Steel T8-CDA
Supply condition
AISI/SAE T8 · UNS T12008
CDA = cold drawn annealed bar / drill rod
Pick for small-diameter precision bar and drill-rod blanks needing close size and straightness before hardening.
Values for the CDA condition
Other T8 tempers and conditions
T8 is listed in 5 conditions; see the grade overview at T8.
Compare all 5 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
AnnealedDefault soft annealed bar/billet, ≤277 HB | Standard stocked condition for machining tool blanks before hardening. | 570 | 900 | 15 | 240 HB | — |
CDAThis page Cold drawn annealed bar / drill rod | Pick for small-diameter precision bar and drill-rod blanks needing close size and straightness before hardening. | 750 | 1,000 | 9 | 28 HRC | 3.1 % IACS |
Maximum hardness, low-temperature-limit temper | Use only for rigid, continuous-cut tooling on abrasive work where maximum wear resistance outweighs chipping risk. | 2,000 | 2,100 | 0 | 67 HRC | 2.8 % IACS |
Hardened and high-temperature tempered | Choose when interrupted cuts or shock demand extra toughness at some loss of wear resistance. | — | 2,100 | 0.5 | 63 HRC | — |
Hardened (1230–1260 °C) and double tempered ~550 °C | The normal working hardness for T8 cutting tools — best balance of red hardness and wear resistance. | — | 2,250 | 0.3 | 65 HRC | — |
What is T8-CDA?
T8-CDA is T8 supplied in the CDA condition — pick for small-diameter precision bar and drill-rod blanks needing close size and straightness before hardening. T8-CDA has a yield strength of 750 MPa (109 ksi) and a tensile strength of 1,000 MPa (145 ksi) — stronger than 84% of steel grades. Elongation at break is 9% and the elastic modulus is 220 GPa (31.9 Msi). T8-CDA has a density of 8.6 g/cm³ (0.311 lb/in³), heavier than 99% of steel grades. It melts at 1,400°C (2,552 °F). Annealed is the default condition FabDigit quotes; CDA is available on request or by drawing note.
Advantages
- Polishes to a fine finish — 70/100, better than 87% of steel grades
- High strength — 750 MPa (109 ksi), better than 84% of steel grades
Limitations
- Limited formability — 8/100, worse than 97% of steel grades
- High embodied carbon — 4.2 kg CO₂/kg, worse than 95% of steel grades
- Limited ductility — 9%, worse than 93% of steel grades
- Poor heat conductor — 22 W/m·K (12.7 BTU/hr·ft·°F), worse than 93% of steel grades
- Difficult to weld — 15/100, worse than 91% of steel grades
T8-CDA properties
Typical room-temperature values for T8-CDA; 23 are specific to this condition. Other listed values are T8 reference data and may not represent this condition. Bars are the position among steel grades.
Physical3
T8-CDA has a density of 8.6 g/cm³ (0.311 lb/in³), heavier than 99% of steel grades. It melts at 1,400°C (2,552 °F).
Mechanical13
T8-CDA has a yield strength of 750 MPa (109 ksi) and a tensile strength of 1,000 MPa (145 ksi) — stronger than 84% of steel grades. Elongation at break is 9% and the elastic modulus is 220 GPa (31.9 Msi).
Thermal6
T8-CDA is rated for continuous service to 400°C (752 °F). It conducts heat at 22 W/m·K (12.7 BTU/hr·ft·°F), worse than 93% of steel grades. Thermal expansion is 11.2 µm/m·K (6.22 µin/in·°F).
Electrical3
T8-CDA conducts electricity at 3.1 % IACS, worse than 89% of steel grades.
Chemical & Environmental3
Corrosion resistance is poor (18/100), better than 83% of steel grades.
Sustainability4
Producing a kilogram of T8-CDA takes about 60 MJ of energy and emits 4.2 kg of CO₂ — more than 96% of steel grades. Typical recycled content is 35%.
Manufacturability7
T8-CDA's machinability is poor (34/100, worse than 86% of steel grades); weldability poor (15/100); formability not recommended (8/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with T8-CDA
Is T8 easy to machine?
Machine only in the annealed condition with rigid setups, sharp carbide or cobalt-HSS tooling, low speed and heavy flood coolant; hardened T8 must be ground or EDM'd, using soft wheels and light dressing to avoid grinding burn.
Can T8 be welded?
Not a structural welding grade — repair only, by GTAW/PTA with matching HSS or high-Co filler, preheat 500–550 °C, immediate re-temper; expect cracking if cooled to room temperature unbuffered.
Can T8 be formed, bent or molded?
Hot work at 1050–1150 °C with slow furnace cooling and mandatory full anneal (~870 °C, slow cool) afterwards; no meaningful cold forming — harden from 1230–1260 °C (salt or vacuum), oil/air/salt quench, double temper 540–595 °C.
What surface finishes work on T8?
Stress-relieve rough-machined blanks before hardening; finish by precision grinding and lapping, then steam-oxide, black-oxide, nitriding or TiN/TiAlN PVD (below temper temperature) for wear and rust protection — never anodise.
T8 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| C | 0.75 – 0.85 | 0.8 |
| W | 13.25 – 14.75 | 14 |
| Co | 4.25 – 5.75 | 5 |
| Cr | 3.75 – 4.5 | 4.1 |
| V | 1.8 – 2.4 | 2 |
| Mo | 0.4 – 1 | 0.7 |
| Mn | 0.15 – 0.4 | 0.28 |
| Si | 0.15 – 0.4 | 0.28 |
| P | ≤ 0.03 | — |
| S | ≤ 0.03 | — |
| Fe | balance | — |
T8-CDA — frequently asked
What is T8-CDA used for?
T8-CDA is typically used for cold cutting knives and blades, hand tools, lathe tool bits and form tools, milling cutters, twist drills and taps and punches and trim dies. In short: tough water-hardening tool.
What is the yield strength of T8-CDA?
T8-CDA has a typical yield strength of 750 MPa (109 ksi) and a tensile strength of 1,000 MPa (145 ksi) — stronger than 84% of steel grades. Strength varies by condition: see the 5 listed tempers.
Is T8-CDA easy to machine?
Not especially — machinability is rated poor (34/100, worse than 86% of steel grades). Machine only in the annealed condition with rigid setups, sharp carbide or cobalt-HSS tooling, low speed and heavy flood coolant; hardened T8 must be ground or EDM'd, using soft wheels and light dressing to avoid grinding burn.
Can T8-CDA be welded?
Not readily — weldability is rated poor (15/100). Not a structural welding grade — repair only, by GTAW/PTA with matching HSS or high-Co filler, preheat 500–550 °C, immediate re-temper; expect cracking if cooled to room temperature unbuffered.
What surface finishes work on T8-CDA?
Stress-relieve rough-machined blanks before hardening; finish by precision grinding and lapping, then steam-oxide, black-oxide, nitriding or TiN/TiAlN PVD (below temper temperature) for wear and rust protection — never anodise.
Can T8-CDA be formed, bent or molded?
Hot work at 1050–1150 °C with slow furnace cooling and mandatory full anneal (~870 °C, slow cool) afterwards; no meaningful cold forming — harden from 1230–1260 °C (salt or vacuum), oil/air/salt quench, double temper 540–595 °C.
What is the maximum service temperature of T8-CDA?
T8-CDA is rated for continuous use to about 400°C (752 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between T8 Annealed and T8-CDA?
Annealed is the default condition — standard stocked condition for machining tool blanks before hardening. CDA: pick for small-diameter precision bar and drill-rod blanks needing close size and straightness before hardening. Yield strength is 570 MPa in Annealed versus 750 MPa in CDA.
Can FabDigit make parts in T8-CDA?
Yes — T8-CDA is available for CNC machining; every part is priced by an engineer rather than instantly. Upload a STEP file to get a price and a DFM check.
Sources
- ASTM A600 — Tool Steel, High Speed, Tool and Die Steels — ASTM International (2016)
- ASM Handbook Vol. 1: Properties and Selection — Irons, Steels, and High-Performance Alloys (High Speed Tool Steels) — ASM International (1990)
- ASM Specialty Handbook: Tool Materials — ASM International (1995)
- SAE J437/J438 — Tool and Die Steels — SAE International (2015)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.