Steel 1.2714 QT50-54
Heat-treated state
EN 1.2714
QT50-54 = q&T 50–54 HRC
Use the low-temper 50–54 HRC condition for wear punches and shear blades under limited impact loading; elongation drops to 6%, service to 200 °C and machinability to 12.
Values for the QT50-54 condition
Other 1.2714 tempers and conditions
1.2714 is listed in 7 conditions; see the grade overview at 1.2714.
Compare all 7 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
soft annealed, ≤248 HB | Order soft annealed at 248 HB maximum (230 HB typical) for rough machining and deep cavity milling when you will quench and temper the finished insert yourself. | 430 | 720 | 20 | 230 HB | — |
PrehardDefault Pre-hardened | Use the block supplied quenched and tempered to 28–34 HRC (295 HB) when the cavity is machined straight from stock and no further hardening is planned. | 850 | 1,000 | 13 | 31 HRC | — |
gas/plasma nitrided surface over Q&T core | Add gas or plasma nitriding over the quenched and tempered core to raise cavity wear and heat-erosion resistance; keep the nitriding temperature below the tempering temperature. | 850 | 1,000 | 11 | 31 HRC | 6.9 % IACS |
Electroslag remelted, prehard 28–34 HRC | Specify electroslag remelted stock, prehardened to 28–34 HRC, for large cross-sections and high-polish cavities that need higher cleanliness and transverse toughness. | 870 | 1,020 | 15 | 31 HRC | 6.9 % IACS |
Q&T 38–42 HRC | Harden and temper to 38–42 HRC for hammer forging dies: the best compromise between thermal fatigue and deformation resistance and toughness, with machinability down to 35. | 1,120 | 1,300 | 11 | 40 HRC | — |
Q&T 44–48 HRC | Harden and temper to 44–48 HRC for small die blocks, trim edges and cold or warm punches where wear resistance outranks toughness; elongation falls to 9% and service to 350 °C. | 1,350 | 1,550 | 9 | 46 HRC | — |
QT50-54This page Q&T 50–54 HRC | Use the low-temper 50–54 HRC condition for wear punches and shear blades under limited impact loading; elongation drops to 6%, service to 200 °C and machinability to 12. | 1,550 | 1,800 | 6 | 52 HRC | — |
What is 1.2714 QT50-54?
1.2714 QT50-54 is 1.2714 heat treated to QT50-54 — use the low-temper 50–54 HRC condition for wear punches and shear blades under limited impact loading; elongation drops to 6%, service to 200 °C and machinability to 12. 1.2714 QT50-54 has a yield strength of 1,550 MPa (225 ksi) and a tensile strength of 1,800 MPa (261 ksi) — stronger than 97% of steel grades. Elongation at break is 6% and the elastic modulus is 210 GPa (30.5 Msi). 1.2714 QT50-54 has a density of 7.85 g/cm³ (0.284 lb/in³), heavier than 56% of steel grades. It melts at 1,420°C (2,588 °F). Prehard is the default condition FabDigit quotes; QT50-54 is available on request or by drawing note.
Advantages
- High strength — 1,550 MPa (225 ksi), better than 97% of steel grades
Limitations
- Difficult to machine — 12/100, worse than 99% of steel grades
- Limited ductility — 6%, worse than 97% of steel grades
- Limited service temperature — 200°C (392 °F), worse than 93% of steel grades
- Low fracture toughness — 40 MPa·√m (36.4 ksi·√in), worse than 92% of steel grades
- Limited formability — 12/100, worse than 92% of steel grades
1.2714 QT50-54 properties
Typical room-temperature values for 1.2714 QT50-54; 12 are specific to this condition. Other listed values are 1.2714 reference data and may not represent this condition. Bars are the position among steel grades.
Physical3
1.2714 QT50-54 has a density of 7.85 g/cm³ (0.284 lb/in³), heavier than 56% of steel grades. It melts at 1,420°C (2,588 °F).
Mechanical16
1.2714 QT50-54 has a yield strength of 1,550 MPa (225 ksi) and a tensile strength of 1,800 MPa (261 ksi) — stronger than 97% of steel grades. Elongation at break is 6% and the elastic modulus is 210 GPa (30.5 Msi).
Thermal6
1.2714 QT50-54 is rated for continuous service to 200°C (392 °F). It conducts heat at 34 W/m·K (19.6 BTU/hr·ft·°F), worse than 77% of steel grades. Thermal expansion is 12.5 µm/m·K (6.94 µin/in·°F).
Electrical2
1.2714 QT50-54 has an electrical resistivity of 2.5×10⁻⁷ Ω·m.
Chemical & Environmental2
Corrosion resistance is not recommended (12/100), worse than 53% of steel grades.
Sustainability4
Producing a kilogram of 1.2714 QT50-54 takes about 34 MJ of energy and emits 2.4 kg of CO₂ — more than 82% of steel grades. Typical recycled content is 35%.
Manufacturability7
1.2714 QT50-54's machinability is not recommended (12/100, worse than 99% of steel grades); weldability poor (25/100); formability not recommended (12/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with 1.2714 QT50-54
Is 1.2714 easy to machine?
Annealed material cuts easily; above about 30 HRC in the prehard condition use coated carbide, rigid clamping and high-stiffness milling at reduced feed. Leave 0.2-0.3 mm finishing stock in deep cavities.
Can 1.2714 be welded?
Repair welding with matching or dedicated die-repair filler is workable. Preheat to 300-350 °C, maintain interpass temperature and temper immediately after welding to prevent cracking.
Can 1.2714 be formed, bent or molded?
Hot forging or hot forming only, roughly 1050-850 °C, followed by slow cooling and prompt annealing. Cold forming is not feasible.
What surface finishes work on 1.2714?
Nitriding, nitride plus oxidation, hard chrome or PVD coatings raise wear resistance. The steel takes a mirror polish, better on ESR material, and should be stored under rust-preventive oil.
1.2714 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| C | 0.5 – 0.6 | 0.56 |
| Si | 0.1 – 0.4 | 0.25 |
| Mn | 0.65 – 0.95 | 0.8 |
| P | ≤ 0.03 | |
| S | ≤ 0.03 | |
| Cr | 0.8 – 1.2 | 1.05 |
| Mo | 0.35 – 0.55 | 0.47 |
| Ni | 1.5 – 1.8 | 1.65 |
| V | 0.05 – 0.15 | 0.1 |
| Fe | balance |
1.2714 QT50-54 — frequently asked
What is 1.2714 QT50-54 used for?
1.2714 QT50-54 is typically used for hammer forging dies, die blocks, forging die inserts, trim dies, die-casting die frames and holders and hot shear blades. In short: tough hot-work mold steel.
What is the yield strength of 1.2714 QT50-54?
1.2714 QT50-54 has a typical yield strength of 1,550 MPa (225 ksi) and a tensile strength of 1,800 MPa (261 ksi) — stronger than 97% of steel grades. Strength varies by condition: see the 7 listed tempers.
Is 1.2714 QT50-54 easy to machine?
Not especially — machinability is rated not recommended (12/100, worse than 99% of steel grades). Annealed material cuts easily; above about 30 HRC in the prehard condition use coated carbide, rigid clamping and high-stiffness milling at reduced feed. Leave 0.2-0.3 mm finishing stock in deep cavities.
Can 1.2714 QT50-54 be welded?
Not readily — weldability is rated poor (25/100). Repair welding with matching or dedicated die-repair filler is workable. Preheat to 300-350 °C, maintain interpass temperature and temper immediately after welding to prevent cracking.
What surface finishes work on 1.2714 QT50-54?
Nitriding, nitride plus oxidation, hard chrome or PVD coatings raise wear resistance. The steel takes a mirror polish, better on ESR material, and should be stored under rust-preventive oil.
Can 1.2714 QT50-54 be formed, bent or molded?
Hot forging or hot forming only, roughly 1050-850 °C, followed by slow cooling and prompt annealing. Cold forming is not feasible.
What is the maximum service temperature of 1.2714 QT50-54?
1.2714 QT50-54 is rated for continuous use to about 200°C (392 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between 1.2714 Prehard and 1.2714 QT50-54?
Prehard is the default condition — use the block supplied quenched and tempered to 28–34 HRC (295 HB) when the cavity is machined straight from stock and no further hardening is planned. QT50-54: use the low-temper 50–54 HRC condition for wear punches and shear blades under limited impact loading; elongation drops to 6%, service to 200 °C and machinability to 12. Yield strength is 850 MPa in Prehard versus 1,550 MPa in QT50-54.
Can FabDigit make parts in 1.2714 QT50-54?
Yes — 1.2714 QT50-54 is available for CNC machining; every part is priced by an engineer rather than instantly. Upload a STEP file to get a price and a DFM check.
Sources
- EN ISO 4957 Tool steels — ISO/CEN (2018)
- GB/T 1299 (5CrNiMo/5CrNiMoV) — SAC (2014)
- ASM Handbook Vol.1: Properties and Selection — Irons, Steels and High-Performance Alloys — ASM International (1990)
- 1.2714 / 56NiCrMoV7 hot-work die steel data sheets — Böhler / (2022)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.