Rebond Foam RB150
Grade
ASTM D3574 Type I
RB150 = 150 kg/m³ rebond
High-density block for gym landing mats, crash pads and vibration-isolation bases.
Values for the RB150 condition
Other Rebond Foam grades and fills
Rebond Foam is listed in 8 conditions; see the grade overview at Rebond Foam.
Compare all 8 grades and fillsHide
| Grade · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness |
|---|---|---|---|---|---|
60 kg/m³ light rebond | Cheapest, softest rebond for void-fill packaging, light carpet underlay and non-structural padding. | 0.01 | 0.09 | 70 | 8 Shore A |
RB80Default 80 kg/m³ standard rebond | The stocked default: firm, cost-effective cushioning core, carpet cushion and mattress/furniture base layer. | 0.02 | 0.15 | 60 | 12 Shore A |
antimicrobial / low-odour treated rebond | Use for mattress, pet-bed and healthcare underlay where mildew, odour or bacterial growth in a humid environment is a concern. | 0.02 | 0.15 | 60 | 12 Shore A |
Flame-retardant rebond | Specify when the pad must pass furniture, transit or carpet-cushion fire tests; FR additive slightly stiffens the foam and adds cost. | 0.02 | 0.14 | 55 | 14 Shore A |
100 kg/m³ rebond | Pick for floor acoustic underlayment and firmer seating cores where deflection must stay low. | 0.02 | 0.19 | 55 | 15 Shore A |
120 kg/m³ rebond | Use where repeated heavy loading (commercial seating, equipment pads, tumbling mats) would bottom out lighter grades. | 0.03 | 0.23 | 50 | 20 Shore A |
RB150This page 150 kg/m³ rebond | High-density block for gym landing mats, crash pads and vibration-isolation bases. | 0.03 | 0.29 | 45 | 25 Shore A |
200 kg/m³ ultra-dense rebond | Choose for very high static loads, machinery isolation pads and anti-fatigue mat cores; nearly board-like feel. | 0.05 | 0.38 | 40 | 32 Shore A |
What is Rebond Foam RB150?
Rebond Foam RB150 is Rebond Foam in the RB150 grade — high-density block for gym landing mats, crash pads and vibration-isolation bases. Rebond Foam RB150 has a yield strength of 0.03 MPa (0.0049 ksi) and a tensile strength of 0.29 MPa (0.0421 ksi) — weaker than 99% of polymer grades. Elongation at break is 45% and the elastic modulus is 0 GPa (3.05×10⁻⁴ Msi). Rebond Foam RB150 has a density of 0.15 g/cm³ (0.0054 lb/in³), lighter than 86% of polymer grades. Its glass-transition temperature is -50°C (-58 °F). RB80 is the default condition FabDigit quotes; RB150 is available on request or by drawing note.
Advantages
- Low embodied carbon — 1.3 kg CO₂/kg, better than 100% of polymer grades
- Easy to machine — 85/100, better than 88% of polymer grades
- Lightweight — 0.15 g/cm³ (0.0054 lb/in³), better than 86% of polymer grades
Limitations
- Low strength — 0.03 MPa (0.0049 ksi), worse than 99% of polymer grades
- Low stiffness — 0 GPa (3.05×10⁻⁴ Msi), worse than 94% of polymer grades
- Needs corrosion protection — 55/100, worse than 94% of polymer grades
- Degrades in UV without stabilisers — 20/100, worse than 88% of polymer grades
- Poor heat conductor — 0.05 W/m·K (0.0306 BTU/hr·ft·°F), worse than 84% of polymer grades
Rebond Foam RB150 properties
Typical room-temperature values for Rebond Foam RB150; 18 are specific to this condition. Other listed values are Rebond Foam reference data and may not represent this condition. Bars are the position among polymer grades.
Physical2
Rebond Foam RB150 has a density of 0.15 g/cm³ (0.0054 lb/in³), lighter than 86% of polymer grades. Its glass-transition temperature is -50°C (-58 °F).
Mechanical11
Rebond Foam RB150 has a yield strength of 0.03 MPa (0.0049 ksi) and a tensile strength of 0.29 MPa (0.0421 ksi) — weaker than 99% of polymer grades. Elongation at break is 45% and the elastic modulus is 0 GPa (3.05×10⁻⁴ Msi).
Thermal7
Rebond Foam RB150 is rated for continuous service to 90°C (194 °F). It conducts heat at 0.05 W/m·K (0.0306 BTU/hr·ft·°F), worse than 84% of polymer grades.
Electrical2
Rebond Foam RB150 has an electrical resistivity of 1×10¹⁰ Ω·m.
Chemical & Environmental3
Corrosion resistance is good (55/100), worse than 94% of polymer grades. UV resistance is poor.
Sustainability3
Producing a kilogram of Rebond Foam RB150 takes about 20 MJ of energy and emits 1.3 kg of CO₂ — less than 100% of polymer grades. Typical recycled content is 90%.
Manufacturability3
Rebond Foam RB150's machinability is excellent (85/100, better than 88% of polymer grades); weldability poor (15/100); formability very good (72/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with Rebond Foam RB150
Is Rebond Foam easy to machine?
Cut with band-knife, oscillating/drag blade CNC or hot-wire-free reciprocating saw; large cylinders are peeled into continuous roll stock — expect chip dust and blade dulling from the cured binder.
Can Rebond Foam be welded?
Not weldable as a thermoset; bond with contact/hot-melt PU adhesive or flame lamination to fabric and film.
Can Rebond Foam be formed, bent or molded?
Not injection moulded — chips plus MDI binder are steam-cured in a mould or cylinder press at roughly 100–130 °C, then cured/aged before cutting; compression moulding of profiled pads is common.
What surface finishes work on Rebond Foam?
Usually left raw or laminated with scrim, nonwoven, film or fabric; no paint or plating — surfaces can be flame-laminated, glued or heat-embossed only.
Rebond Foam chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| MDI prepolymer bindermoisture-cured polyurethane adhesive, steam-activated in the press | 5 – 12 | 8 |
| flame retardant (FR grades only)phosphate/phosphonate additive for CAL TB117 or FMVSS 302 | 0 – 5 | 0 |
| pigment / additivescolourant, antimicrobial, antistatic optional | 0 – 1 | 0.3 |
| recycled flexible polyurethane foam chipshredded scrap from slabstock trim, mixed colours | ≥ 85 (balance) | — |
Rebond Foam RB150 — frequently asked
What is Rebond Foam RB150 used for?
Rebond Foam RB150 is typically used for carpet underlay/padding, gym and playground mats, packaging dunnage and furniture core stock. In short: lowest-cost high-density foam; recycled-content cushioning core; densest flexible PU stock.
What is the yield strength of Rebond Foam RB150?
Rebond Foam RB150 has a typical yield strength of 0.03 MPa (0.0049 ksi) and a tensile strength of 0.29 MPa (0.0421 ksi) — weaker than 99% of polymer grades. Strength varies by condition: see the 8 listed tempers.
Is Rebond Foam RB150 easy to machine?
Yes — machinability is rated excellent (85/100, better than 88% of polymer grades). Cut with band-knife, oscillating/drag blade CNC or hot-wire-free reciprocating saw; large cylinders are peeled into continuous roll stock — expect chip dust and blade dulling from the cured binder.
Can Rebond Foam RB150 be welded?
Not readily — weldability is rated poor (15/100). Not weldable as a thermoset; bond with contact/hot-melt PU adhesive or flame lamination to fabric and film.
What surface finishes work on Rebond Foam RB150?
Usually left raw or laminated with scrim, nonwoven, film or fabric; no paint or plating — surfaces can be flame-laminated, glued or heat-embossed only.
Can Rebond Foam RB150 be formed, bent or molded?
Not injection moulded — chips plus MDI binder are steam-cured in a mould or cylinder press at roughly 100–130 °C, then cured/aged before cutting; compression moulding of profiled pads is common.
What is the maximum service temperature of Rebond Foam RB150?
Rebond Foam RB150 is rated for continuous use to about 90°C (194 °F), and briefly to 120°C. Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between Rebond Foam RB80 and Rebond Foam RB200?
RB80 is the default condition — the stocked default: firm, cost-effective cushioning core, carpet cushion and mattress/furniture base layer. RB200: choose for very high static loads, machinery isolation pads and anti-fatigue mat cores; nearly board-like feel. Yield strength is 0.02 MPa in RB80 versus 0.05 MPa in RB200.
Sources
- ASTM D3574 — Standard Test Methods for Flexible Cellular Materials, Slab, Bonded and Molded Urethane Foams — ASTM International (2017)
- ASTM D3676 — Standard Specification for Rubber Cellular Cushion Used for Carpet or Rug Underlay — ASTM International (2018)
- California TB 117-2013 and FMVSS 302 flammability requirements — CA BEARHFTI / NHTSA (2013)
- Polyurethane Handbook (Oertel) and Gibson & Ashby, Cellular Solids — Hanser / Cambridge University Press (1997)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.