YG15 vs YG8C
Ceramic · grade comparison
YG15 and YG8C are both ceramic grades. YG15 is the stronger of the two: tensile strength 1,400 MPa (203 ksi) against 1,100 MPa (160 ksi) for YG8C, about 27% more. YG15 is the more ductile: elongation 0.3% versus 0% for YG8C, and YG8C is harder (1,220 HV vs 1,150 HV). YG15 is lighter (14 g/cm³ vs 14.7 g/cm³ for YG8C) and YG8C is stiffer (600 GPa vs 520 GPa).
YG15Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
YG8CChoose it when the part sees heat.
YG15 vs YG8C: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all ceramic grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all ceramic grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Elongation at Break
Compressive Strength
Flexural Strength
Shear Strength
Fracture Toughness (K_IC)
Hardness, Vickers
Hardness, Knoop
Hardness, Mohs
Physical
Density and transition temperatures.
Density
Porosity
Same in both: Melting Point (Solidus) 1,320°C2,408 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Same in both: Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Resistivity 2×10⁻⁷ Ω·m7.87 µΩ·in · Volume Resistivity 2×10⁻⁵ Ω·cm
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Same in both: Polishability 90 / 100 · Sintering / Firing Temperature 1,420°C2,588 °F
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Embodied Water
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every ceramic grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | YG15 | YG8C |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
YG15 vs YG8C — frequently asked
Is YG15 stronger than YG8C?
Yes. YG15 has a typical tensile strength of 1,400 MPa (203 ksi) against 1,100 MPa (160 ksi) for YG8C — about 27% more.
Which is cheaper, YG15 or YG8C?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
When should I choose YG15 over YG8C?
Pick YG15 when strength drives the design, or when the part is bent, formed or impact-loaded. Pick YG8C when the part sees heat.
Ready to make it?
Upload a CAD file and FabDigit prices the part in YG15 and YG8C side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.