 Annealed is SK5 in the Annealed temper — softest, most machinable and most formable condition; the standard delivery state for tool-steel bar prior to hardening. SK5 Annealed has a yield strength of 380 MPa (55.1 ksi) and a tensile strength of 640 MPa (92.8 ksi) — weaker than 68% of steel grades. Elongation at break is 20% and the elastic modulus is 205 GPa (29.7 Msi). SK5 Annealed has a density of 7.82 g/cm³ (0.283 lb/in³), lighter than 82% of steel grades. It melts at 1,425°C (2,597 °F). HR is the default condition FabDigit quotes; Annealed is available on request or by drawing note.
Advantages
- Polishes to a fine finish — 70/100, better than 87% of steel grades
- Conducts heat well — 48 W/m·K (27.7 BTU/hr·ft·°F), better than 79% of steel grades
- High electrical conductivity — 9.5 % IACS, better than 75% of steel grades
Limitations
- Difficult to weld — 18/100, worse than 87% of steel grades
- Low fracture toughness — 50 MPa·√m (45.5 ksi·√in), worse than 86% of steel grades
SK5 Annealed properties
Typical room-temperature values for SK5 Annealed; 14 are specific to this condition. Other listed values are SK5 reference data and may not represent this condition. Bars are the position among steel grades.
Physical3
SK5 Annealed has a density of 7.82 g/cm³ (0.283 lb/in³), lighter than 82% of steel grades. It melts at 1,425°C (2,597 °F).
Mechanical16
SK5 Annealed has a yield strength of 380 MPa (55.1 ksi) and a tensile strength of 640 MPa (92.8 ksi) — weaker than 68% of steel grades. Elongation at break is 20% and the elastic modulus is 205 GPa (29.7 Msi).
Thermal6
SK5 Annealed is rated for continuous service to 400°C (752 °F). It conducts heat at 48 W/m·K (27.7 BTU/hr·ft·°F), better than 79% of steel grades. Thermal expansion is 11.5 µm/m·K (6.39 µin/in·°F).
Electrical3
SK5 Annealed conducts electricity at 9.5 % IACS, better than 75% of steel grades.
Chemical & Environmental3
Corrosion resistance is not recommended (10/100), worse than 86% of steel grades.
Sustainability4
Producing a kilogram of SK5 Annealed takes about 27 MJ of energy and emits 2.1 kg of CO₂ — less than 59% of steel grades. Typical recycled content is 30%.
Manufacturability8
SK5 Annealed's machinability is fair (42/100, worse than 73% of steel grades); weldability poor (18/100); formability fair (45/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with SK5 Annealed
Is SK5 easy to machine?
Machine only in the annealed condition (≈45% of 1212) with sharp carbide or coated HSS tooling; once hardened above ~50 HRC, switch to grinding, EDM or hard turning with CBN.
Can SK5 be welded?
Poor weldability at 0.85% C — expect martensite and quench cracks; if unavoidable, preheat 250–350 °C, use low-hydrogen/austenitic filler and post-weld temper immediately.
Can SK5 be formed, bent or molded?
Blank, bend and coil in the soft/annealed temper with generous radii (≥2t) and well-lubricated tooling; blue-tempered strip forms only to spring-type radii, then stress-relieve at 200–260 °C.
What surface finishes work on SK5?
Not anodizable — protect with oil, phosphate/black oxide, electroless nickel, zinc or hard chrome; polish easily to a bright edge but keep humidity off unprotected surfaces.
SK5 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| CJIS G 4401 SK5 / SK85 | 0.8 – 0.9 | 0.85 |
| Si | 0.1 – 0.35 | 0.25 |
| Mn | 0.1 – 0.5 | 0.35 |
| P | ≤ 0.03 | |
| S | ≤ 0.03 | |
| Curesidual max | ≤ 0.25 | |
| Niresidual max; Ni+Cr ≤ 0.35 | ≤ 0.25 | |
| Crresidual max | ≤ 0.3 | |
| Fe | balance |
SK5 Annealed — frequently asked
What is SK5 Annealed used for?
SK5 Annealed is typically used for hand tools, cold cutting knives, saw blades, doctor and scraper blades, spring clips and retainers and shims and feeler strip. In short: spring carbon steel sheet.
What is the yield strength of SK5 Annealed?
SK5 Annealed has a typical yield strength of 380 MPa (55.1 ksi) and a tensile strength of 640 MPa (92.8 ksi) — weaker than 68% of steel grades. Strength varies by condition: see the 6 listed tempers.
Is SK5 Annealed easy to machine?
Not especially — machinability is rated fair (42/100, worse than 73% of steel grades). Machine only in the annealed condition (≈45% of 1212) with sharp carbide or coated HSS tooling; once hardened above ~50 HRC, switch to grinding, EDM or hard turning with CBN.
Can SK5 Annealed be welded?
Not readily — weldability is rated poor (18/100). Poor weldability at 0.85% C — expect martensite and quench cracks; if unavoidable, preheat 250–350 °C, use low-hydrogen/austenitic filler and post-weld temper immediately.
What surface finishes work on SK5 Annealed?
Not anodizable — protect with oil, phosphate/black oxide, electroless nickel, zinc or hard chrome; polish easily to a bright edge but keep humidity off unprotected surfaces.
Can SK5 Annealed be formed, bent or molded?
Blank, bend and coil in the soft/annealed temper with generous radii (≥2t) and well-lubricated tooling; blue-tempered strip forms only to spring-type radii, then stress-relieve at 200–260 °C.
What is the maximum service temperature of SK5 Annealed?
SK5 Annealed is rated for continuous use to about 400°C (752 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between SK5-HR and SK5-BT?
HR is the default condition — cheapest starting stock for parts that will be re-annealed, machined or hardened afterwards. BT: ready-to-use spring/shim strip: high elastic limit with enough toughness to bend and coil without re-heat-treating. Yield strength is 400 MPa in HR versus 1,350 MPa in BT.
Can FabDigit make parts in SK5 Annealed?
Yes — SK5 Annealed is available for CNC machining and sheet metal; every part is priced by an engineer rather than instantly. Upload a STEP file to get a price and a DFM check.
Sources
- JIS G 4401 Carbon tool steels (SK85/SK5) — JISC (2009)
- ASM Handbook Vol. 1 — Properties and Selection: Irons, Steels, and High-Performance Alloys (AISI 1080 data) — ASM International (1990)
- ASM Specialty Handbook — Tool Materials — ASM International (1995)
- GB/T 1298 (T8A/T9A comparison) — SAC (2008)
- Hardened & tempered / blue-tempered carbon spring strip datasheets — strip mill producers (e.g. Sandvik, Nippon Steel strip) (2022)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.