Steel Ingot Iron Full Hard
Supply condition
ASTM A867 · GB DT4 · also ARMCO Ingot Iron
Only for stiff springy strip, wire and shims; magnetic softness is lost and ductility is minimal.
Values for the Full Hard condition
Other Ingot Iron tempers and conditions
Ingot Iron is listed in 6 conditions; see the grade overview at Ingot Iron.
Compare all 6 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
850–950 °C, controlled slow cool | Choose for finished electromagnet cores and relay parts needing lowest coercivity and highest permeability after machining. | 130 | 260 | 48 | 65 HB | 17.6 % IACS |
AnnealedDefault full anneal ~850–900 °C, slow cool | Standard stocked condition for magnetic cores, poles and deep-drawn parts; softest mechanically with good permeability. | 150 | 275 | 45 | 70 HB | 78 W/m·K |
~900 °C, air cool | Uniform fine-grained structure for heavier sections where a full magnetic anneal is not required. | 170 | 295 | 40 | 80 HB | 17.3 % IACS |
as-rolled plate, bar and coil | Lowest-cost mill condition for weldments and parts that will be annealed after fabrication. | 185 | 310 | 35 | 85 HB | 17.2 % IACS |
Cold Drawn / cold rolled ~1/4–1/2 hard | Pick for straight, close-tolerance bar and shafts where higher strength and better surface finish matter more than magnetic quality. | 320 | 380 | 15 | 110 HB | 74 W/m·K |
Full HardThis page heavily cold rolled strip/wire | Only for stiff springy strip, wire and shims; magnetic softness is lost and ductility is minimal. | 410 | 460 | 6 | 135 HB | 16.8 % IACS |
What is Ingot Iron Full Hard?
Ingot Iron Full Hard is Ingot Iron supplied in the Full Hard condition — only for stiff springy strip, wire and shims; magnetic softness is lost and ductility is minimal. Ingot Iron Full Hard has a yield strength of 410 MPa (59.5 ksi) and a tensile strength of 460 MPa (66.7 ksi) — weaker than 57% of steel grades. Elongation at break is 6% and the elastic modulus is 205 GPa (29.7 Msi). Ingot Iron Full Hard has a density of 7.87 g/cm³ (0.284 lb/in³), heavier than 92% of steel grades. It melts at 1,535°C (2,795 °F). Annealed is the default condition FabDigit quotes; Full Hard is available on request or by drawing note.
Advantages
- Conducts heat well — 74 W/m·K (42.8 BTU/hr·ft·°F), better than 100% of steel grades
- High electrical conductivity — 16.8 % IACS, better than 100% of steel grades
- Readily welded — 85/100, better than 83% of steel grades
Limitations
- Limited ductility — 6%, worse than 97% of steel grades
- Limited service temperature — 250°C (482 °F), worse than 85% of steel grades
Ingot Iron Full Hard properties
Typical room-temperature values for Ingot Iron Full Hard; 22 are specific to this condition. Other listed values are Ingot Iron reference data and may not represent this condition. Bars are the position among steel grades.
Physical3
Ingot Iron Full Hard has a density of 7.87 g/cm³ (0.284 lb/in³), heavier than 92% of steel grades. It melts at 1,535°C (2,795 °F).
Mechanical16
Ingot Iron Full Hard has a yield strength of 410 MPa (59.5 ksi) and a tensile strength of 460 MPa (66.7 ksi) — weaker than 57% of steel grades. Elongation at break is 6% and the elastic modulus is 205 GPa (29.7 Msi).
Thermal6
Ingot Iron Full Hard is rated for continuous service to 250°C (482 °F). It conducts heat at 74 W/m·K (42.8 BTU/hr·ft·°F), better than 100% of steel grades. Thermal expansion is 12 µm/m·K (6.67 µin/in·°F).
Electrical3
Ingot Iron Full Hard conducts electricity at 16.8 % IACS, better than 100% of steel grades.
Chemical & Environmental3
Corrosion resistance is not recommended (10/100), worse than 86% of steel grades.
Sustainability4
Producing a kilogram of Ingot Iron Full Hard takes about 28 MJ of energy and emits 2.1 kg of CO₂ — less than 56% of steel grades. Typical recycled content is 15%.
Manufacturability8
Ingot Iron Full Hard's machinability is good (56/100, better than 71% of steel grades); weldability excellent (85/100); formability poor (30/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with Ingot Iron Full Hard
Is Ingot Iron easy to machine?
Very gummy — use sharp positive-rake tools, high speed, generous coolant and light finishing passes to avoid built-up edge and tearing; chip breaking is poor.
Can Ingot Iron be welded?
Excellent by any process (GTAW, GMAW, resistance, EB); no preheat or PWHT needed for hardness, but re-anneal welded magnetic cores to restore permeability.
Can Ingot Iron be formed, bent or molded?
Outstanding cold formability — deep drawing, spinning, cold heading and severe bending all practical; expect low springback and stick-slip galling, so lubricate well.
What surface finishes work on Ingot Iron?
Rusts quickly bare: zinc/nickel plate, phosphate + oil, or paint; polishes to a bright but soft, easily scratched surface; not anodizable.
Ingot Iron chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| C≤0.010 % typical for hydrogen-annealed magnetic grades | ≤ 0.03 | 0.01 |
| SiARMCO-type ingot iron typically <0.01 % | ≤ 0.3 | 0.02 |
| Mn | ≤ 0.4 | 0.05 |
| P | ≤ 0.02 | 0.01 |
| S | ≤ 0.03 | 0.01 |
| Alresidual from deoxidation | ≤ 0.1 | 0.02 |
| Fe≥99.8 %, commonly 99.85–99.95 % | balance | — |
Ingot Iron Full Hard — frequently asked
What is Ingot Iron Full Hard used for?
Ingot Iron Full Hard is typically used for magnetic pole pieces and cores, electromagnet cores, chemical/corrosion test coupons, enameling stock and welding electrode cores. In short: magnetically softest iron stock; best cold formability; lowest-carbon iron grade.
What is the yield strength of Ingot Iron Full Hard?
Ingot Iron Full Hard has a typical yield strength of 410 MPa (59.5 ksi) and a tensile strength of 460 MPa (66.7 ksi) — weaker than 57% of steel grades. Strength varies by condition: see the 6 listed tempers.
Is Ingot Iron Full Hard easy to machine?
Reasonably — machinability is rated good (56/100, better than 71% of steel grades). Very gummy — use sharp positive-rake tools, high speed, generous coolant and light finishing passes to avoid built-up edge and tearing; chip breaking is poor.
Can Ingot Iron Full Hard be welded?
Yes — weldability is rated excellent (85/100). Excellent by any process (GTAW, GMAW, resistance, EB); no preheat or PWHT needed for hardness, but re-anneal welded magnetic cores to restore permeability.
What surface finishes work on Ingot Iron Full Hard?
Rusts quickly bare: zinc/nickel plate, phosphate + oil, or paint; polishes to a bright but soft, easily scratched surface; not anodizable.
Can Ingot Iron Full Hard be formed, bent or molded?
Outstanding cold formability — deep drawing, spinning, cold heading and severe bending all practical; expect low springback and stick-slip galling, so lubricate well.
What is the maximum service temperature of Ingot Iron Full Hard?
Ingot Iron Full Hard is rated for continuous use to about 250°C (482 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Sources
- GB/T 6983 — SAC (2008)
- ASTM A848 Standard Specification for Low-Carbon Magnetic Iron — ASTM (2016)
- ASM Handbook Vol.1 — Properties and Selection: Irons, Steels, and High-Performance Alloys — ASM International (1990)
- ASM Handbook Vol.13A — Corrosion: Fundamentals, Testing, and Protection — ASM International (2003)
- ASM Metals Reference Book, 3rd ed. — ASM International (1993)
- Commercially pure / magnetic iron bar and strip datasheets — AK Steel / Ed Fagan / · (2022)