ASA vs PS
Polymer · grade comparison
ASA and PS are both polymer grades. Both yield at about 45 MPa — strength does not separate them. ASA is the more ductile: elongation 25% versus 2.5% for PS, and PS is harder (85 Shore D vs 78 Shore D). PS is stiffer (3.2 GPa vs 2.2 GPa) and ASA runs hotter in service (80°C vs 65°C continuous). On the shop floor, ASA machines more easily (very good vs good) and PS sits in a lower cost tier (budget, $) than ASA (standard, $$).
ASAChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
PSChoose it when cost is the deciding factor.
ASA vs PS: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Elongation at Break
Compressive Strength
Flexural Strength
Flexural Modulus
Shear Strength
Izod Impact, Notched
Hardness, Shore D
Hardness, Rockwell M
Hardness, Rockwell R
Compressive Modulus
Fracture Toughness (K_IC)
Same in both: Bulk Modulus 4 GPa0.51 Msi · Yield Strength (0.2% offset) 45 MPa6.5 ksi
Physical
Density and transition temperatures.
Density
Glass Transition (Tg)
Water Absorption (24 h)
Water Absorption (Saturation)
Refractive Index
Light Transmission
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Heat Deflection Temp. @ 0.45 MPa
Heat Deflection Temp. @ 1.8 MPa
Vicat Softening Point (B50)
Limiting Oxygen Index
Max Service Temperature (short-term)
Same in both: Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Dielectric Strength
Dielectric Constant (1 MHz)
Dissipation Factor (1 MHz)
Same in both: Electrical Resistivity 1×10¹⁴ Ω·m3.94×10²¹ µΩ·in · Volume Resistivity 1×10¹⁶ Ω·cm · Surface Resistivity 1×10¹⁵ Ω · Comparative Tracking Index (CTI) 600 V
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
UV / Weathering Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Polishability
Melt Flow Rate
Processing Melt Temperature (typ.)
Mold Temperature (typ.)
Same in both: Weldability 70 / 100 · Mold Shrinkage 0.5%
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Water 200 L/kg24 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Stiffness (E / density)
Modulus of Resilience
Same in both: Specific Strength (UTS / density) 44 kN·m/kg · Thermal Diffusivity 0.1 mm²/s · Thermal Shock Resistance Index 0
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | ASA | PS |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Injection molding | Yes | — |
| 3D printing | Yes | — |
| Default condition | Unfilled | — |
| Relative cost | $$ Standard | $ Budget |
| Min. machined wall | 0.5 mm | — |
| Best machined surface | Ra 0.8 µm | — |
| Chrome Plating (Plastic) | Yes | — |
| Conductive Coating | Yes | — |
| Dyeing (Nylon) | Yes | — |
| EMI Shielding Coating | Yes | — |
| Painting | Yes | — |
| Primer Coating | Yes | — |
| Soft Touch Coating | Yes | — |
| Spray Painting | Yes | — |
| Tinted Coating | Yes | — |
| UV Coating | Yes | — |
| Vacuum Metallization | Yes | — |
| Waterproof Coating | Yes | — |
ASA vs PS — frequently asked
What is the difference between ASA and PS?
ASA and PS are both polymer grades. Both yield at about 45 MPa — strength does not separate them. ASA is the more ductile: elongation 25% versus 2.5% for PS, and PS is harder (85 Shore D vs 78 Shore D).
Which is cheaper, ASA or PS?
PS is the lower-cost material: it sits in the budget tier ($) while ASA is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, ASA or PS?
ASA. Its machinability rates very good (75/100) against good (60/100) for PS.
Ready to make it?
Upload a CAD file and FabDigit prices the part in ASA and PS side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.