Copper Alloy C17300-TD02
Supply condition
UNS C17300 · ASTM B196 · EN CuBe2Pb, CW102C
TD02 = solution heat treated and cold worked, half hard
Medium cold work; higher pre-age strength for parts machined then aged.
Values for the TD02 condition
Other C17300 tempers and conditions
C17300 is listed in 9 conditions; see the grade overview at C17300.
Compare all 9 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
ADefault Solution annealed | Soft, most-stocked supply condition for machining or forming before customer ageing. | 220 | 470 | 40 | 110 HB | 18 % IACS |
Solution heat treated and cold worked, quarter hard | Light cold work for straighter, stiffer bar that will still be age hardened later. | 450 | 560 | 25 | 150 HB | 18 % IACS |
TD02This page Solution heat treated and cold worked, half hard | Medium cold work; higher pre-age strength for parts machined then aged. | 550 | 640 | 15 | 12 HRC | 18 % IACS |
Solution heat treated and cold worked, full hard | Maximum cold-worked strength without ageing; best chip control on screw machines. | 660 | 760 | 6 | 22 HRC | 18 % IACS |
Hardened | Standard fully heat-treated condition (≈315 °C/3 h) for springs, tooling and high-strength machined parts. | 1,035 | 1,220 | 5 | 39 HRC | 23 % IACS |
Solution heat treated and precipitation hardened | Solution-annealed C17300 given a full precipitation age (~315–345 °C), giving peak strength and hardness with the free-machining benefit of the lead addition; ductility is low. | 1,035 | 1,210 | 5 | 39 HRC | 24 % IACS |
TD01 and precipitation hardened | Slightly higher strength than AT with retained ductility for machined spring parts. | 1,105 | 1,240 | 4 | 40 HRC | 23 % IACS |
TD02 and precipitation hardened | Higher yield strength for heavily loaded pins, bushings and die inserts. | 1,150 | 1,290 | 3 | 41 HRC | 23 % IACS |
TD04 and precipitation hardened | Peak strength and hardness condition; choose for maximum wear/bearing loads, ductility is minimal. | 1,240 | 1,380 | 2 | 42 HRC | 23 % IACS |
What is C17300-TD02?
C17300-TD02 is C17300 supplied in the TD02 condition — medium cold work; higher pre-age strength for parts machined then aged. C17300-TD02 has a yield strength of 550 MPa (79.8 ksi) and a tensile strength of 640 MPa (92.8 ksi) — stronger than 92% of copper alloy grades. Elongation at break is 15% and the elastic modulus is 128 GPa (18.6 Msi). C17300-TD02 has a density of 8.26 g/cm³ (0.298 lb/in³), lighter than 83% of copper alloy grades. It melts at 865°C (1,589 °F). A is the default condition FabDigit quotes; TD02 is available on request or by drawing note.
Advantages
- High strength — 550 MPa (79.8 ksi), better than 92% of copper alloy grades
Limitations
- Limited service temperature — 100°C (212 °F), worse than 100% of copper alloy grades
- High embodied carbon — 7.5 kg CO₂/kg, worse than 97% of copper alloy grades
- Difficult to weld — 15/100, worse than 94% of copper alloy grades
C17300-TD02 properties
Typical room-temperature values for C17300-TD02; 23 are specific to this condition. Other listed values are C17300 reference data and may not represent this condition. Bars are the position among copper alloy grades.
Physical3
C17300-TD02 has a density of 8.26 g/cm³ (0.298 lb/in³), lighter than 83% of copper alloy grades. It melts at 865°C (1,589 °F).
Mechanical13
C17300-TD02 has a yield strength of 550 MPa (79.8 ksi) and a tensile strength of 640 MPa (92.8 ksi) — stronger than 92% of copper alloy grades. Elongation at break is 15% and the elastic modulus is 128 GPa (18.6 Msi).
Thermal6
C17300-TD02 is rated for continuous service to 100°C (212 °F). It conducts heat at 105 W/m·K (60.7 BTU/hr·ft·°F), better than 56% of copper alloy grades. Thermal expansion is 17.5 µm/m·K (9.72 µin/in·°F).
Electrical3
C17300-TD02 conducts electricity at 18 % IACS, better than 51% of copper alloy grades.
Chemical & Environmental3
Corrosion resistance is good (62/100), worse than 57% of copper alloy grades.
Sustainability4
Producing a kilogram of C17300-TD02 takes about 120 MJ of energy and emits 7.5 kg of CO₂ — more than 98% of copper alloy grades. Typical recycled content is 35%.
Manufacturability8
C17300-TD02's machinability is good (60/100, better than 74% of copper alloy grades); weldability poor (15/100); formability fair (40/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with C17300-TD02
Is C17300 easy to machine?
Lead makes it the easiest BeCu to turn (~60 % of AISI 1212); machine in Condition A or TD tempers, use carbide, flood coolant and wet dust control — beryllium-containing swarf and dust must be captured.
Can C17300 be welded?
Fusion welding is not recommended because of the lead; use resistance/spot welding, mechanical joints, or silver brazing with careful flux and post-braze re-ageing.
Can C17300 be formed, bent or molded?
Form, bend and thread only in Condition A or 1/4–1/2 hard; age at ~315 °C for 2–3 h afterwards, allowing ~0.1–0.2 % dimensional shrinkage.
What surface finishes work on C17300?
Not anodizable; electroless Ni, Ni/Au or Ag plating, passivation or bright polishing are standard — avoid ammonia-based cleaners to prevent stress-corrosion cracking.
C17300 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| BeASTM B196 C17300 | 1.8 – 2 | 1.9 |
| Pbfree-machining addition | 0.2 – 0.6 | 0.4 |
| Ni+Co0.20 % minimum | ≥ 0.2 | 0.3 |
| Ni+Co+Fe0.6 % maximum combined | ≤ 0.6 | — |
| Curemainder, ~97.3 % | balance | — |
C17300-TD02 — frequently asked
What is C17300-TD02 used for?
C17300-TD02 is typically used for automatic-lathe pins and plungers, machined electrical contacts, miniature connector sockets, valve components, mould and die inserts and non-sparking safety tools. In short: high-strength copper; conductive.
What is the yield strength of C17300-TD02?
C17300-TD02 has a typical yield strength of 550 MPa (79.8 ksi) and a tensile strength of 640 MPa (92.8 ksi) — stronger than 92% of copper alloy grades. Strength varies by condition: see the 9 listed tempers.
Is C17300-TD02 easy to machine?
Reasonably — machinability is rated good (60/100, better than 74% of copper alloy grades). Lead makes it the easiest BeCu to turn (~60 % of AISI 1212); machine in Condition A or TD tempers, use carbide, flood coolant and wet dust control — beryllium-containing swarf and dust must be captured.
Can C17300-TD02 be welded?
Not readily — weldability is rated poor (15/100). Fusion welding is not recommended because of the lead; use resistance/spot welding, mechanical joints, or silver brazing with careful flux and post-braze re-ageing.
What surface finishes work on C17300-TD02?
Not anodizable; electroless Ni, Ni/Au or Ag plating, passivation or bright polishing are standard — avoid ammonia-based cleaners to prevent stress-corrosion cracking.
Can C17300-TD02 be formed, bent or molded?
Form, bend and thread only in Condition A or 1/4–1/2 hard; age at ~315 °C for 2–3 h afterwards, allowing ~0.1–0.2 % dimensional shrinkage.
What is the maximum service temperature of C17300-TD02?
C17300-TD02 is rated for continuous use to about 100°C (212 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between C17300-A and C17300-TH04?
A is the default condition — soft, most-stocked supply condition for machining or forming before customer ageing. TH04: peak strength and hardness condition; choose for maximum wear/bearing loads, ductility is minimal. Yield strength is 220 MPa in A versus 1,240 MPa in TH04.
Can FabDigit make parts in C17300-TD02?
Yes — C17300-TD02 is available for CNC machining and sheet metal; every part is priced by an engineer rather than instantly. Upload a STEP file to get a price and a DFM check.
Sources
- ASTM B196/B196M — Copper-Beryllium Alloy Rod and Bar — ASTM International (2018)
- ASTM B441 — Copper-Cobalt-Beryllium and Copper-Beryllium Rod/Bar (related tempers) — ASTM International (2019)
- CDA Alloy C17300 property sheet — Copper Development Association (2023)
- Alloy 25 / Alloy M25 technical data — Materion Brush Performance Alloys (2022)
- ASM Handbook Vol. 2 — Properties of Nonferrous Alloys — ASM International (1990)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.