Steel A11 H&T 62-64 HRC
Hardness band
AISI/SAE A11
H&T 62-64 HRC = hardened & Tempered
Highest hardness setting for pure abrasive wear with well-supported, low-impact tooling.
Values for the H&T 62-64 HRC condition
Other A11 tempers and conditions
A11 is listed in 3 conditions; see the grade overview at A11.
- Annealed
- H&T 62-64 HRC
- Hardened & Tempered
Compare all 3 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
AnnealedDefault soft annealed bar/plate for machining | Standard mill supply condition: machine/EDM the tool, then harden and temper. | 600 | 900 | 8 | 26 HRC | 2.7 % IACS |
H&T 62-64 HRCThis page Hardened & Tempered | Highest hardness setting for pure abrasive wear with well-supported, low-impact tooling. | 2,000 | 2,200 | 0.5 | 63 HRC | 2.5 % IACS |
60–62 HRC (standard wear setting) | Default working hardness for blanking dies, powder-compaction tooling and granulator knives. | — | 2,100 | — | 61 HRC | — |
What is A11 H&T 62-64 HRC?
A11 H&T 62-64 HRC is A11 heat treated to H&T 62-64 HRC — highest hardness setting for pure abrasive wear with well-supported, low-impact tooling. A11 H&T 62-64 HRC has a yield strength of 2,000 MPa (290 ksi) and a tensile strength of 2,200 MPa (319 ksi) — stronger than 100% of steel grades. Elongation at break is 0.5% and the elastic modulus is 221 GPa (32.1 Msi). A11 H&T 62-64 HRC has a density of 7.41 g/cm³ (0.268 lb/in³), lighter than 98% of steel grades. Annealed is the default condition FabDigit quotes; H&T 62-64 HRC is available on request or by drawing note.
Advantages
- High strength — 2,000 MPa (290 ksi), better than 100% of steel grades
- Good corrosion resistance — 22/100, better than 90% of steel grades
- High service temperature — 480°C (896 °F), better than 88% of steel grades
- Polishes to a fine finish — 65/100, better than 78% of steel grades
Limitations
- Limited ductility — 0.5%, worse than 100% of steel grades
- Difficult to machine — 4/100, worse than 100% of steel grades
- Difficult to weld — 5/100, worse than 100% of steel grades
- Limited formability — 1/100, worse than 100% of steel grades
- Low fracture toughness — 19 MPa·√m (17.3 ksi·√in), worse than 99% of steel grades
A11 H&T 62-64 HRC properties
Typical room-temperature values for A11 H&T 62-64 HRC; 21 are specific to this condition. Other listed values are A11 reference data and may not represent this condition. Bars are the position among steel grades.
Physical1
A11 H&T 62-64 HRC has a density of 7.41 g/cm³ (0.268 lb/in³), lighter than 98% of steel grades.
Mechanical16
A11 H&T 62-64 HRC has a yield strength of 2,000 MPa (290 ksi) and a tensile strength of 2,200 MPa (319 ksi) — stronger than 100% of steel grades. Elongation at break is 0.5% and the elastic modulus is 221 GPa (32.1 Msi).
Thermal5
A11 H&T 62-64 HRC is rated for continuous service to 480°C (896 °F). It conducts heat at 20 W/m·K (11.6 BTU/hr·ft·°F), worse than 96% of steel grades. Thermal expansion is 10.6 µm/m·K (5.89 µin/in·°F).
Electrical3
A11 H&T 62-64 HRC conducts electricity at 2.5 % IACS, worse than 97% of steel grades.
Chemical & Environmental2
Corrosion resistance is poor (22/100), better than 90% of steel grades.
Sustainability3
Producing a kilogram of A11 H&T 62-64 HRC takes about 55 MJ of energy and emits 4.5 kg of CO₂ — more than 94% of steel grades. Typical recycled content is 25%.
Manufacturability5
A11 H&T 62-64 HRC's machinability is not recommended (4/100, worse than 100% of steel grades); weldability not recommended (5/100); formability not recommended (1/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with A11 H&T 62-64 HRC
Is A11 easy to machine?
Machine only in the annealed state with rigid setups, low speeds and coated carbide or CBN; grinding needs soft/friable SG or CBN wheels because 10% V carbides destroy conventional Al2O3 wheels.
Can A11 be welded?
Essentially non-weldable for structural joints; repair only by preheated (≈480 °C) TIG/microwelding with matched or tool-steel filler followed by re-temper.
Can A11 be formed, bent or molded?
No cold forming; hot work 1040–1150 °C with slow controlled cooling, then full anneal — heat treat: austenitize 1100–1150 °C, quench, temper 2×2 h at 200–550 °C, cryo optional.
What surface finishes work on A11?
Wire EDM and grinding are the normal finishing routes; phosphating, nitriding or PVD (TiCN/AlCrN) coatings are used for galling and corrosion protection since the steel rusts readily.
A11 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| C | 2.35 – 2.55 | 2.45 |
| Vforms MC vanadium carbides, ~15–17 vol% | 9.5 – 10 | 9.75 |
| Cr | 5 – 5.5 | 5.25 |
| Mo | 1.15 – 1.45 | 1.3 |
| Mn | 0.4 – 0.6 | 0.5 |
| Si | 0.8 – 1 | 0.9 |
| Ssulfur-enhanced machinability versions available | ≤ 0.07 | 0.03 |
| Fe | balance | — |
A11 H&T 62-64 HRC — frequently asked
What is A11 H&T 62-64 HRC used for?
A11 H&T 62-64 HRC is typically used for blanking and piercing punches, powder compaction tooling, slitter and shear knives, pelletizing and shredder blades, extruder screw bushings and liners and cold forming and coining dies. In short: extreme wear resistance.
What is the yield strength of A11 H&T 62-64 HRC?
A11 H&T 62-64 HRC has a typical yield strength of 2,000 MPa (290 ksi) and a tensile strength of 2,200 MPa (319 ksi) — stronger than 100% of steel grades. Strength varies by condition: see the 3 listed tempers.
Is A11 H&T 62-64 HRC easy to machine?
Not especially — machinability is rated not recommended (4/100, worse than 100% of steel grades). Machine only in the annealed state with rigid setups, low speeds and coated carbide or CBN; grinding needs soft/friable SG or CBN wheels because 10% V carbides destroy conventional Al2O3 wheels.
Can A11 H&T 62-64 HRC be welded?
Not readily — weldability is rated not recommended (5/100). Essentially non-weldable for structural joints; repair only by preheated (≈480 °C) TIG/microwelding with matched or tool-steel filler followed by re-temper.
What surface finishes work on A11 H&T 62-64 HRC?
Wire EDM and grinding are the normal finishing routes; phosphating, nitriding or PVD (TiCN/AlCrN) coatings are used for galling and corrosion protection since the steel rusts readily.
Can A11 H&T 62-64 HRC be formed, bent or molded?
No cold forming; hot work 1040–1150 °C with slow controlled cooling, then full anneal — heat treat: austenitize 1100–1150 °C, quench, temper 2×2 h at 200–550 °C, cryo optional.
What is the maximum service temperature of A11 H&T 62-64 HRC?
A11 H&T 62-64 HRC is rated for continuous use to about 480°C (896 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Can FabDigit make parts in A11 H&T 62-64 HRC?
Yes — A11 H&T 62-64 HRC is available for CNC machining; every part is priced by an engineer rather than instantly. Upload a STEP file to get a price and a DFM check.
Sources
- CPM 10V Data Sheet — Crucible Industries (2020)
- ASM Handbook Vol.1 — Properties and Selection: Irons, Steels, and High-Performance Alloys (Tool Steels) — ASM International (1990)
- ASTM A681 — Alloy Tool Steels — ASTM International (2015)
- PM cold-work tool steel comparison data — Erasteel / Böhler-Uddeholm technical literature (2021)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.