ABS · reinforced grade
ABS-GF30
Properties of the GF30 condition, compared with the other ABS grades.
Highest-stiffness ABS grade for load-bearing frames and metal-replacement parts; brittle, abrasive to tooling and shows fibre read-through.
What is ABS-GF30?
ABS-GF30 is ABS in the GF30 grade — highest-stiffness ABS grade for load-bearing frames and metal-replacement parts; brittle, abrasive to tooling and shows fibre read-through. ABS-GF30 has a yield strength of 42 MPa (6.09 ksi) and a tensile strength of 95 MPa (13.8 ksi) — weaker than 65% of polymer grades. Elongation at break is 2.3% and the elastic modulus is 7.5 GPa (1.09 Msi). ABS-GF30 has a density of 1.28 g/cm³ (0.0462 lb/in³), heavier than 67% of polymer grades. Its glass-transition temperature is 105°C (221 °F). Unfilled is the default condition FabDigit quotes; GF30 is available on request or by drawing note.
Advantages
- Low, predictable mold shrinkage — 0.15%, better than 97% of polymer grades
- Stiff — 7.5 GPa (1.09 Msi), better than 90% of polymer grades
- Readily welded — 78/100, better than 82% of polymer grades
- Forms and bends easily — 82/100, better than 79% of polymer grades
Limitations
- Limited ductility — 2.3%, worse than 91% of polymer grades
- Needs corrosion protection — 68/100, worse than 87% of polymer grades
- Degrades in UV without stabilisers — 22/100, worse than 83% of polymer grades
ABS-GF30 properties
Typical room-temperature values for ABS-GF30 — 12 properties are specific to this condition; the rest are grade-level values shared by every ABS grade. Each bar shows where the value sits among the polymer grades in FabDigit's library — further right is higher.
Physical4
ABS-GF30 has a density of 1.28 g/cm³ (0.0462 lb/in³), heavier than 67% of polymer grades. Its glass-transition temperature is 105°C (221 °F).
Mechanical16
ABS-GF30 has a yield strength of 42 MPa (6.09 ksi) and a tensile strength of 95 MPa (13.8 ksi) — weaker than 65% of polymer grades. Elongation at break is 2.3% and the elastic modulus is 7.5 GPa (1.09 Msi).
Thermal11
ABS-GF30 is rated for continuous service to 75°C (167 °F). It conducts heat at 0.24 W/m·K (0.139 BTU/hr·ft·°F), better than 66% of polymer grades. Thermal expansion is 30 µm/m·K (16.7 µin/in·°F).
Electrical7
ABS-GF30 is an electrical insulator with a dielectric strength of 16 kV/mm (406.4 V/mil) and a resistivity of 1×10¹³ Ω·m.
Chemical & Environmental3
Corrosion resistance is good (68/100), worse than 87% of polymer grades. UV resistance is poor.
Sustainability4
Producing a kilogram of ABS-GF30 takes about 95 MJ of energy and emits 3.8 kg of CO₂ — less than 70% of polymer grades. Typical recycled content is 5%.
Manufacturability8
ABS-GF30's machinability is good (55/100, worse than 63% of polymer grades); weldability very good (78/100); formability very good (82/100).
Values are nominal handbook figures for design screening. Certified mill or lot data ships with every FabDigit order on request.
Other ABS grades and fills
ABS is also supplied in 17 other conditions. The full side-by-side table is on the ABS overview.
- UnfilledDefaultDefault balanced grade for housings, trim and enclosures where impact, appearance and cost matter more than heat or stiffness.43 MPa tensile
- StandardDefaultBaseline commercial ABS resin for cost-driven moulded and extruded parts; properties essentially the same as the unfilled default.42 MPa tensile
- GF40Highly stiff, dimensionally stable short-glass-reinforced ABS injection grade with near-isotropic low shrinkage but low ductility and abrasive processing.110 MPa tensile
- GF30Highest-stiffness ABS grade for load-bearing frames and metal-replacement parts; brittle, abrasive to tooling and shows fibre read-through.95 MPa tensile
- GF20Common structural ABS grade where creep resistance and low warpage matter more than impact or surface gloss.80 MPa tensile
- GF15Intermediate stiffness/dimensional-stability grade for structural brackets and covers.72 MPa tensile
- GF10Mild stiffening and shrinkage reduction while keeping usable toughness and surface quality.65 MPa tensile
- HHStyrene-maleic-anhydride/α-methylstyrene modified ABS lifting HDT by 10–20 °C for automotive interiors and appliance parts near heat sources.48 MPa tensile
- TransparentMethyl-methacrylate-modified ABS (MABS) with refractive-index-matched rubber phase giving glass-clear parts while retaining good toughness and easy processing.45 MPa yield · 72 HRM
- FR V-0Specify when a V-0 listing at the design wall thickness is a hard requirement (power supplies, switchgear, appliance electrics).43 MPa tensile
- FRUse for electrical enclosures, chargers and IT housings that must pass a UL 94 rating; slightly heavier, less tough and lower flowing than standard ABS.42 MPa tensile
- ESDCarbon- or additive-modified ABS for electronics trays, tote boxes and housings needing 10⁴–10⁹ Ω surface resistivity.40 MPa tensile
- ToughVat-photopolymer resin marketed as ABS-like for snap fits, prototypes and functional assemblies; tough and ductile but far lower heat resistance and UV-ageing than moulded ABS.38 MPa yield · 78 Shore D
- High ImpactChoose when notched impact and low-temperature toughness dominate (power-tool housings, luggage, protective covers); pays with lower stiffness and heat resistance.36 MPa yield · 98 HRR
- As PrintedUse for realistic design values of FDM ABS parts: layer bonding and voids cut strength 25–50 % versus moulded ABS, with much lower Z-axis strength.29 MPa yield
Working with ABS-GF30
Is ABS easy to machine?
Machines easily with sharp, positive-rake, polished-flute tools and high speed/low feed; use air blast rather than flood coolant and avoid solvent-based cutting fluids that cause stress cracking.
Can ABS be welded?
Excellent solvent bonding (MEK, acetone, ABS cement) plus ultrasonic, vibration, hot-plate and hot-gas welding; anneal or de-stress before solvent exposure to prevent crazing.
Can ABS be formed, bent or molded?
Dry 2–4 h at 80 °C, mould at 210–260 °C melt / 40–80 °C tool with 0.4–0.7 % shrinkage; extruded sheet vacuum-forms readily at 150–180 °C.
What surface finishes work on ABS?
Takes paint, hot stamping, vapour smoothing (acetone) and is the standard plastic for decorative chrome electroplating after chromic/permanganate etch; requires UV-stable topcoat for outdoor use.
ABS chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| styrenerigid SAN matrix component | 40 – 60 | 50 |
| acrylonitrileprovides chemical resistance and strength | 15 – 35 | 24 |
| polybutadiene rubbergrafted rubber phase; higher levels = high-impact grades | 5 – 30 | 18 |
| additives (stabilisers, lubricants, pigm | 0.5 – 3 | 1.5 |
ABS-GF30 — frequently asked
What is ABS-GF30 used for?
ABS-GF30 is typically used for electronic enclosures and housings, power tool housings, computer keyboards, automotive interior trim, appliance panels and bezels and thermoformed trays and luggage shells. In short: tough general purpose.
What is the yield strength of ABS-GF30?
ABS-GF30 has a typical yield strength of 42 MPa (6.09 ksi) and a tensile strength of 95 MPa (13.8 ksi) — weaker than 65% of polymer grades. Strength varies by condition: see the 18 listed tempers.
Is ABS-GF30 easy to machine?
Reasonably — machinability is rated good (55/100, worse than 63% of polymer grades). Machines easily with sharp, positive-rake, polished-flute tools and high speed/low feed; use air blast rather than flood coolant and avoid solvent-based cutting fluids that cause stress cracking.
Can ABS-GF30 be welded?
Yes — weldability is rated very good (78/100). Excellent solvent bonding (MEK, acetone, ABS cement) plus ultrasonic, vibration, hot-plate and hot-gas welding; anneal or de-stress before solvent exposure to prevent crazing.
What surface finishes work on ABS-GF30?
Takes paint, hot stamping, vapour smoothing (acetone) and is the standard plastic for decorative chrome electroplating after chromic/permanganate etch; requires UV-stable topcoat for outdoor use.
Can ABS-GF30 be formed, bent or molded?
Dry 2–4 h at 80 °C, mould at 210–260 °C melt / 40–80 °C tool with 0.4–0.7 % shrinkage; extruded sheet vacuum-forms readily at 150–180 °C.
What is the maximum service temperature of ABS-GF30?
ABS-GF30 is rated for continuous use to about 75°C (167 °F), and briefly to 95°C. Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between ABS Unfilled and ABS Tough?
Unfilled is the default condition — default balanced grade for housings, trim and enclosures where impact, appearance and cost matter more than heat or stiffness. Tough: vat-photopolymer resin marketed as ABS-like for snap fits, prototypes and functional assemblies; tough and ductile but far lower heat resistance and UV-ageing than moulded ABS. Yield strength is 42 MPa in Unfilled versus 38 MPa in Tough.
Can FabDigit make parts in ABS-GF30?
Yes — ABS-GF30 is available for CNC machining, sheet metal, injection molding and 3D printing with instant online pricing. Upload a STEP file to get a price and a DFM check.
Sources
- ASTM D4673 / D3965 — Standard Classification for ABS Molding and Extrusion Materials — ASTM International (2021)
- ISO 2580-1/-2 — Plastics — Acrylonitrile-butadiene-styrene (ABS) moulding and extrusion materials — ISO (2019)
- Terluran / Novodur / Lustran ABS product datasheets — INEOS Styrolution (2023)
- Cycolac ABS resin datasheets — SABIC (2022)
- Magnum ABS resin datasheets — Trinseo (2022)
- Tough 1500 / Tough 2000 / Durable resin technical data sheets — Formlabs (2023)
- CAMPUS plastics database — ABS ISO 10350 datasets — CWFG / CAMPUS (2024)
- Engineered Materials Handbook Vol. 2: Engineering Plastics — ASM International (1988)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.