Aluminum 3003 vs 3103
Aluminum · grade comparison
Aluminum 3003 and 3103 are both aluminum grades, both corrosion resistant al. 3003 is the stronger of the two: yield strength 145 MPa (21 ksi) against 130 MPa (18.9 ksi) for 3103, about 12% more. 3003 is the more ductile: elongation 10% versus 7% for 3103. 3003 runs hotter in service (150°C vs 120°C continuous). On the shop floor, 3003 machines more easily (45 vs 35 out of 100).
3003Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
3003 vs 3103: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Hardness, Brinell
Hardness, Vickers
Same in both: Bulk Modulus 69 GPa10 Msi · Poisson's Ratio 0.33 · Tensile Strength (Ultimate) 150 MPa21.8 ksi · Fatigue Strength (Endurance Limit) 62 MPa9 ksi
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 2.73 g/cm³0.1 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 893 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.2 µm/m·K12.9 µin/in·°F · Latent Heat of Fusion 390 J/g168 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.83 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Brazeability / Solderability
Polishability
Machinability Rating (AISI 1212 = 100 %)
Same in both: Weldability 90 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 35%
Common Calculations
Ratios derived from the values above.
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Specific Strength (UTS / density) 55 kN·m/kg · Thermal Shock Resistance Index 15
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 3003 | 3103 |
|---|---|---|
| CNC machining | Yes | — |
| Default condition | — | — |
| Relative cost | $ Budget | $ Budget |
| Min. machined wall | 0.5 mm | — |
| Best machined surface | Ra 0.8 µm | — |
| DLC | Yes | — |
Both are offered for Sheet metal. They share 15 finishes: Anodizing Type II, Cerakote, Chem Film (Alodine), E-Coating, Electroless Nickel (EN), Electropolishing, Epoxy Coating, Gold Plating, Hard Anodize Type III w/ PTFE, Hard Anodizing Type III, Nickel Plating, PTFE Coating and 3 more.
3003 vs 3103 — frequently asked
Is 3003 stronger than 3103?
Yes. 3003 has a typical yield strength of 145 MPa (21 ksi) against 130 MPa (18.9 ksi) for 3103 — about 12% more. Tensile strength is 150 MPa (21.8 ksi) vs 150 MPa (21.8 ksi).
Which is cheaper, 3003 or 3103?
Both sit in the same relative cost tier ($, budget); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 3003 or 3103?
3003, by a small margin. Both rate fair for machinability — 45/100 against 35/100 for 3103.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 3003 and 3103 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.