YG8C SINT
Print state · default condition
ISO K30
SINT = sintered
Use the conventional vacuum liquid-phase sintered blank or rod as the cost-effective default for general heavy cutting and wear components with 2.5–5 µm coarse grain.
Values for the SINT condition
Other YG8C tempers and conditions
YG8C is listed in 3 conditions; see the grade overview at YG8C.
Compare all 3 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
Extra-coarse grain (>5 µm) rock-tool version | Pick the extra-coarse grain (>5 µm) rock-tool version for drill bits and TBM cutter teeth under heavy impact and thermal fatigue; toughness is highest but hardness and wear resistance drop. | — | 1,050 | 0 | 1,120 HV | 90 W/m·K |
SINTDefaultThis page Sintered | Use the conventional vacuum liquid-phase sintered blank or rod as the cost-effective default for general heavy cutting and wear components with 2.5–5 µm coarse grain. | — | 1,100 | 0 | 1,220 HV | 80 W/m·K |
Hot isostatic pressed | Choose sinter-HIP densification when impact loading is high and chipping resistance plus fatigue life govern; porosity is near zero and transverse rupture strength is highest. | — | 1,250 | 0 | 1,250 HV | 82 W/m·K |
What is YG8C SINT?
YG8C SINT is YG8C in the SINT condition — use the conventional vacuum liquid-phase sintered blank or rod as the cost-effective default for general heavy cutting and wear components with 2.5–5 µm coarse grain. YG8C SINT has a tensile strength of 1,100 MPa (160 ksi), stronger than 88% of ceramic grades. Elongation at break is 0% and the elastic modulus is 600 GPa (87 Msi). YG8C SINT has a density of 14.7 g/cm³ (0.531 lb/in³), heavier than 93% of ceramic grades. It melts at 1,320°C (2,408 °F).
Advantages
- Tough — resists crack growth — 15 MPa·√m (13.7 ksi·√in), better than 98% of ceramic grades
- Stiff — 600 GPa (87 Msi), better than 91% of ceramic grades
- Polishes to a fine finish — 90/100, better than 78% of ceramic grades
- Conducts heat well — 80 W/m·K (46.2 BTU/hr·ft·°F), better than 77% of ceramic grades
Limitations
- Heavy — 14.7 g/cm³ (0.531 lb/in³), worse than 93% of ceramic grades
- Needs corrosion protection — 45/100, worse than 90% of ceramic grades
- High embodied carbon — 25 kg CO₂/kg, worse than 78% of ceramic grades
YG8C SINT properties
Typical room-temperature values for YG8C SINT; 14 are specific to this condition. Other listed values are YG8C reference data and may not represent this condition. Bars are the position among ceramic grades.
Physical3
YG8C SINT has a density of 14.7 g/cm³ (0.531 lb/in³), heavier than 93% of ceramic grades. It melts at 1,320°C (2,408 °F).
Mechanical13
YG8C SINT has a tensile strength of 1,100 MPa (160 ksi), stronger than 88% of ceramic grades. Elongation at break is 0% and the elastic modulus is 600 GPa (87 Msi).
Thermal5
YG8C SINT is rated for continuous service to 600°C (1,112 °F). It conducts heat at 80 W/m·K (46.2 BTU/hr·ft·°F), better than 77% of ceramic grades. Thermal expansion is 5.2 µm/m·K (2.89 µin/in·°F).
Electrical2
YG8C SINT has an electrical resistivity of 2×10⁻⁷ Ω·m.
Chemical & Environmental2
Corrosion resistance is fair (45/100), worse than 90% of ceramic grades.
Sustainability4
Producing a kilogram of YG8C SINT takes about 320 MJ of energy and emits 25 kg of CO₂ — more than 78% of ceramic grades. Typical recycled content is 30%.
Manufacturability3
YG8C SINT's machinability is not recommended (3/100, worse than 95% of ceramic grades).
Common Calculations4
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with YG8C SINT
Is YG8C easy to machine?
After sintering, only diamond wheel grinding, EDM (wire or sinker) or laser processing is possible; conventional cutting will not work. Green or pre-sintered blanks can be turned and milled with carbide tooling before final sintering.
Can YG8C be welded?
Not fusion weldable. Join to steel bodies by copper- or silver-based brazing (for example BAg-40Cu-Zn at 700–900 °C, with a copper foil interlayer to reduce residual stress) or by vacuum brazing.
Can YG8C be formed, bent or molded?
Powder-metallurgy route only: die pressing, extrusion or injection moulding followed by liquid-phase sintering at 1380–1460 °C, optionally with 6 MPa sinter-HIP. Linear sintering shrinkage is about 18–22 %, so tooling must be oversized by the shrinkage factor.
What surface finishes work on YG8C?
Diamond lapping and polishing reach a mirror finish of Ra <0.05 µm. PVD TiN/TiAlN or CVD coatings can be applied for wear resistance, but coarse-grain substrates used in impact duty are often left uncoated.
YG8C chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Cobinder phase | 7.5 – 8.5 | 8 |
| TaC+NbCoptional additive for grain and property adjustment | 0 – 0.5 | 0.2 |
| Ctotal carbon; kept in two-phase field to avoid η phase/free C | 5.5 – 5.9 | 5.7 |
| WCcoarse grain, mean grain size 2.5–5 µm | balance | — |
YG8C SINT — frequently asked
What is YG8C SINT used for?
YG8C SINT is typically used for heavy roughing, mining bits, impact wear parts and cold heading dies. In short: coarse-grain impact grade; tough WC-8Co variant; for interrupted cuts.
What is the tensile strength of YG8C SINT?
YG8C SINT has a typical tensile strength of 1,100 MPa (160 ksi) — stronger than 88% of ceramic grades. Strength varies by condition: see the 3 listed tempers.
Is YG8C SINT easy to machine?
Not especially — machinability is rated not recommended (3/100, worse than 95% of ceramic grades). After sintering, only diamond wheel grinding, EDM (wire or sinker) or laser processing is possible; conventional cutting will not work. Green or pre-sintered blanks can be turned and milled with carbide tooling before final sintering.
Can YG8C SINT be welded?
Not fusion weldable. Join to steel bodies by copper- or silver-based brazing (for example BAg-40Cu-Zn at 700–900 °C, with a copper foil interlayer to reduce residual stress) or by vacuum brazing.
What surface finishes work on YG8C SINT?
Diamond lapping and polishing reach a mirror finish of Ra <0.05 µm. PVD TiN/TiAlN or CVD coatings can be applied for wear resistance, but coarse-grain substrates used in impact duty are often left uncoated.
Can YG8C SINT be formed, bent or molded?
Powder-metallurgy route only: die pressing, extrusion or injection moulding followed by liquid-phase sintering at 1380–1460 °C, optionally with 6 MPa sinter-HIP. Linear sintering shrinkage is about 18–22 %, so tooling must be oversized by the shrinkage factor.
What is the maximum service temperature of YG8C SINT?
YG8C SINT is rated for continuous use to about 600°C (1,112 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Sources
- ASM Handbook Vol. 2 — Properties and Selection: Nonferrous Alloys and Special-Purpose Materials (Cemented Carbides) — ASM International (1990)
- Cemented Carbide Grade Data (WC-Co straight grades) — Sandvik Hard Materials / (2022)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.