Stainless Steel CN3MN SA-HIP
Heat-treated state
ASTM CN3MN · UNS J94651
Specified for critical pressure-containing or subsea valve/pump bodies where microporosity must be closed for radiographic and fatigue quality.
Values for the SA-HIP condition
Other CN3MN tempers and conditions
CN3MN is listed in 3 conditions; see the grade overview at CN3MN.
Compare all 3 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
SADefault Solution annealed ≥1120 °C and water quenched | The only condition CN3MN castings are supplied in — required by ASTM A351/A743/A744 to dissolve σ/χ phases and restore full corrosion resistance. | 300 | 620 | 45 | 180 HB | 1.9 % IACS |
SA-HIPThis page hot isostatically pressed then solution annealed and quenched | Specified for critical pressure-containing or subsea valve/pump bodies where microporosity must be closed for radiographic and fatigue quality. | 310 | 645 | 50 | 180 HB | 1.9 % IACS |
Centrifugally cast, solution annealed and quenched | Choose for cylindrical items (pipe spools, sleeves, liners) where the denser, more directionally solidified centrifugal structure gives slightly higher strength. | 320 | 650 | 42 | 190 HB | 1.9 % IACS |
What is CN3MN SA-HIP?
CN3MN SA-HIP is CN3MN heat treated to SA-HIP — specified for critical pressure-containing or subsea valve/pump bodies where microporosity must be closed for radiographic and fatigue quality. CN3MN SA-HIP has a yield strength of 310 MPa (45 ksi) and a tensile strength of 645 MPa (93.5 ksi) — weaker than 63% of stainless steel grades. Elongation at break is 50% and the elastic modulus is 195 GPa (28.3 Msi). CN3MN SA-HIP has a density of 8.06 g/cm³ (0.291 lb/in³), heavier than 98% of stainless steel grades. It melts at 1,320°C (2,408 °F). SA is the default condition FabDigit quotes; SA-HIP is available on request or by drawing note.
Advantages
- Good corrosion resistance — 90/100, better than 99% of stainless steel grades
- Tough — resists crack growth — 220 MPa·√m (200.2 ksi·√in), better than 97% of stainless steel grades
- Ductile — tolerates forming and impact — 50%, better than 90% of stainless steel grades
Limitations
- Poor heat conductor — 11.5 W/m·K (6.64 BTU/hr·ft·°F), worse than 97% of stainless steel grades
- Low electrical conductivity — 1.9 % IACS, worse than 84% of stainless steel grades
- High embodied carbon — 5.5 kg CO₂/kg, worse than 77% of stainless steel grades
CN3MN SA-HIP properties
Typical room-temperature values for CN3MN SA-HIP; 22 are specific to this condition. Other listed values are CN3MN reference data and may not represent this condition. Bars are the position among stainless steel grades.
Physical3
CN3MN SA-HIP has a density of 8.06 g/cm³ (0.291 lb/in³), heavier than 98% of stainless steel grades. It melts at 1,320°C (2,408 °F).
Mechanical16
CN3MN SA-HIP has a yield strength of 310 MPa (45 ksi) and a tensile strength of 645 MPa (93.5 ksi) — weaker than 63% of stainless steel grades. Elongation at break is 50% and the elastic modulus is 195 GPa (28.3 Msi).
Thermal6
CN3MN SA-HIP is rated for continuous service to 425°C (797 °F). It conducts heat at 11.5 W/m·K (6.64 BTU/hr·ft·°F), worse than 97% of stainless steel grades. Thermal expansion is 15.2 µm/m·K (8.44 µin/in·°F).
Electrical3
CN3MN SA-HIP conducts electricity at 1.9 % IACS, worse than 84% of stainless steel grades.
Chemical & Environmental3
Corrosion resistance is excellent (90/100), better than 99% of stainless steel grades.
Sustainability4
Producing a kilogram of CN3MN SA-HIP takes about 75 MJ of energy and emits 5.5 kg of CO₂ — more than 84% of stainless steel grades. Typical recycled content is 65%.
Manufacturability7
CN3MN SA-HIP's machinability is poor (28/100, worse than 79% of stainless steel grades); weldability very good (72/100); formability fair (45/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with CN3MN SA-HIP
Is CN3MN easy to machine?
Very gummy and strongly work-hardening — use rigid setups, sharp positive-rake carbide or coated inserts, heavy positive feed (never dwell), low-to-moderate speed and copious high-pressure coolant.
Can CN3MN be welded?
Readily welded by GTAW/GMAW/SMAW using overalloyed Ni-base filler (ERNiCrMo-3/alloy 625 or ERNiCrMo-4) to avoid Mo-depleted dendrite cores; keep interpass below ~150 °C, no preheat, no post-weld heat treatment except full re-solution if practical.
Can CN3MN be formed, bent or molded?
Supplied as castings — pour hot with generous risers and chills because the wide freezing range promotes centreline shrinkage; mandatory solution anneal at 1120–1150 °C followed by rapid water quench.
What surface finishes work on CN3MN?
Pickle and passivate (nitric-hydrofluoric) after welding or grinding to remove heat tint and restore the passive film; the alloy polishes to a bright non-magnetic finish and needs no coating in seawater service.
CN3MN chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Clow carbon to avoid sensitisation | ≤ 0.03 | 0.02 |
| Mn | ≤ 2 | 1 |
| Si | ≤ 1 | 0.6 |
| P | ≤ 0.04 | 0.02 |
| S | ≤ 0.01 | 0.01 |
| Cr | 20 – 22 | 21 |
| Ni | 23.5 – 25.5 | 24.5 |
| Modrives PREN ≈ 45–48 | 6 – 7 | 6.5 |
| Nsolid-solution strengthening + pitting resistance | 0.18 – 0.26 | 0.22 |
| Cu | ≤ 0.75 | 0.3 |
| Fe | balance | — |
CN3MN SA-HIP — frequently asked
What is CN3MN SA-HIP used for?
CN3MN SA-HIP is typically used for chemical pumps, acid transfer valves and corrosive slurry handling components. In short: nitrogen-strengthened CN3M; high sulfuric-acid resistance; super-austenitic casting grade.
What is the yield strength of CN3MN SA-HIP?
CN3MN SA-HIP has a typical yield strength of 310 MPa (45 ksi) and a tensile strength of 645 MPa (93.5 ksi) — weaker than 63% of stainless steel grades. Strength varies by condition: see the 3 listed tempers.
Is CN3MN SA-HIP easy to machine?
Not especially — machinability is rated poor (28/100, worse than 79% of stainless steel grades). Very gummy and strongly work-hardening — use rigid setups, sharp positive-rake carbide or coated inserts, heavy positive feed (never dwell), low-to-moderate speed and copious high-pressure coolant.
Can CN3MN SA-HIP be welded?
Yes — weldability is rated very good (72/100). Readily welded by GTAW/GMAW/SMAW using overalloyed Ni-base filler (ERNiCrMo-3/alloy 625 or ERNiCrMo-4) to avoid Mo-depleted dendrite cores; keep interpass below ~150 °C, no preheat, no post-weld heat treatment except full re-solution if practical.
What surface finishes work on CN3MN SA-HIP?
Pickle and passivate (nitric-hydrofluoric) after welding or grinding to remove heat tint and restore the passive film; the alloy polishes to a bright non-magnetic finish and needs no coating in seawater service.
Can CN3MN SA-HIP be formed, bent or molded?
Supplied as castings — pour hot with generous risers and chills because the wide freezing range promotes centreline shrinkage; mandatory solution anneal at 1120–1150 °C followed by rapid water quench.
What is the maximum service temperature of CN3MN SA-HIP?
CN3MN SA-HIP is rated for continuous use to about 425°C (797 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between CN3MN-SA and CN3MN CENT-SA?
SA is the default condition — the only condition CN3MN castings are supplied in — required by ASTM A351/A743/A744 to dissolve σ/χ phases and restore full corrosion resistance. CENT-SA: choose for cylindrical items (pipe spools, sleeves, liners) where the denser, more directionally solidified centrifugal structure gives slightly higher strength. Yield strength is 300 MPa in SA versus 320 MPa in CENT-SA.
Sources
- ASTM A351/A351M — Castings, Austenitic, for Pressure-Containing Parts — ASTM International (2018)
- ASTM A743/A743M and A744/A744M — Corrosion-Resistant Iron-Chromium-Nickel Castings — ASTM International (2021)
- ASM Handbook Vol.1 — Cast Stainless Steels — ASM International (1990)
- Steel Castings Handbook, Supplement 8 — High Alloy Data Sheets, Corrosion Series — Steel Founders' Society of America (2004)
- AL-6XN Alloy (UNS N08367) data sheet — wrought analogue property reference — ATI (2020)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.