Precious Metal Pt90Ir10-H02
Supply condition
ASTM B562 · EN PtIr10
H02 = half hard
Compromise temper for marker bands, contacts and stamped parts needing strength with some residual ductility.
Values for the H02 condition
Other Pt90Ir10 tempers and conditions
Pt90Ir10 is listed in 6 conditions; see the grade overview at Pt90Ir10.
Compare all 6 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
AnnealedDefault fully softened (≈1000–1200 °C, air or H2) | Standard stocked condition for wire, ribbon, sheet and tubing that must be formed, coiled, swaged or welded. | 210 | 380 | 27 | 105 HB | — |
Quarter hard | Pick when parts still need mild bending but require more spring-back control and handling stiffness than soft temper. | 420 | 550 | 12 | 143 HB | 6.8 % IACS |
Stress relieved | Used to stabilise dimensions and reduce spring-back in formed electrodes/standards while retaining most cold-work strength. | 480 | 620 | 10 | 166 HB | 6.9 % IACS |
H02This page Half hard | Compromise temper for marker bands, contacts and stamped parts needing strength with some residual ductility. | 570 | 700 | 6 | 180 HB | 6.7 % IACS |
Full hard | Choose for stiff guidewires, probe tips, pen nib tipping stock and electrodes needing maximum strength and wear resistance. | 830 | 950 | 2.5 | 23 HRC | 6.6 % IACS |
Spring hard | Fine wire for springs, coils and stylus/contact elements where elastic limit matters more than ductility. | 930 | 1,050 | 1.5 | 28 HRC | 6.5 % IACS |
What is Pt90Ir10-H02?
Pt90Ir10-H02 is Pt90Ir10 supplied in the H02 condition — compromise temper for marker bands, contacts and stamped parts needing strength with some residual ductility. Pt90Ir10-H02 has a yield strength of 570 MPa (82.7 ksi) and a tensile strength of 700 MPa (102 ksi) — stronger than 97% of precious metal grades. Elongation at break is 6% and the elastic modulus is 202 GPa (29.3 Msi). Pt90Ir10-H02 has a density of 21.54 g/cm³ (0.778 lb/in³), heavier than 99% of precious metal grades. It melts at 1,780°C (3,236 °F). Annealed is the default condition FabDigit quotes; H02 is available on request or by drawing note.
Advantages
- Stiff — 202 GPa (29.3 Msi), better than 98% of precious metal grades
- High strength — 570 MPa (82.7 ksi), better than 97% of precious metal grades
- Good corrosion resistance — 99/100, better than 93% of precious metal grades
- High service temperature — 550°C (1,022 °F), better than 84% of precious metal grades
Limitations
- Heavy — 21.54 g/cm³ (0.778 lb/in³), worse than 99% of precious metal grades
- Poor heat conductor — 30 W/m·K (17.3 BTU/hr·ft·°F), worse than 94% of precious metal grades
- Limited ductility — 6%, worse than 93% of precious metal grades
- High embodied carbon — 14,500 kg CO₂/kg, worse than 92% of precious metal grades
- Limited formability — 45/100, worse than 91% of precious metal grades
Pt90Ir10-H02 properties
Typical room-temperature values for Pt90Ir10-H02; 19 are specific to this condition. Other listed values are Pt90Ir10 reference data and may not represent this condition. Bars are the position among precious metal grades.
Physical3
Pt90Ir10-H02 has a density of 21.54 g/cm³ (0.778 lb/in³), heavier than 99% of precious metal grades. It melts at 1,780°C (3,236 °F).
Mechanical11
Pt90Ir10-H02 has a yield strength of 570 MPa (82.7 ksi) and a tensile strength of 700 MPa (102 ksi) — stronger than 97% of precious metal grades. Elongation at break is 6% and the elastic modulus is 202 GPa (29.3 Msi).
Thermal6
Pt90Ir10-H02 is rated for continuous service to 550°C (1,022 °F). It conducts heat at 30 W/m·K (17.3 BTU/hr·ft·°F), worse than 94% of precious metal grades. Thermal expansion is 8.8 µm/m·K (4.89 µin/in·°F).
Electrical3
Pt90Ir10-H02 conducts electricity at 6.7 % IACS, worse than 90% of precious metal grades.
Chemical & Environmental3
Corrosion resistance is excellent (99/100), better than 93% of precious metal grades.
Sustainability4
Producing a kilogram of Pt90Ir10-H02 takes about 250,000 MJ of energy and emits 14,500 kg of CO₂ — more than 95% of precious metal grades. Typical recycled content is 45%.
Manufacturability8
Pt90Ir10-H02's machinability is poor (32/100, worse than 80% of precious metal grades); weldability good (60/100); formability fair (45/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with Pt90Ir10-H02
Is Pt90Ir10 easy to machine?
Very gummy and rapidly work-hardening: use sharp, high-positive-rake carbide or PCD tools, light-but-positive feeds, flood coolant, and collect all swarf/coolant for refining.
Can Pt90Ir10 be welded?
Excellent for resistance, laser and micro-TIG welding autogenously in argon; keep the joint clean of sulphur, lead, silicon and carbon contamination which cause hot cracking.
Can Pt90Ir10 be formed, bent or molded?
Highly ductile when annealed — cold drawn to <25 µm wire and rolled to thin foil, with interstage anneals near 1000–1100 °C after roughly 60–75 % reduction.
What surface finishes work on Pt90Ir10?
Polishes to a durable mirror without tarnish or plating; electropolishing, Pt-black deposition or laser texturing are used on electrode surfaces; no anodizing or protective coating needed.
Pt90Ir10 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Irsolid-solution hardener | 9.5 – 10.5 | 10 |
| Other PGM + base metals (total)Rh, Pd, Ru, Fe, Cu, Ni impurities; high-purity grades ≤0.05 % | ≤ 0.1 | 0.05 |
| Pt | ≥ 89.4 (balance) | — |
Pt90Ir10-H02 — frequently asked
What is Pt90Ir10-H02 used for?
Pt90Ir10-H02 is typically used for fountain pen nib tipping, spark plug electrodes, surgical wire and reference standards. In short: hardest common Pt-Ir grade; tarnish-free to 1200 °C; reference-standard platinum alloy.
What is the yield strength of Pt90Ir10-H02?
Pt90Ir10-H02 has a typical yield strength of 570 MPa (82.7 ksi) and a tensile strength of 700 MPa (102 ksi) — stronger than 97% of precious metal grades. Strength varies by condition: see the 6 listed tempers.
Is Pt90Ir10-H02 easy to machine?
Not especially — machinability is rated poor (32/100, worse than 80% of precious metal grades). Very gummy and rapidly work-hardening: use sharp, high-positive-rake carbide or PCD tools, light-but-positive feeds, flood coolant, and collect all swarf/coolant for refining.
Can Pt90Ir10-H02 be welded?
Yes — weldability is rated good (60/100). Excellent for resistance, laser and micro-TIG welding autogenously in argon; keep the joint clean of sulphur, lead, silicon and carbon contamination which cause hot cracking.
What surface finishes work on Pt90Ir10-H02?
Polishes to a durable mirror without tarnish or plating; electropolishing, Pt-black deposition or laser texturing are used on electrode surfaces; no anodizing or protective coating needed.
Can Pt90Ir10-H02 be formed, bent or molded?
Highly ductile when annealed — cold drawn to <25 µm wire and rolled to thin foil, with interstage anneals near 1000–1100 °C after roughly 60–75 % reduction.
What is the maximum service temperature of Pt90Ir10-H02?
Pt90Ir10-H02 is rated for continuous use to about 550°C (1,022 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between Pt90Ir10 Annealed and Pt90Ir10 Spring?
Annealed is the default condition — standard stocked condition for wire, ribbon, sheet and tubing that must be formed, coiled, swaged or welded. Spring: fine wire for springs, coils and stylus/contact elements where elastic limit matters more than ductility. Yield strength is 210 MPa in Annealed versus 930 MPa in Spring.
Sources
- ASTM B562 — Refined Platinum — ASTM International (2020)
- ASTM F2181 / F560-family specifications for implantable precious-metal wire — ASTM International (2021)
- ASM Handbook Vol. 2 — Properties and Selection: Nonferrous Alloys (Precious Metals) — ASM International (1990)
- Platinum-Iridium alloy technical data — Johnson Matthey Noble Metals (2022)
- Precious metal alloys for medical and electrical applications — Heraeus / Deringer-Ney (2023)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.