PVC Flexible
Grade
also Sintra, Trovidur
Plasticizer-modified PVC for hose, cable jacketing, gaskets, sheeting and RF-welded fabrics.
Values for the Flexible condition
Other PVC grades and fills
PVC is listed in 4 conditions; see the grade overview at PVC.
- FOAM
- Flexible
- Type II
- Rigid (Type I)
Compare all 4 grades and fillsHide
| Grade · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness |
|---|---|---|---|---|---|
Free-foamed / co-extruded rigid PVC board | Low-density closed-cell rigid PVC board for signage, display, model-making and lightweight panels. | 14 | 12 | 48 Shore D | |
FlexibleThis page plasticized PVC (PVC-P), typical Shore A 80 | Plasticizer-modified PVC for hose, cable jacketing, gaskets, sheeting and RF-welded fabrics. | 15 | 300 | 30 Shore D | |
Impact-modified rigid PVC | Choose when notched impact and low-temperature toughness matter more than stiffness/HDT, e.g. exposed ducting and machine guards. | 42 | 44 | 100 | 78 Shore D |
Rigid (Type I)Default Unplasticized PVC-U, ASTM D1784 cell class 12454 | Standard grey/white unplasticized PVC sheet, pipe and machined parts for chemical tanks, ducting and fixtures. | 52 | 45 | 82 Shore D |
What is PVC Flexible?
PVC Flexible is PVC in the Flexible grade — plasticizer-modified PVC for hose, cable jacketing, gaskets, sheeting and RF-welded fabrics. PVC Flexible has a yield strength of 50 MPa (7.25 ksi) and a tensile strength of 15 MPa (2.18 ksi) — stronger than 52% of polymer grades. Elongation at break is 300% and the elastic modulus is 0.02 GPa (0.0029 Msi). PVC Flexible has a density of 1.25 g/cm³ (0.0452 lb/in³), heavier than 64% of polymer grades. Its glass-transition temperature is -25°C (-13 °F). Rigid (Type I) is the default condition FabDigit quotes; Flexible is available on request or by drawing note.
Advantages
- Forms and bends easily — 95/100, better than 99% of polymer grades
- Readily welded — 92/100, better than 97% of polymer grades
- Low embodied carbon — 2.4 kg CO₂/kg, better than 92% of polymer grades
- Good corrosion resistance — 90/100, better than 82% of polymer grades
- Low moisture uptake — 0.06%, better than 82% of polymer grades
Limitations
- Difficult to machine — 35/100, worse than 84% of polymer grades
- Limited service temperature — 65°C (149 °F), worse than 83% of polymer grades
- High mold shrinkage — 2%, worse than 81% of polymer grades
- Poor heat conductor — 0.15 W/m·K (0.0867 BTU/hr·ft·°F), worse than 80% of polymer grades
- Low stiffness — 0.02 GPa (0.0029 Msi), worse than 75% of polymer grades
PVC Flexible properties
Typical room-temperature values for PVC Flexible; 22 are specific to this condition. Other listed values are PVC reference data and may not represent this condition. Bars are the position among polymer grades.
Physical5
PVC Flexible has a density of 1.25 g/cm³ (0.0452 lb/in³), heavier than 64% of polymer grades. Its glass-transition temperature is -25°C (-13 °F).
Mechanical16
PVC Flexible has a yield strength of 50 MPa (7.25 ksi) and a tensile strength of 15 MPa (2.18 ksi) — stronger than 52% of polymer grades. Elongation at break is 300% and the elastic modulus is 0.02 GPa (0.0029 Msi).
Thermal11
PVC Flexible is rated for continuous service to 65°C (149 °F). It conducts heat at 0.15 W/m·K (0.0867 BTU/hr·ft·°F), worse than 80% of polymer grades. Thermal expansion is 200 µm/m·K (111.1 µin/in·°F).
Electrical7
PVC Flexible is an electrical insulator with a dielectric strength of 18 kV/mm (457.2 V/mil) and a resistivity of 1×10¹³ Ω·m.
Chemical & Environmental3
Corrosion resistance is excellent (90/100), better than 82% of polymer grades. UV resistance is good.
Sustainability4
Producing a kilogram of PVC Flexible takes about 67 MJ of energy and emits 2.4 kg of CO₂ — less than 95% of polymer grades. Typical recycled content is 10%.
Manufacturability7
PVC Flexible's machinability is fair (35/100, worse than 84% of polymer grades); weldability excellent (92/100); formability excellent (95/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with PVC Flexible
Is PVC easy to machine?
Machines easily with sharp, polished, high-rake carbide tools and generous chip clearance; keep cutting speeds moderate and use air blast to avoid local overheating and chlorine-releasing degradation.
Can PVC be welded?
Solvent-cements (THF/MEK based) and hot-gas or extrusion welds readily at 300–350 °C torch air; flexible PVC also RF (dielectric) and hot-bar weldable — never weld with contaminated or overheated stock.
Can PVC be formed, bent or molded?
Line-bend or thermoform at 120–150 °C sheet temperature; extrude/injection mold at 170–200 °C melt with corrosion-resistant screws and short residence time, since HCl evolution starts near 200 °C.
What surface finishes work on PVC?
Accepts sanding, flame-free polishing, screen printing and solvent-based or two-part PU paints after light abrasion; not platable by standard methods and no anodizing analogue.
PVC chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| heat stabilizer (Ca/Zn, organotin or leatin stabilizers used for clear grades | 1 – 5 | 3 |
| plasticizer (DINP/DOTP/TOTM)0 for rigid PVC-U; 25–45 phr for flexible PVC-P | 0 – 45 | 0 |
| calcium carbonate filler | 0 – 15 | 5 |
| impact modifier (CPE/MBS/acrylic)4–8 phr in Type II / PVC-HI | 0 – 10 | 0 |
| titanium dioxide (TiO2)pigment + UV screen in outdoor grades | 0 – 6 | 2 |
| lubricants / processing aids | 0.5 – 3 | 1.5 |
| vinyl chloride repeat unit (-CH2-CHCl-)PVC resin, K-value 57–70 (SG-3 to SG-8); chlorine ≈56.7 wt% of the pure polymer | ≥ 55 (balance) |
PVC Flexible — frequently asked
What is PVC Flexible used for?
PVC Flexible is typically used for plumbing and drainage pipe, window and door frames, chemical tank linings and ducting, electrical conduit and cable insulation, pipe fittings and valve bodies and wall cladding and signage sheet. In short: standard rigid plastic.
What is the yield strength of PVC Flexible?
PVC Flexible has a typical yield strength of 50 MPa (7.25 ksi) and a tensile strength of 15 MPa (2.18 ksi) — stronger than 52% of polymer grades. Strength varies by condition: see the 4 listed tempers.
Is PVC Flexible easy to machine?
Not especially — machinability is rated fair (35/100, worse than 84% of polymer grades). Machines easily with sharp, polished, high-rake carbide tools and generous chip clearance; keep cutting speeds moderate and use air blast to avoid local overheating and chlorine-releasing degradation.
Can PVC Flexible be welded?
Yes — weldability is rated excellent (92/100). Solvent-cements (THF/MEK based) and hot-gas or extrusion welds readily at 300–350 °C torch air; flexible PVC also RF (dielectric) and hot-bar weldable — never weld with contaminated or overheated stock.
What surface finishes work on PVC Flexible?
Accepts sanding, flame-free polishing, screen printing and solvent-based or two-part PU paints after light abrasion; not platable by standard methods and no anodizing analogue.
Can PVC Flexible be formed, bent or molded?
Line-bend or thermoform at 120–150 °C sheet temperature; extrude/injection mold at 170–200 °C melt with corrosion-resistant screws and short residence time, since HCl evolution starts near 200 °C.
What is the maximum service temperature of PVC Flexible?
PVC Flexible is rated for continuous use to about 65°C (149 °F), and briefly to 80°C. Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Can FabDigit make parts in PVC Flexible?
Yes — PVC Flexible is available for CNC machining, sheet metal and injection molding with instant online pricing. Upload a STEP file to get a price and a DFM check.
Sources
- ASTM D1784 — Rigid PVC and CPVC Compounds (cell classification) — ASTM International (2020)
- ASTM D1785 / D1784 pipe & sheet property requirements — ASTM International (2021)
- ISO 1163 / EN ISO 1163 Plastics — Unplasticized PVC moulding and extrusion materials — ISO (1995)
- Trovidur EN / EC rigid PVC sheet datasheet — Röchling Industrial (2023)
- Simona PVC-U / PVC-CAW sheet technical data — Simona AG (2022)
- Engineered Materials Handbook Vol. 2: Engineering Plastics — ASM International (1988)
- CAMPUS plastics database — PVC-U / PVC-P compounds — CWFG (2024)
- GB/T 4454 / GB/T 5761 PVC (2018)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.