TPS PHA-BLEND
Matrix
Choose where marine/soil biodegradation of the whole compound is required, accepting higher resin cost.
Values for the PHA-BLEND condition
Other TPS grades and fills
TPS is listed in 8 conditions; see the grade overview at TPS.
Compare all 8 grades and fillsHide
| Grade · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness |
|---|---|---|---|---|---|
Extruded starch foam | Water-steam expanded starch foam replacing EPS loose-fill and protective packaging; dissolves in water. | 0.08 | 0.1 | 8 | — |
Soft / high-plasticizer TPS | Pick for flexible film, bags and cushioning where elongation matters more than stiffness. | 2 | 3 | 110 | 25 Shore D |
PHA-BLENDThis page TPS/PHA blend (20–50% starch) | Choose where marine/soil biodegradation of the whole compound is required, accepting higher resin cost. | 16 | 18 | 12 | 65 Shore D |
TPS/PBAT compostable blend (30–60% starch) | The dominant commercial form — blown-film grade for shopping/compost bags and mulch film; starch cuts cost, PBAT gives toughness and water tolerance. | — | 20 | 350 | — |
TPS/PBS blend (20–50% starch) | Balanced stiffness/toughness compostable compound for injection-moulded tableware and thermoformed trays. | 20 | 25 | 90 | 58 Shore D |
Natural-fibre / cellulose reinforced TPS | Pick for stiffer, more dimensionally stable and less moisture-sensitive moulded parts (pots, trays, packaging inserts). | — | 20 | 4 | — |
Rigid / low-plasticizer TPS | Pick for injection-moulded rigid disposables (cutlery, trays) where stiffness matters and brittleness is acceptable. | 22 | 25 | 6 | 68 Shore D |
TPS/PLA blend (20–40% starch) | Pick when rigidity and clarity-free structural disposables are needed at lower resin cost than neat PLA. | — | 32 | 5 | — |
What is TPS PHA-BLEND?
TPS PHA-BLEND is TPS in the PHA-BLEND condition — choose where marine/soil biodegradation of the whole compound is required, accepting higher resin cost. TPS PHA-BLEND has a yield strength of 16 MPa (2.32 ksi) and a tensile strength of 18 MPa (2.61 ksi) — weaker than 83% of polymer grades. Elongation at break is 12% and the elastic modulus is 1.4 GPa (0.203 Msi). TPS PHA-BLEND has a density of 1.32 g/cm³ (0.0477 lb/in³), heavier than 72% of polymer grades. Its glass-transition temperature is 10°C (50 °F).
Advantages
- Low embodied carbon — 1.4 kg CO₂/kg, better than 99% of polymer grades
Limitations
- Needs corrosion protection — 30/100, worse than 100% of polymer grades
- Absorbs moisture — dry before molding — 35%, worse than 100% of polymer grades
- Hard to polish — 25/100, worse than 90% of polymer grades
- Low strength — 16 MPa (2.32 ksi), worse than 83% of polymer grades
- Limited service temperature — 70°C (158 °F), worse than 77% of polymer grades
TPS PHA-BLEND properties
Typical room-temperature values for TPS PHA-BLEND; 29 are specific to this condition. Other listed values are TPS reference data and may not represent this condition. Bars are the position among polymer grades.
Physical7
TPS PHA-BLEND has a density of 1.32 g/cm³ (0.0477 lb/in³), heavier than 72% of polymer grades. Its glass-transition temperature is 10°C (50 °F).
Mechanical12
TPS PHA-BLEND has a yield strength of 16 MPa (2.32 ksi) and a tensile strength of 18 MPa (2.61 ksi) — weaker than 83% of polymer grades. Elongation at break is 12% and the elastic modulus is 1.4 GPa (0.203 Msi).
Thermal11
TPS PHA-BLEND is rated for continuous service to 70°C (158 °F). It conducts heat at 0.2 W/m·K (0.116 BTU/hr·ft·°F), worse than 56% of polymer grades. Thermal expansion is 150 µm/m·K (83.3 µin/in·°F).
Electrical5
TPS PHA-BLEND is an electrical insulator with a dielectric strength of 15 kV/mm (381 V/mil) and a resistivity of 1×10¹² Ω·m.
Chemical & Environmental3
Corrosion resistance is poor (30/100), worse than 100% of polymer grades. UV resistance is fair.
Sustainability4
Producing a kilogram of TPS PHA-BLEND takes about 25 MJ of energy and emits 1.4 kg of CO₂ — less than 100% of polymer grades. Typical recycled content is 0%.
Manufacturability8
TPS PHA-BLEND's machinability is fair (50/100, worse than 73% of polymer grades); weldability good (55/100); formability fair (40/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with TPS PHA-BLEND
Is TPS easy to machine?
Machines poorly — soft and gummy, absorbs coolant water; use sharp tools, high rake, dry cutting and light passes, and expect swelling/dimensional drift with humidity.
Can TPS be welded?
Heat-seals and hot-plate/ultrasonic welds at low temperature (110–150 °C); solvent bonding with water or aqueous adhesives is possible because of its hydrophilicity.
Can TPS be formed, bent or molded?
Extrude/inject at 110–170 °C melt with degassing (water vapour) and low back pressure; degradation and browning start above ~180 °C, so keep short residence time; blown film runs best in PBAT/PLA blends.
What surface finishes work on TPS?
Water-based inks and coatings adhere well; a barrier lacquer or PBAT skin is usually needed to control moisture pickup; not paintable with solvent systems that dissolve the plasticizer.
TPS chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| starch (amylose+amylopectin, maize/potatdry basis; amylose 20–30% of starch typical | 55 – 80 | 68 |
| glycerol (plasticizer)may be partly replaced by sorbitol, urea, glycols | 15 – 35 | 25 |
| waterco-plasticizer; equilibrium content varies with RH | 3 – 15 | 6 |
| processing aids / emulsifier / lubricantlecithin, stearates, mono-glycerides | 0.5 – 3 | 1 |
TPS PHA-BLEND — frequently asked
What is TPS PHA-BLEND used for?
TPS PHA-BLEND is typically used for biodegradable shopping bags, loose-fill packaging foam, PLA/PBS cost-reduction blends and agricultural mulch film. In short: lowest-cost bio-based resin; fully compostable blend base; moisture-sensitive, low strength.
What is the yield strength of TPS PHA-BLEND?
TPS PHA-BLEND has a typical yield strength of 16 MPa (2.32 ksi) and a tensile strength of 18 MPa (2.61 ksi) — weaker than 83% of polymer grades. Strength varies by condition: see the 8 listed tempers.
Is TPS PHA-BLEND easy to machine?
Reasonably — machinability is rated fair (50/100, worse than 73% of polymer grades). Machines poorly — soft and gummy, absorbs coolant water; use sharp tools, high rake, dry cutting and light passes, and expect swelling/dimensional drift with humidity.
Can TPS PHA-BLEND be welded?
Yes — weldability is rated good (55/100). Heat-seals and hot-plate/ultrasonic welds at low temperature (110–150 °C); solvent bonding with water or aqueous adhesives is possible because of its hydrophilicity.
What surface finishes work on TPS PHA-BLEND?
Water-based inks and coatings adhere well; a barrier lacquer or PBAT skin is usually needed to control moisture pickup; not paintable with solvent systems that dissolve the plasticizer.
Can TPS PHA-BLEND be formed, bent or molded?
Extrude/inject at 110–170 °C melt with degassing (water vapour) and low back pressure; degradation and browning start above ~180 °C, so keep short residence time; blown film runs best in PBAT/PLA blends.
What is the maximum service temperature of TPS PHA-BLEND?
TPS PHA-BLEND is rated for continuous use to about 70°C (158 °F), and briefly to 90°C. Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Sources
- Biodegradable Multiphase Systems Based on Plasticized Starch (Avérous, J. Macromol. Sci. Part C) — Taylor & Francis (2004)
- Materials and the Environment: Eco-Informed Material Choice — Butterworth-Heinemann (Ashby) (2021)
- Solanyl potato-starch biopolymer compounds — Rodenburg Biopolymers (2023)
- BIOPLAST starch-based compounds (film & injection grades) — BIOTEC GmbH (2023)
- Mater-Bi starch-based bioplastic family data — Novamont (2023)
- EN 13432 / GB/T 19277 compostability requirements — CEN / SAC (2011)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.