XPS X150
Grade
ASTM C578 · EN 13164 · GB GB/T 10801.2
X150 = x150 / ASTM C578 Type X
Lightest economy grade for cavity walls, sheathing and non-load-bearing insulation.
Values for the X150 condition
Other XPS grades and fills
XPS is listed in 8 conditions; see the grade overview at XPS.
Compare all 8 grades and fillsHide
| Grade · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness |
|---|---|---|---|---|---|
X150This page X150 / ASTM C578 Type X | Lightest economy grade for cavity walls, sheathing and non-load-bearing insulation. | 0.26 | 0.3 | 3 | — |
X200 / W200 | Intermediate grade for wall and floor heating layers where 250 kPa is not required. | 0.35 | 0.4 | 3 | — |
X250Default X250 / ASTM C578 Type IV | Mainstream building board for roofs, floors and under-slab insulation; best cost/strength balance. | 0.4 | 0.45 | 3 | — |
flame-retardant board, GB 8624 B1(B) rating | Mandatory grade for most Chinese building façade and roof insulation projects requiring B1 fire performance. | 0.4 | 0.45 | 3 | — |
flame-retardant board, GB 8624 B2 rating | Economy fire-rated board for floors, under-slab and non-façade uses where only B2 is required. | 0.4 | 0.45 | 3 | — |
X300 / ASTM C578 Type VI | For loaded floors, inverted roofs and cold-store floors with moderate traffic. | 0.45 | 0.5 | 3.5 | — |
X350 / ASTM C578 Type VII | High-strength grade for road/railway frost protection and heavy under-slab loads. | 0.52 | 0.6 | 3.5 | — |
X500 / ASTM C578 Type V | Highest-density XPS for airport aprons, tank bases, deep foundations and other high compressive loads. | 0.7 | 0.8 | 4 | — |
What is XPS X150?
XPS X150 is XPS in the X150 grade — lightest economy grade for cavity walls, sheathing and non-load-bearing insulation. XPS X150 has a yield strength of 0.26 MPa (0.0377 ksi) and a tensile strength of 0.3 MPa (0.0435 ksi) — weaker than 97% of polymer grades. Elongation at break is 3% and the elastic modulus is 0.01 GPa (0.0012 Msi). XPS X150 has a density of 0.02 g/cm³ (8.67×10⁻⁴ lb/in³), lighter than 96% of polymer grades. Its glass-transition temperature is 100°C (212 °F). X250 is the default condition FabDigit quotes; X150 is available on request or by drawing note.
Advantages
- Easy to machine — 92/100, better than 99% of polymer grades
- Lightweight — 0.02 g/cm³ (8.67×10⁻⁴ lb/in³), better than 96% of polymer grades
Limitations
- Low strength — 0.26 MPa (0.0377 ksi), worse than 97% of polymer grades
- Poor heat conductor — 0.03 W/m·K (0.0173 BTU/hr·ft·°F), worse than 96% of polymer grades
- Degrades in UV without stabilisers — 15/100, worse than 95% of polymer grades
- Limited ductility — 3%, worse than 83% of polymer grades
- Low stiffness — 0.01 GPa (0.0012 Msi), worse than 82% of polymer grades
XPS X150 properties
Typical room-temperature values for XPS X150; 19 are specific to this condition. Other listed values are XPS reference data and may not represent this condition. Bars are the position among polymer grades.
Physical4
XPS X150 has a density of 0.02 g/cm³ (8.67×10⁻⁴ lb/in³), lighter than 96% of polymer grades. Its glass-transition temperature is 100°C (212 °F).
Mechanical10
XPS X150 has a yield strength of 0.26 MPa (0.0377 ksi) and a tensile strength of 0.3 MPa (0.0435 ksi) — weaker than 97% of polymer grades. Elongation at break is 3% and the elastic modulus is 0.01 GPa (0.0012 Msi).
Thermal9
XPS X150 is rated for continuous service to 75°C (167 °F). It conducts heat at 0.03 W/m·K (0.0173 BTU/hr·ft·°F), worse than 96% of polymer grades. Thermal expansion is 70 µm/m·K (38.9 µin/in·°F).
Electrical3
XPS X150 has an electrical resistivity of 1×10¹⁴ Ω·m.
Chemical & Environmental3
Corrosion resistance is very good (75/100), worse than 66% of polymer grades. UV resistance is poor.
Sustainability3
Producing a kilogram of XPS X150 takes about 100 MJ of energy and emits 4.5 kg of CO₂ — less than 61% of polymer grades. Typical recycled content is 10%.
Manufacturability4
XPS X150's machinability is excellent (92/100, better than 99% of polymer grades); weldability poor (20/100); formability poor (28/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with XPS X150
Is XPS easy to machine?
Cuts easily with hot wire, knife, fine-tooth saw or CNC router; keep speeds low and vacuum the dust, and avoid overheating that melts/collapses cells.
Can XPS be welded?
Not structurally weldable; joints are made by tongue-and-groove interlock plus water-based or PU foam adhesive and taped seams.
Can XPS be formed, bent or molded?
Produced by continuous extrusion foaming with gas injection then sizing/skinning; boards are rigid and only mildly thermoformable, so shapes are cut rather than formed.
What surface finishes work on XPS?
Solvent-free coatings only; needs skin removal or grooving for plaster/mortar adhesion, and must be covered (render, screed, membrane) because it degrades under UV.
XPS chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| blowing agent (CO2 / HFO-1234ze / HCFC-1residual gas in closed cells; determines aged λ and carbon footprint | 1 – 6 | 3 |
| flame retardant (brominated polymeric FRwith Sb2O3 or phosphate synergist in B1 grades | 0.5 – 2.5 | 1.2 |
| talc (nucleating agent) | 0.2 – 1.5 | 0.5 |
| pigment / colourantblue/pink/green brand colours | 0.05 – 0.5 | 0.2 |
| polystyrene (styrene homopolymer)GPPS resin, often with some recycled PS | ≥ 90 (balance) | — |
XPS X150 — frequently asked
What is XPS X150 used for?
XPS X150 is typically used for roof/wall insulation panels, below-grade insulation, floral/craft foam and cold storage panels. In short: stronger, drier than EPS; closed-cell moisture resistance; below-grade insulation standard.
What is the yield strength of XPS X150?
XPS X150 has a typical yield strength of 0.26 MPa (0.0377 ksi) and a tensile strength of 0.3 MPa (0.0435 ksi) — weaker than 97% of polymer grades. Strength varies by condition: see the 8 listed tempers.
Is XPS X150 easy to machine?
Yes — machinability is rated excellent (92/100, better than 99% of polymer grades). Cuts easily with hot wire, knife, fine-tooth saw or CNC router; keep speeds low and vacuum the dust, and avoid overheating that melts/collapses cells.
Can XPS X150 be welded?
Not readily — weldability is rated poor (20/100). Not structurally weldable; joints are made by tongue-and-groove interlock plus water-based or PU foam adhesive and taped seams.
What surface finishes work on XPS X150?
Solvent-free coatings only; needs skin removal or grooving for plaster/mortar adhesion, and must be covered (render, screed, membrane) because it degrades under UV.
Can XPS X150 be formed, bent or molded?
Produced by continuous extrusion foaming with gas injection then sizing/skinning; boards are rigid and only mildly thermoformable, so shapes are cut rather than formed.
What is the maximum service temperature of XPS X150?
XPS X150 is rated for continuous use to about 75°C (167 °F), and briefly to 85°C. Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between XPS X250 and XPS X500?
X250 is the default condition — mainstream building board for roofs, floors and under-slab insulation; best cost/strength balance. X500: highest-density XPS for airport aprons, tank bases, deep foundations and other high compressive loads. Yield strength is 0.4 MPa in X250 versus 0.7 MPa in X500.
Sources
- ASTM C578-22 Standard Specification for Rigid, Cellular Polystyrene Thermal Insulation — ASTM International (2022)
- EN 13164:2012+A1:2015 Thermal insulation products for buildings — Factory made XPS products — CEN (2015)
- STYROFOAM Brand XPS Insulation product data — Dow / DuPont Performance Building Solutions (2023)
- FOAMULAR XPS Insulation technical bulletins (Types X, IV, VI, VII, 600/1000) — Owens Corning (2022)
- Inventory of Carbon & Energy (ICE) — insulation materials — University of Bath / Circular Ecology (2019)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.