PS ESD (Antistatic / ESD HIPS)
Grade
GB GB/T 4454 · ISO 1043-1 PS · also Styron, Polystyrol
Pick for electronics trays, carriers and IC packaging where surface charge must be dissipated.
Values for the ESD condition
Other PS grades and fills
PS is listed in 6 conditions; see the grade overview at PS.
Compare all 6 grades and fillsHide
| Grade · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness |
|---|---|---|---|---|---|
Expanded polystyrene foam | Pick for low-cost thermal insulation, protective packaging and lost-foam patterns where mechanical loads are light. | — | 0.28 | — | — |
ESDThis page Antistatic / ESD HIPS | Pick for electronics trays, carriers and IC packaging where surface charge must be dissipated. | 21 | 24 | 25 | 70 Shore D |
High-impact polystyrene | Pick when parts must survive handling/drop loads or be thermoformed into tough opaque housings, refrigerator liners and packaging trays. | 24 | 25 | 40 | 100 HRR |
PS-FR | Pick for TV/appliance housings and electrical enclosures needing UL 94 V-0 at 1.5–3 mm; accept lower impact, higher density and reduced light stability. | — | 26 | 20 | — |
Medium-impact polystyrene | Compromise grade when some toughness is needed but GPPS-like stiffness and translucency must be kept. | 28 | 33 | 15 | 78 Shore D |
GPPSDefault General-purpose (crystal) polystyrene, unfilled transparent | Pick for clarity, stiffness, gloss and lowest cost where impact loading and solvents are absent. | — | 46 | 2.5 | 75 HRM |
What is PS ESD?
PS ESD is PS in the ESD grade — pick for electronics trays, carriers and IC packaging where surface charge must be dissipated. PS ESD has a yield strength of 21 MPa (3.05 ksi) and a tensile strength of 24 MPa (3.48 ksi) — weaker than 79% of polymer grades. Elongation at break is 25% and the elastic modulus is 1.9 GPa (0.276 Msi). PS ESD has a density of 1.05 g/cm³ (0.0379 lb/in³), lighter than 69% of polymer grades. Its glass-transition temperature is 100°C (212 °F). GPPS is the default condition FabDigit quotes; ESD is available on request or by drawing note.
Advantages
- Polishes to a fine finish — 80/100, better than 89% of polymer grades
- Low moisture uptake — 0.05%, better than 84% of polymer grades
- Low embodied carbon — 3.4 kg CO₂/kg, better than 76% of polymer grades
Limitations
- Needs corrosion protection — 45/100, worse than 98% of polymer grades
- Limited service temperature — 60°C (140 °F), worse than 87% of polymer grades
- Low strength — 21 MPa (3.05 ksi), worse than 79% of polymer grades
- Degrades in UV without stabilisers — 25/100, worse than 76% of polymer grades
- Poor heat conductor — 0.17 W/m·K (0.0982 BTU/hr·ft·°F), worse than 75% of polymer grades
PS ESD properties
Typical room-temperature values for PS ESD; 28 are specific to this condition. Other listed values are PS reference data and may not represent this condition. Bars are the position among polymer grades.
Physical6
PS ESD has a density of 1.05 g/cm³ (0.0379 lb/in³), lighter than 69% of polymer grades. Its glass-transition temperature is 100°C (212 °F).
Mechanical17
PS ESD has a yield strength of 21 MPa (3.05 ksi) and a tensile strength of 24 MPa (3.48 ksi) — weaker than 79% of polymer grades. Elongation at break is 25% and the elastic modulus is 1.9 GPa (0.276 Msi).
Thermal11
PS ESD is rated for continuous service to 60°C (140 °F). It conducts heat at 0.17 W/m·K (0.0982 BTU/hr·ft·°F), worse than 75% of polymer grades. Thermal expansion is 70 µm/m·K (38.9 µin/in·°F).
Electrical7
PS ESD is an electrical insulator with a dielectric strength of 22 kV/mm (558.8 V/mil) and a resistivity of 1×10⁷ Ω·m.
Chemical & Environmental3
Corrosion resistance is fair (45/100), worse than 98% of polymer grades. UV resistance is poor.
Sustainability4
Producing a kilogram of PS ESD takes about 87 MJ of energy and emits 3.4 kg of CO₂ — less than 77% of polymer grades. Typical recycled content is 2%.
Manufacturability8
PS ESD's machinability is good (60/100, better than 51% of polymer grades); weldability good (55/100); formability good (68/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with PS ESD
Is PS easy to machine?
Machines fast with sharp positive-rake tools, high speed and light feeds; use air blast (no solvent/oil coolants) and avoid stress risers to prevent crazing and chip-out.
Can PS be welded?
Excellent solvent cementing (MEK, toluene, dichloromethane) and ultrasonic/hot-plate welding; do not attempt to weld to non-styrenics without adhesives.
Can PS be formed, bent or molded?
Very easy injection molding at 190–250 °C melt / 20–70 °C mold with 0.4–0.7 % shrinkage; HIPS and GPPS sheet thermoform and vacuum-form readily above ~130 °C.
What surface finishes work on PS?
Molds to high gloss and can be printed, hot-stamped, vacuum-metallized or painted with PS-compatible (non-aggressive-solvent) systems; anneal machined parts near 70–80 °C to relieve stress before contact with solvents.
PS chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| polybutadiene rubbergraft rubber phase in HIPS only | 4 – 12 | 7 |
| mineral oil / lubricantinternal lubricant/flow aid in HIPS and easy-flow GPPS | 0 – 3 | 1.5 |
| residual styrene monomerfood-grade limits per GB 4806.6 / EU 10/2011 | ≤ 0.1 | 0.03 |
| styrene (polystyrene homopolymer)GPPS: amorphous atactic polystyrene, Mw typically 200,000–300,000 g/mol | balance | — |
PS ESD — frequently asked
What is PS ESD used for?
PS ESD is typically used for disposable cutlery and cups, CD/DVD cases, packaging inserts, lab-ware, optical light diffusers and model kits. In short: lowest-cost clear thermoplastic; stiff but notch-sensitive; best solvent-cementing styrenic.
What is the yield strength of PS ESD?
PS ESD has a typical yield strength of 21 MPa (3.05 ksi) and a tensile strength of 24 MPa (3.48 ksi) — weaker than 79% of polymer grades. Strength varies by condition: see the 6 listed tempers.
Is PS ESD easy to machine?
Reasonably — machinability is rated good (60/100, better than 51% of polymer grades). Machines fast with sharp positive-rake tools, high speed and light feeds; use air blast (no solvent/oil coolants) and avoid stress risers to prevent crazing and chip-out.
Can PS ESD be welded?
Yes — weldability is rated good (55/100). Excellent solvent cementing (MEK, toluene, dichloromethane) and ultrasonic/hot-plate welding; do not attempt to weld to non-styrenics without adhesives.
What surface finishes work on PS ESD?
Molds to high gloss and can be printed, hot-stamped, vacuum-metallized or painted with PS-compatible (non-aggressive-solvent) systems; anneal machined parts near 70–80 °C to relieve stress before contact with solvents.
Can PS ESD be formed, bent or molded?
Very easy injection molding at 190–250 °C melt / 20–70 °C mold with 0.4–0.7 % shrinkage; HIPS and GPPS sheet thermoform and vacuum-form readily above ~130 °C.
What is the maximum service temperature of PS ESD?
PS ESD is rated for continuous use to about 60°C (140 °F), and briefly to 85°C. Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between PS GPPS and PS MIPS?
GPPS is the default condition — pick for clarity, stiffness, gloss and lowest cost where impact loading and solvents are absent. MIPS: compromise grade when some toughness is needed but GPPS-like stiffness and translucency must be kept. Yield strength is 21 MPa in GPPS versus 28 MPa in MIPS.
Sources
- ISO 1043-1 Plastics — Symbols and abbreviated terms — ISO (2011)
- ASTM D4549 Standard Classification System for Polystyrene Molding and Extrusion Materials — ASTM (2020)
- Engineered Materials Handbook, Vol. 2: Engineering Plastics — ASM International (1988)
- STYRON / Trinseo GPPS and HIPS grade datasheets — Trinseo (2023)
- CAMPUS plastics database — PS/HIPS entries — CWFG (2024)
- PlasticsEurope Eco-profile: General Purpose Polystyrene — PlasticsEurope (2020)
- GPPS/HIPS (2026)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.