Stainless Steel Almar 362-H1050
Precip hard
UNS S46020
H1050 = aged 565 °C / 4 h
Over-aged temper for maximum toughness, best stress-corrosion behaviour and easiest machining of the aged conditions.
Values for the H1050 condition
Other Almar 362 tempers and conditions
Almar 362 is listed in 6 conditions; see the grade overview at Almar 362.
Compare all 6 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
Solution annealed | Choose for blanking, deep drawing, cold forming and machining before the single low-temperature aging cycle. | 760 | 965 | 18 | 30 HRC | — |
H1050This page Aged 565 °C / 4 h | Over-aged temper for maximum toughness, best stress-corrosion behaviour and easiest machining of the aged conditions. | 930 | 1,035 | 18 | 32 HRC | — |
Cold drawn / cold rolled in annealed temper | Cold-worked mill product used where extra unaged strength or tight bar/strip tolerance is needed before aging. | 965 | 1,105 | 10 | 34 HRC | 2.2 % IACS |
Aged 540 °C / 4 h | Balanced condition when toughness, transverse ductility and moderate strength matter more than peak load capacity. | 1,035 | 1,105 | 17 | 35 HRC | — |
Aged 510 °C / 4 h | Slight strength give-back from H900 for better ductility and notch toughness. | 1,140 | 1,205 | 16 | 38 HRC | — |
H900Default Aged 482 °C (900 °F) for 1 h, peak hardness | Standard peak-strength condition: highest tensile/yield with useful ductility, for springs, shafts and fasteners. | 1,205 | 1,275 | 15 | 40 HRC | — |
What is Almar 362-H1050?
Almar 362-H1050 is Almar 362 in the H1050 condition — over-aged temper for maximum toughness, best stress-corrosion behaviour and easiest machining of the aged conditions. Almar 362-H1050 has a yield strength of 930 MPa (135 ksi) and a tensile strength of 1,035 MPa (150 ksi) — stronger than 98% of stainless steel grades. Elongation at break is 18% and the elastic modulus is 200 GPa (29 Msi). Almar 362-H1050 has a density of 7.76 g/cm³ (0.28 lb/in³), lighter than 58% of stainless steel grades. It melts at 1,400°C (2,552 °F). H900 is the default condition FabDigit quotes; H1050 is available on request or by drawing note.
Advantages
- High strength — 930 MPa (135 ksi), better than 98% of stainless steel grades
Limitations
- Limited formability — 15/100, worse than 91% of stainless steel grades
- Limited ductility — 18%, worse than 83% of stainless steel grades
- Low fracture toughness — 80 MPa·√m (72.8 ksi·√in), worse than 79% of stainless steel grades
Almar 362-H1050 properties
Typical room-temperature values for Almar 362-H1050; 13 are specific to this condition. Other listed values are Almar 362 reference data and may not represent this condition. Bars are the position among stainless steel grades.
Physical3
Almar 362-H1050 has a density of 7.76 g/cm³ (0.28 lb/in³), lighter than 58% of stainless steel grades. It melts at 1,400°C (2,552 °F).
Mechanical16
Almar 362-H1050 has a yield strength of 930 MPa (135 ksi) and a tensile strength of 1,035 MPa (150 ksi) — stronger than 98% of stainless steel grades. Elongation at break is 18% and the elastic modulus is 200 GPa (29 Msi).
Thermal6
Almar 362-H1050 is rated for continuous service to 510°C (950 °F). It conducts heat at 16.5 W/m·K (9.53 BTU/hr·ft·°F), better than 70% of stainless steel grades. Thermal expansion is 10.8 µm/m·K (6 µin/in·°F).
Electrical3
Almar 362-H1050 conducts electricity at 2.2 % IACS, worse than 61% of stainless steel grades.
Chemical & Environmental3
Corrosion resistance is good (57/100), worse than 66% of stainless steel grades.
Sustainability4
Producing a kilogram of Almar 362-H1050 takes about 58 MJ of energy and emits 4.6 kg of CO₂ — more than 66% of stainless steel grades. Typical recycled content is 40%.
Manufacturability6
Almar 362-H1050's machinability is poor (32/100, worse than 62% of stainless steel grades); weldability good (60/100); formability poor (15/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with Almar 362-H1050
Is Almar 362 easy to machine?
Machine in the annealed condition with rigid setups, positive-rake carbide, heavy feeds and flood coolant; expect ~35–45 % of AISI 1212 and account for ~0.05–0.1 % growth on aging.
Can Almar 362 be welded?
GTAW/PAW autogenously or with matching/347 filler; keep heat input low, then re-solution-anneal and age for full properties (a straight age recovers most strength).
Can Almar 362 be formed, bent or molded?
Cold form, bend and deep-draw in the annealed martensitic temper — it is notably more formable than 17-4 PH — then harden with a single low-temperature age with minimal distortion.
What surface finishes work on Almar 362?
Takes a fine mechanical polish and passivates per ASTM A967; avoid hydrogen-charging plating processes in peak-aged tempers or bake at 190 °C after plating.
Almar 362 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Clow carbon for toughness and formability | ≤ 0.05 | 0.03 |
| Mn | ≤ 0.5 | 0.3 |
| Si | ≤ 0.3 | 0.2 |
| P | ≤ 0.04 | — |
| S | ≤ 0.03 | — |
| Cr | 14 – 15 | 14.5 |
| Ni | 6 – 7 | 6.5 |
| TiNi3Ti precipitation hardener | 0.55 – 0.9 | 0.8 |
| Fe | balance | — |
Almar 362-H1050 — frequently asked
What is Almar 362-H1050 used for?
Almar 362-H1050 is typically used for fasteners, shafts, cutlery-grade components and industrial hardware. In short: most formable PH stainless; low-nickel 17-4 PH alternative; single-step age hardening.
What is the yield strength of Almar 362-H1050?
Almar 362-H1050 has a typical yield strength of 930 MPa (135 ksi) and a tensile strength of 1,035 MPa (150 ksi) — stronger than 98% of stainless steel grades. Strength varies by condition: see the 6 listed tempers.
Is Almar 362-H1050 easy to machine?
Not especially — machinability is rated poor (32/100, worse than 62% of stainless steel grades). Machine in the annealed condition with rigid setups, positive-rake carbide, heavy feeds and flood coolant; expect ~35–45 % of AISI 1212 and account for ~0.05–0.1 % growth on aging.
Can Almar 362-H1050 be welded?
Yes — weldability is rated good (60/100). GTAW/PAW autogenously or with matching/347 filler; keep heat input low, then re-solution-anneal and age for full properties (a straight age recovers most strength).
What surface finishes work on Almar 362-H1050?
Takes a fine mechanical polish and passivates per ASTM A967; avoid hydrogen-charging plating processes in peak-aged tempers or bake at 190 °C after plating.
Can Almar 362-H1050 be formed, bent or molded?
Cold form, bend and deep-draw in the annealed martensitic temper — it is notably more formable than 17-4 PH — then harden with a single low-temperature age with minimal distortion.
What is the maximum service temperature of Almar 362-H1050?
Almar 362-H1050 is rated for continuous use to about 510°C (950 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between Almar 362-H900 and Almar 362-A?
H900 is the default condition — standard peak-strength condition: highest tensile/yield with useful ductility, for springs, shafts and fasteners. A: choose for blanking, deep drawing, cold forming and machining before the single low-temperature aging cycle. Yield strength is 1,205 MPa in H900 versus 760 MPa in A.
Sources
- Almar 362 Stainless (UNS S36200) alloy data — Carpenter Technology (2020)
- ASM Handbook Vol. 1: Properties and Selection — Irons, Steels, and High-Performance Alloys — ASM International (1990)
- ASM Handbook Vol. 13B: Corrosion — Materials — ASM International (2005)
- ASTM A564/A564M — Hot-Rolled and Cold-Finished Age-Hardening Stainless Steel Bars and Shapes — ASTM International (2019)
- SAE/ASTM Unified Numbering System for Metals and Alloys (UNS S36200) — SAE/ASTM (2017)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.