Steel SCr420-SA (Spheroidize annealed)
Heat-treated state
JIS SCr420 · EN 20Cr
Choose for cold forging / cold extrusion of gear blanks and splined shafts.
Values for the SA condition
Other SCr420 tempers and conditions
SCr420 is listed in 8 conditions; see the grade overview at SCr420.
Compare all 8 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
SAThis page Spheroidize annealed | Choose for cold forging / cold extrusion of gear blanks and splined shafts. | 320 | 500 | 30 | 150 HB | 8 % IACS |
ADefault Solution annealed | Standard stock condition for machining green parts before carburizing. | 350 | 560 | 25 | 170 HB | — |
Hot rolled | Cheapest mill condition for bars that will be forged and fully heat treated later. | 390 | 620 | 22 | 185 HB | — |
Normalized | Refines forging grain structure and gives uniform machinability before carburizing. | 420 | 660 | 22 | 197 HB | — |
Cold drawn | Pick for precise-diameter shafting and automatic-lathe work where tighter tolerance and better finish are needed. | 560 | 680 | 12 | 200 HB | — |
Quenched and tempered | Use for shafts and fasteners that need through strength without a carburized case; JIS core-property condition. | 700 | 900 | 17 | 29 HRC | — |
Carbonitrided | Lower-temperature alternative for thin cases (0.2–0.6 mm) on small gears, washers and pins with less distortion. | 700 | 1,000 | 11 | 59 HRC | 7.4 % IACS |
Carburized and hardened | The service condition for gears and splines: hard wear/pitting-resistant case over a tough core. | 850 | 1,100 | 11 | 60 HRC | — |
What is SCr420-SA?
SCr420-SA is SCr420 heat treated to SA — choose for cold forging / cold extrusion of gear blanks and splined shafts. SCr420-SA has a yield strength of 320 MPa (46.4 ksi) and a tensile strength of 500 MPa (72.5 ksi) — weaker than 81% of steel grades. Elongation at break is 30% and the elastic modulus is 207 GPa (30 Msi). SCr420-SA has a density of 7.85 g/cm³ (0.284 lb/in³), heavier than 56% of steel grades. It melts at 1,425°C (2,597 °F). A is the default condition FabDigit quotes; SA is available on request or by drawing note.
Advantages
- Ductile — tolerates forming and impact — 30%, better than 93% of steel grades
- Forms and bends easily — 78/100, better than 91% of steel grades
Limitations
- Low strength — 320 MPa (46.4 ksi), worse than 81% of steel grades
SCr420-SA properties
Typical room-temperature values for SCr420-SA; 21 are specific to this condition. Other listed values are SCr420 reference data and may not represent this condition. Bars are the position among steel grades.
Physical3
SCr420-SA has a density of 7.85 g/cm³ (0.284 lb/in³), heavier than 56% of steel grades. It melts at 1,425°C (2,597 °F).
Mechanical13
SCr420-SA has a yield strength of 320 MPa (46.4 ksi) and a tensile strength of 500 MPa (72.5 ksi) — weaker than 81% of steel grades. Elongation at break is 30% and the elastic modulus is 207 GPa (30 Msi).
Thermal6
SCr420-SA is rated for continuous service to 400°C (752 °F). It conducts heat at 45 W/m·K (26 BTU/hr·ft·°F), better than 66% of steel grades. Thermal expansion is 12.2 µm/m·K (6.78 µin/in·°F).
Electrical3
SCr420-SA conducts electricity at 8 % IACS, better than 55% of steel grades.
Chemical & Environmental3
Corrosion resistance is not recommended (12/100), worse than 53% of steel grades.
Sustainability4
Producing a kilogram of SCr420-SA takes about 27 MJ of energy and emits 2.1 kg of CO₂ — less than 59% of steel grades. Typical recycled content is 30%.
Manufacturability8
SCr420-SA's machinability is good (55/100, better than 62% of steel grades); weldability good (58/100); formability very good (78/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with SCr420-SA
Is SCr420 easy to machine?
Machine green in the annealed or normalized state (~60 % of 1212); after carburizing only grinding, honing or hard turning with CBN is practical.
Can SCr420 be welded?
Weldable before heat treatment with 100–200 °C preheat and low-hydrogen consumables; welding carburized parts is not recommended due to case cracking.
Can SCr420 be formed, bent or molded?
Hot forges readily at 1100–1200 °C; spheroidize annealed bar cold-forges and cold-extrudes well for gear and shaft blanks.
What surface finishes work on SCr420?
No anodizing — protect with Mn/Zn phosphate, black oxide, zinc or Cr plating; shot peening after carburizing markedly raises bending fatigue life.
SCr420 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| CJIS G4053 | 0.18 – 0.23 | 0.2 |
| Si | 0.15 – 0.35 | 0.25 |
| Mn | 0.6 – 0.9 | 0.75 |
| P | ≤ 0.03 | — |
| S | ≤ 0.03 | — |
| Cr | 0.9 – 1.2 | 1.05 |
| Niresidual max | ≤ 0.25 | — |
| Curesidual max | ≤ 0.3 | — |
| Moresidual, not intentionally added | ≤ 0.08 | — |
| Fe | balance | — |
SCr420-SA — frequently asked
What is SCr420-SA used for?
SCr420-SA is typically used for automotive gears, shafts and pins. In short: standard carburising gear steel; 5120 / 20MnCr5 equivalent; cold-forgeable case-hardening bar.
What is the yield strength of SCr420-SA?
SCr420-SA has a typical yield strength of 320 MPa (46.4 ksi) and a tensile strength of 500 MPa (72.5 ksi) — weaker than 81% of steel grades. Strength varies by condition: see the 8 listed tempers.
Is SCr420-SA easy to machine?
Reasonably — machinability is rated good (55/100, better than 62% of steel grades). Machine green in the annealed or normalized state (~60 % of 1212); after carburizing only grinding, honing or hard turning with CBN is practical.
Can SCr420-SA be welded?
Yes — weldability is rated good (58/100). Weldable before heat treatment with 100–200 °C preheat and low-hydrogen consumables; welding carburized parts is not recommended due to case cracking.
What surface finishes work on SCr420-SA?
No anodizing — protect with Mn/Zn phosphate, black oxide, zinc or Cr plating; shot peening after carburizing markedly raises bending fatigue life.
Can SCr420-SA be formed, bent or molded?
Hot forges readily at 1100–1200 °C; spheroidize annealed bar cold-forges and cold-extrudes well for gear and shaft blanks.
What is the maximum service temperature of SCr420-SA?
SCr420-SA is rated for continuous use to about 400°C (752 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between SCr420-A and SCr420-CH?
A is the default condition — standard stock condition for machining green parts before carburizing. CH: the service condition for gears and splines: hard wear/pitting-resistant case over a tough core. Yield strength is 350 MPa in A versus 850 MPa in CH.
Sources
- JIS G 4053 — Low-alloyed steels for machine structural use — JSA (2016)
- ASTM A29/A29M and SAE J404 (AISI 5120) — ASTM / SAE (2020)
- GB/T 3077 (20Cr) — SAC (2015)
- ASM Handbook Vol.1 — Properties and Selection: Irons, Steels, and High-Performance Alloys — ASM International (1990)
- ASM Handbook Vol.4A — Steel Heat Treating Fundamentals (carburizing) — ASM International (2013)
- SMM / Mysteel (2025)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.