PBT vs PCT
Polymer · grade comparison
PBT and PCT are both polymer grades. PBT is the stronger of the two: yield strength 55 MPa (7.98 ksi) against 52 MPa (7.54 ksi) for PCT, about 6% more. PBT is the more ductile: elongation 100% versus 30% for PCT. PCT is lighter (1.23 g/cm³ vs 1.31 g/cm³ for PBT) and PBT is stiffer (2.6 GPa vs 2.1 GPa). On the shop floor, PBT machines more easily (68 vs 55 out of 100), PBT welds better (very good vs good), and PBT sits in a lower cost tier (standard, $$) than PCT (high, $$$$).
PBTChoose it when strength drives the design, or when the part is bent, formed or impact-loaded.
PCTChoose it when weight is the constraint, or when the part sees heat.
PBT vs PCT: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Compressive Modulus
Flexural Strength
Flexural Modulus
Shear Strength
Fracture Toughness (K_IC)
Izod Impact, Notched
Hardness, Shore D
Hardness, Rockwell M
Same in both: Poisson's Ratio 0.4 · Tensile Strength (Ultimate) 55 MPa8 ksi · Hardness, Rockwell R 118 HRR
Physical
Density and transition temperatures.
Density
Melting Temperature (Tm)
Glass Transition (Tg)
Water Absorption (Saturation)
Refractive Index
Same in both: Water Absorption (24 h) 0.09%
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Heat Deflection Temp. @ 0.45 MPa
Heat Deflection Temp. @ 1.8 MPa
Vicat Softening Point (B50)
Limiting Oxygen Index
Max Service Temperature (short-term)
Same in both: Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Dielectric Strength
Dielectric Constant (1 MHz)
Dissipation Factor (1 MHz)
Surface Resistivity
Comparative Tracking Index (CTI)
Same in both: Electrical Resistivity 1×10¹⁴ Ω·m3.94×10²¹ µΩ·in · Volume Resistivity 1×10¹⁶ Ω·cm
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
UV / Weathering Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Polishability
Mold Shrinkage
Melt Flow Rate
Processing Melt Temperature (typ.)
Mold Temperature (typ.)
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Same in both: Thermal Diffusivity 0.1 mm²/s · Thermal Shock Resistance Index 0
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | PBT | PCT |
|---|---|---|
| Injection molding | Yes | — |
| Default condition | Unfilled | — |
| Relative cost | $$ Standard | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
| Chrome Plating (Plastic) | Yes | — |
| EMI Shielding Coating | Yes | — |
| Soft Touch Coating | Yes | — |
| Spray Painting | Yes | — |
| UV Coating | Yes | — |
PBT vs PCT — frequently asked
Is PBT stronger than PCT?
Yes. PBT has a typical yield strength of 55 MPa (7.98 ksi) against 52 MPa (7.54 ksi) for PCT — about 6% more. Tensile strength is 55 MPa (7.98 ksi) vs 55 MPa (7.98 ksi).
Which is cheaper, PBT or PCT?
PBT is the lower-cost material: it sits in the standard tier ($$) while PCT is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, PBT or PCT?
PBT, by a small margin. Both rate good for machinability — 68/100 against 55/100 for PCT; for welding the order is PBT first (very good, 70/100) then PCT (good, 60/100).