mPP GF30
Reinforced grade
GF30 = 30 % glass-fiber reinforced
Structural mPP compound for brackets, pump housings and hot-water fittings needing stiffness and creep resistance.
Values for the GF30 condition
Other mPP grades and fills
mPP is listed in 11 conditions; see the grade overview at mPP.
Compare all 11 grades and fillsHide
| Grade · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness |
|---|---|---|---|---|---|
Propylene-based elastomer / plastomer | Very soft, low-crystallinity metallocene propylene copolymer used as modifier, elastic film and soft-touch TPO component. | — | 12 | 900 | 25 Shore D |
Impact-modified | Choose for sub-zero drop-impact requirements in housings, thin-wall crates and automotive interior parts. | 22 | 24 | 500 | 60 Shore D |
Flame-retardant, UL 94 V-0 | Required for electrical enclosures and appliance parts; FR package cuts impact strength and clarity. | 25 | 26 | 30 | 70 Shore D |
Metallocene random copolymer | Pick when you need high transparency, low-temperature seal initiation and better low-temp toughness (film, thin-wall containers, medical packaging). | 26 | 28 | 600 | — |
Antistatic / conductive | For electronics trays and dust-sensitive packaging needing controlled surface resistivity. | 27 | 28 | 15 | 72 Shore D |
Talc / mineral filled | Cheap stiffness and dimensional stability boost for housings and automotive parts where clarity is not needed. | 29 | 30 | 25 | — |
Fiber / nonwoven grade | High-MFR narrow-MWD resin for fine-denier spunbond and meltblown webs with stable spinning and soft handfeel. | 32 | 34 | 300 | 69 Shore D |
Heat-stabilized | For hot-air/hot-water contact and under-hood-adjacent parts requiring 1000+ h oven aging. | 32 | 34 | 400 | 68 Shore D |
UNFDefault Unfilled / natural | Baseline clear/natural mPP homopolymer for injection molding, sheet and CPP film where stiffness and clarity matter. | 33 | 35 | 400 | — |
Clarified / nucleated | Use for glass-clear thin-wall injection parts and faster cycles; clarifier raises stiffness and HDT slightly. | 33 | 34 | 350 | 70 Shore D |
GF30This page 30 % glass-fiber reinforced | Structural mPP compound for brackets, pump housings and hot-water fittings needing stiffness and creep resistance. | — | 80 | 3 | — |
What is mPP GF30?
mPP GF30 is mPP in the GF30 grade — structural mPP compound for brackets, pump housings and hot-water fittings needing stiffness and creep resistance. mPP GF30 has a yield strength of 33 MPa (4.79 ksi) and a tensile strength of 80 MPa (11.6 ksi) — weaker than 68% of polymer grades. Elongation at break is 3% and the elastic modulus is 6 GPa (0.87 Msi). mPP GF30 has a density of 1.13 g/cm³ (0.0408 lb/in³), lighter than 62% of polymer grades. Its glass-transition temperature is -5°C (23 °F). UNF is the default condition FabDigit quotes; GF30 is available on request or by drawing note.
Advantages
- Low moisture uptake — 0.01%, better than 97% of polymer grades
- Low embodied carbon — 2 kg CO₂/kg, better than 96% of polymer grades
- Stiff — 6 GPa (0.87 Msi), better than 89% of polymer grades
- Conducts heat well — 0.3 W/m·K (0.173 BTU/hr·ft·°F), better than 83% of polymer grades
- Good corrosion resistance — 90/100, better than 82% of polymer grades
Limitations
- Limited ductility — 3%, worse than 83% of polymer grades
- Degrades in UV without stabilisers — 25/100, worse than 76% of polymer grades
mPP GF30 properties
Typical room-temperature values for mPP GF30; 15 are specific to this condition. Other listed values are mPP reference data and may not represent this condition. Bars are the position among polymer grades.
Physical7
mPP GF30 has a density of 1.13 g/cm³ (0.0408 lb/in³), lighter than 62% of polymer grades. Its glass-transition temperature is -5°C (23 °F).
Mechanical15
mPP GF30 has a yield strength of 33 MPa (4.79 ksi) and a tensile strength of 80 MPa (11.6 ksi) — weaker than 68% of polymer grades. Elongation at break is 3% and the elastic modulus is 6 GPa (0.87 Msi).
Thermal11
mPP GF30 is rated for continuous service to 120°C (248 °F). It conducts heat at 0.3 W/m·K (0.173 BTU/hr·ft·°F), better than 83% of polymer grades. Thermal expansion is 30 µm/m·K (16.7 µin/in·°F).
Electrical7
mPP GF30 is an electrical insulator with a dielectric strength of 30 kV/mm (762 V/mil) and a resistivity of 1×10¹⁴ Ω·m.
Chemical & Environmental3
Corrosion resistance is excellent (90/100), better than 82% of polymer grades. UV resistance is poor.
Sustainability4
Producing a kilogram of mPP GF30 takes about 78 MJ of energy and emits 2 kg of CO₂ — less than 88% of polymer grades. Typical recycled content is 0%.
Manufacturability8
mPP GF30's machinability is good (55/100, worse than 64% of polymer grades); weldability good (60/100); formability very good (80/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with mPP GF30
Is mPP easy to machine?
Machines easily with sharp positive-rake tools, high speed and low feed; use coolant/air blast to avoid gumming and expect springback on tight tolerances.
Can mPP be welded?
Excellent hot-plate, hot-gas, ultrasonic, IR and spin welding with PP filler rod; no solvent bonding — surface must be flame/corona/plasma treated before adhesive or print.
Can mPP be formed, bent or molded?
Narrow MWD gives low melt elasticity: high-clarity injection molding is easy (melt 200–250 °C, mold 20–40 °C), but blow molding, extrusion foaming and deep thermoforming need higher melt strength or a broadened blend.
What surface finishes work on mPP?
Not paintable or platable as-molded; requires corona/flame/plasma activation or adhesion primer, and dyeing is not possible — use masterbatch coloring or in-mold texture/film decoration.
mPP chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| ethylene (comonomer)random-copolymer / plastomer grades; 0 for homopolymer | 0 – 12 | 3.5 |
| 1-butene / higher alpha-olefin (comonomeused in some terpolymer seal-layer grades | 0 – 8 | 0 |
| stabilizer & process additive packagephenolic/phosphite AO, acid scavenger, slip/antiblock, optional clarifier | 0.05 – 0.6 | 0.25 |
| metallocene catalyst residue (Zr, Al)ppm-level; lower ash than Z-N PP | 0 – 0.01 | 0 |
| propylenemetallocene-catalyzed polypropylene backbone; homopolymer = 100 % propylene | ≥ 88 (balance) | — |
mPP GF30 — frequently asked
What is mPP GF30 used for?
mPP GF30 is typically used for flexible packaging film, medical device components, non-woven fibers, retort packaging and heat-seal layers. In short: clearest polypropylene class; low-extractable medical PP; best heat-seal PP.
What is the yield strength of mPP GF30?
mPP GF30 has a typical yield strength of 33 MPa (4.79 ksi) and a tensile strength of 80 MPa (11.6 ksi) — weaker than 68% of polymer grades. Strength varies by condition: see the 11 listed tempers.
Is mPP GF30 easy to machine?
Reasonably — machinability is rated good (55/100, worse than 64% of polymer grades). Machines easily with sharp positive-rake tools, high speed and low feed; use coolant/air blast to avoid gumming and expect springback on tight tolerances.
Can mPP GF30 be welded?
Yes — weldability is rated good (60/100). Excellent hot-plate, hot-gas, ultrasonic, IR and spin welding with PP filler rod; no solvent bonding — surface must be flame/corona/plasma treated before adhesive or print.
What surface finishes work on mPP GF30?
Not paintable or platable as-molded; requires corona/flame/plasma activation or adhesion primer, and dyeing is not possible — use masterbatch coloring or in-mold texture/film decoration.
Can mPP GF30 be formed, bent or molded?
Narrow MWD gives low melt elasticity: high-clarity injection molding is easy (melt 200–250 °C, mold 20–40 °C), but blow molding, extrusion foaming and deep thermoforming need higher melt strength or a broadened blend.
What is the maximum service temperature of mPP GF30?
mPP GF30 is rated for continuous use to about 120°C (248 °F), and briefly to 120°C. Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between mPP UNF and mPP IM?
UNF is the default condition — baseline clear/natural mPP homopolymer for injection molding, sheet and CPP film where stiffness and clarity matter. IM: choose for sub-zero drop-impact requirements in housings, thin-wall crates and automotive interior parts. Yield strength is 33 MPa in UNF versus 22 MPa in IM.
Sources
- Lumicene metallocene polypropylene product range — TotalEnergies Polymers (2023)
- Achieve / Vistamaxx performance polymers technical data — ExxonMobil Chemical (2023)
- Metocene metallocene PP grade data — LyondellBasell (2022)
- CAMPUS plastics — polypropylene ISO 10350 datasheets — CWFG / CAMPUS consortium (2024)
- ISO 1873-1/-2 Plastics — Polypropylene (PP) moulding and extrusion materials — ISO (2019)
- GB/T 12670 (PP) (2008)
- Engineered Materials Handbook Vol. 2: Engineering Plastics — ASM International (1988)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.