HR Foam CMHR
Flame-retardant grade
CMHR = combustion-modified / flame-retardant HR
Choose for public, medical and vehicle cushioning that must meet BS 5852 Crib 5, CAL TB117 or GB 17927 fire requirements; combustion modifiers trim tensile strength to 0.11 MPa.
Values for the CMHR condition
Other HR Foam grades and fills
HR Foam is listed in 9 conditions; see the grade overview at HR Foam.
Compare all 9 grades and fillsHide
| Grade · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness |
|---|---|---|---|---|---|
Super-soft / hyper-soft HR | Pick for mattress and pillow top layers and soft back cushions: indentation hardness is low at ~38 kg/m³ while resilience stays high and hysteresis low. | — | 0.08 | 180 | — |
Low-density HR slabstock, ~32–38 kg/m³ | Choose for cost-sensitive furniture backs, upholstery and packaging cushioning at ~32–38 kg/m³; resilience stays good but load bearing and durability are lower. | — | 0.1 | 150 | — |
Conductive / antistatic HR | Choose the carbon-loaded conductive version for electronic component packaging and ESD workstation pads with controlled surface resistance; tensile strength drops to 0.1 MPa. | — | 0.1 | 110 | — |
CMHRThis page Combustion-modified / flame-retardant HR | Choose for public, medical and vehicle cushioning that must meet BS 5852 Crib 5, CAL TB117 or GB 17927 fire requirements; combustion modifiers trim tensile strength to 0.11 MPa. | — | 0.11 | 110 | — |
Medical / antimicrobial-treated HR | Pick for medical mattresses, wheelchair cushions and rehabilitation supports needing low VOC and antimicrobial treatment, and suitable for use with waterproof film. | — | 0.12 | 130 | — |
HR45Default Standard HR slabstock, ~42–48 kg/m³ | Default slabstock for sofa seat cushions, mattress comfort layers and office chair pads at ~42–48 kg/m³, giving the best balance of resilience and durability. | — | 0.13 | 130 | — |
Cold-cure molded HR | Use the cold-cure molded version for automotive seats and headrests with bonded covers: one-shot molding avoids cutting scrap but needs mold temperature and release agent control. | — | 0.14 | 110 | — |
High-density HR slabstock, ~52–58 kg/m³ | Pick for high-end sofas, mattresses and long sitting or lying use, where ~52–58 kg/m³ gives the best sag resistance and fatigue life at higher weight and cost. | — | 0.16 | 120 | — |
High load-bearing / firm HR | Use for heavy-duty seating, truck and bus cushions and mattress support layers, where 60 kg/m³ gives a high support (SAG) factor and strong sag resistance at a firmer feel. | — | 0.17 | 100 | — |
What is HR Foam CMHR?
HR Foam CMHR is HR Foam in the CMHR grade — choose for public, medical and vehicle cushioning that must meet BS 5852 Crib 5, CAL TB117 or GB 17927 fire requirements; combustion modifiers trim tensile strength to 0.11 MPa. HR Foam CMHR has a tensile strength of 0.11 MPa (0.016 ksi), weaker than 99% of polymer grades. Elongation at break is 110% and the elastic modulus is 2.2×10⁻⁵ GPa (3.19×10⁻⁶ Msi). HR Foam CMHR has a density of 0.05 g/cm³ (0.0017 lb/in³), lighter than 89% of polymer grades. Its glass-transition temperature is -55°C (-67 °F). HR45 is the default condition FabDigit quotes; CMHR is available on request or by drawing note.
Advantages
- Lightweight — 0.05 g/cm³ (0.0017 lb/in³), better than 89% of polymer grades
- Easy to machine — 84/100, better than 86% of polymer grades
- Forms and bends easily — 88/100, better than 85% of polymer grades
Limitations
- Low stiffness — 2.2×10⁻⁵ GPa (3.19×10⁻⁶ Msi), worse than 100% of polymer grades
- Poor heat conductor — 0.04 W/m·K (0.0243 BTU/hr·ft·°F), worse than 86% of polymer grades
- Degrades in UV without stabilisers — 25/100, worse than 76% of polymer grades
HR Foam CMHR properties
Typical room-temperature values for HR Foam CMHR; 16 are specific to this condition. Other listed values are HR Foam reference data and may not represent this condition. Bars are the position among polymer grades.
Physical2
HR Foam CMHR has a density of 0.05 g/cm³ (0.0017 lb/in³), lighter than 89% of polymer grades. Its glass-transition temperature is -55°C (-67 °F).
Mechanical8
HR Foam CMHR has a tensile strength of 0.11 MPa (0.016 ksi), weaker than 99% of polymer grades. Elongation at break is 110% and the elastic modulus is 2.2×10⁻⁵ GPa (3.19×10⁻⁶ Msi).
Thermal7
HR Foam CMHR is rated for continuous service to 100°C (212 °F). It conducts heat at 0.04 W/m·K (0.0243 BTU/hr·ft·°F), worse than 86% of polymer grades.
Electrical2
HR Foam CMHR has an electrical resistivity of 1×10⁹ Ω·m.
Chemical & Environmental3
Corrosion resistance is very good (76/100), worse than 64% of polymer grades. UV resistance is poor.
Sustainability4
Producing a kilogram of HR Foam CMHR takes about 103 MJ of energy and emits 5 kg of CO₂ — less than 54% of polymer grades. Typical recycled content is 0%.
Manufacturability3
HR Foam CMHR's machinability is very good (84/100, better than 86% of polymer grades); weldability fair (35/100); formability excellent (88/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with HR Foam CMHR
Is HR Foam easy to machine?
Cut with band saw, horizontal splitting machine, oscillating knife or CNC contour and profile cutting. Hot-wire cutting is not suitable because PU chars and smokes; keep blades sharp and use extraction to avoid torn edges and dust.
Can HR Foam be welded?
Not weldable; bond with water-based or hot-melt adhesive, flame lamination, or high-frequency welding and sewing when combined with fabric.
Can HR Foam be formed, bent or molded?
Two routes: TDI-based continuous box or vertical slabstock foaming with 24 h cure before cutting (Type R), or MDI cold-cure moulding (Type Q) at 45–70 °C mould temperature with 4–6 min demould. Formulation index and cell-opening control set resilience and compression set.
What surface finishes work on HR Foam?
Can be flame- or adhesive-laminated to fabric and nonwoven, fitted with a waterproof TPU film, and die-cut to shape. Plating and hard paint films are not possible, and the open cells absorb solvent-based adhesives.
HR Foam chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| polyether polyol (high-reactivity, EO-timain polyol, functionality 3, OH value 28–35 mgKOH/g | 40 – 60 | 50 |
| polymer (graft SAN/PHD) polyolprovides load bearing and support factor | 5 – 25 | 12 |
| TDI 80/20 or MDI / TDI-MDI blend isocyanTDI for slabstock, MDI for cold-cure molding; index 95–105 | 28 – 40 | 34 |
| water (blowing agent)reacts with NCO to generate CO₂ for blowing | 2 – 4.5 | 3.2 |
| amine + tin catalysts | 0.2 – 1 | 0.5 |
| silicone surfactant (cell opener type) | 0.3 – 1.5 | 0.8 |
| flame retardant / additives (optional)CMHR grades use intumescent or phosphorus FR and melamine | 0 – 15 | 0 |
HR Foam CMHR — frequently asked
What is HR Foam CMHR used for?
HR Foam CMHR is typically used for furniture and mattress cushioning, automotive seat cushions, molded seating pads and sports padding. In short: high-resilience flexible PU; better fatigue than slabstock; higher support factor.
What is the tensile strength of HR Foam CMHR?
HR Foam CMHR has a typical tensile strength of 0.11 MPa (0.016 ksi) — weaker than 99% of polymer grades. Strength varies by condition: see the 9 listed tempers.
Is HR Foam CMHR easy to machine?
Yes — machinability is rated very good (84/100, better than 86% of polymer grades). Cut with band saw, horizontal splitting machine, oscillating knife or CNC contour and profile cutting. Hot-wire cutting is not suitable because PU chars and smokes; keep blades sharp and use extraction to avoid torn edges and dust.
Can HR Foam CMHR be welded?
With care — weldability is rated fair (35/100). Not weldable; bond with water-based or hot-melt adhesive, flame lamination, or high-frequency welding and sewing when combined with fabric.
What surface finishes work on HR Foam CMHR?
Can be flame- or adhesive-laminated to fabric and nonwoven, fitted with a waterproof TPU film, and die-cut to shape. Plating and hard paint films are not possible, and the open cells absorb solvent-based adhesives.
Can HR Foam CMHR be formed, bent or molded?
Two routes: TDI-based continuous box or vertical slabstock foaming with 24 h cure before cutting (Type R), or MDI cold-cure moulding (Type Q) at 45–70 °C mould temperature with 4–6 min demould. Formulation index and cell-opening control set resilience and compression set.
What is the maximum service temperature of HR Foam CMHR?
HR Foam CMHR is rated for continuous use to about 100°C (212 °F), and briefly to 120°C. Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Sources
- ASTM D3574 — Standard Test Methods for Flexible Cellular Materials—Slab, Bonded, and Molded Urethane Foams — ASTM (2017)
- JIS K 6401 Flexible cellular polymeric materials — Polyurethane foam — JSA (2011)
- ISO 2439 Flexible cellular polymeric materials — Determination of hardness (indentation technique) — ISO (2008)
- Cellular Solids: Structure and Properties (Gibson & Ashby) — Cambridge University Press (1997)
- Engineered Materials Handbook Vol. 2: Engineering Plastics — ASM International (1988)
- HR slabstock and cold-cure molded foam technical data — FXI / Carpenter / Recticel (2023)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.