Cobalt-Chrome Alloy Stellite 20 OAW-DEP
Print state
OAW-DEP = as-Deposited
Choose for hand-applied hardfacing of valve seats and tool edges where a thin, low-dilution layer of maximum hardness is wanted.
Values for the OAW-DEP condition
Other Stellite 20 tempers and conditions
Stellite 20 is listed in 3 conditions; see the grade overview at Stellite 20.
Compare all 3 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
OAW-DEPThis page As-Deposited | Choose for hand-applied hardfacing of valve seats and tool edges where a thin, low-dilution layer of maximum hardness is wanted. | 420 | 450 | 0.5 | 53 HRC | 1.8 % IACS |
AS-CASTDefault cast hardfacing rod / cast part | Standard supply form: chill-cast bare rod for oxy-acetylene or GTAW hardfacing, and small cast wear parts. | 450 | 480 | 0.5 | 55 HRC | 1.8 % IACS |
PTA / Plasma Transferred Arc powder overlay | Choose for automated, thick (2–6 mm), metallurgically bonded overlays on valve seats, pump sleeves and drilling tools. | 450 | 480 | 0.5 | 54 HRC | 1.8 % IACS |
What is Stellite 20 OAW-DEP?
Stellite 20 OAW-DEP is Stellite 20 in the OAW-DEP condition — choose for hand-applied hardfacing of valve seats and tool edges where a thin, low-dilution layer of maximum hardness is wanted. Stellite 20 OAW-DEP has a yield strength of 420 MPa (60.9 ksi) and a tensile strength of 450 MPa (65.3 ksi) — weaker than 96% of cobalt-chrome alloy grades. Elongation at break is 0.5% and the elastic modulus is 245 GPa (35.5 Msi). Stellite 20 OAW-DEP has a density of 8.98 g/cm³ (0.324 lb/in³), heavier than 91% of cobalt-chrome alloy grades. It melts at 1,150°C (2,102 °F). AS-CAST is the default condition FabDigit quotes; OAW-DEP is available on request or by drawing note.
Limitations
- Low fracture toughness — 9 MPa·√m (8.19 ksi·√in), worse than 100% of cobalt-chrome alloy grades
- Low strength — 420 MPa (60.9 ksi), worse than 96% of cobalt-chrome alloy grades
- Limited ductility — 0.5%, worse than 89% of cobalt-chrome alloy grades
- Needs corrosion protection — 63/100, worse than 86% of cobalt-chrome alloy grades
- High embodied carbon — 16 kg CO₂/kg, worse than 84% of cobalt-chrome alloy grades
Stellite 20 OAW-DEP properties
Typical room-temperature values for Stellite 20 OAW-DEP; 22 are specific to this condition. Other listed values are Stellite 20 reference data and may not represent this condition. Bars are the position among cobalt-chrome alloy grades.
Physical3
Stellite 20 OAW-DEP has a density of 8.98 g/cm³ (0.324 lb/in³), heavier than 91% of cobalt-chrome alloy grades. It melts at 1,150°C (2,102 °F).
Mechanical15
Stellite 20 OAW-DEP has a yield strength of 420 MPa (60.9 ksi) and a tensile strength of 450 MPa (65.3 ksi) — weaker than 96% of cobalt-chrome alloy grades. Elongation at break is 0.5% and the elastic modulus is 245 GPa (35.5 Msi).
Thermal5
Stellite 20 OAW-DEP is rated for continuous service to 700°C (1,292 °F). It conducts heat at 14.5 W/m·K (8.38 BTU/hr·ft·°F), better than 64% of cobalt-chrome alloy grades. Thermal expansion is 10.8 µm/m·K (6 µin/in·°F).
Electrical3
Stellite 20 OAW-DEP conducts electricity at 1.8 % IACS, worse than 75% of cobalt-chrome alloy grades.
Chemical & Environmental2
Corrosion resistance is good (63/100), worse than 86% of cobalt-chrome alloy grades.
Sustainability3
Producing a kilogram of Stellite 20 OAW-DEP takes about 200 MJ of energy and emits 16 kg of CO₂ — more than 75% of cobalt-chrome alloy grades. Typical recycled content is 20%.
Manufacturability8
Stellite 20 OAW-DEP's machinability is not recommended (3/100, worse than 100% of cobalt-chrome alloy grades); weldability poor (25/100); formability not recommended (1/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with Stellite 20 OAW-DEP
Is Stellite 20 easy to machine?
Effectively unmachinable by conventional cutting — finish by wet grinding with SiC/CBN wheels, EDM or lapping; allow grinding stock on overlays.
Can Stellite 20 be welded?
Deposit by OFW/GTAW with cast rod or by PTA/laser with powder; preheat 400–650 °C, keep interpass hot, slow furnace cool — some check-cracking is normal and usually acceptable in wear service.
Can Stellite 20 be formed, bent or molded?
No cold or hot forming possible; parts are cast to shape or produced as weld overlays/coatings.
What surface finishes work on Stellite 20?
Grind and lap for sealing faces (Ra <0.4 µm achievable); no plating or anodizing needed — the alloy itself is the wear/corrosion surface.
Stellite 20 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Crforms M7C3 carbides + solid-solution corrosion resistance | 31 – 34 | 33 |
| WM6C carbide former, hot hardness | 16 – 19 | 17.5 |
| Chigh carbide volume fraction | 2.3 – 2.7 | 2.45 |
| Ni | ≤ 3 | 2.5 |
| Fe | ≤ 3 | 2.5 |
| Si | ≤ 1.5 | 1 |
| Mn | ≤ 1 | 0.5 |
| Mo | ≤ 1 | 0.3 |
| Cobalance, ~38–42 % | balance | — |
Stellite 20 OAW-DEP — frequently asked
What is Stellite 20 OAW-DEP used for?
Stellite 20 OAW-DEP is typically used for valve trim, abrasive wear plates and oilfield tool hardfacing. In short: severe abrasion hardfacing; erosion-resistant overlay grade; low toughness, grind-finished.
What is the yield strength of Stellite 20 OAW-DEP?
Stellite 20 OAW-DEP has a typical yield strength of 420 MPa (60.9 ksi) and a tensile strength of 450 MPa (65.3 ksi) — weaker than 96% of cobalt-chrome alloy grades. Strength varies by condition: see the 3 listed tempers.
Is Stellite 20 OAW-DEP easy to machine?
Not especially — machinability is rated not recommended (3/100, worse than 100% of cobalt-chrome alloy grades). Effectively unmachinable by conventional cutting — finish by wet grinding with SiC/CBN wheels, EDM or lapping; allow grinding stock on overlays.
Can Stellite 20 OAW-DEP be welded?
Not readily — weldability is rated poor (25/100). Deposit by OFW/GTAW with cast rod or by PTA/laser with powder; preheat 400–650 °C, keep interpass hot, slow furnace cool — some check-cracking is normal and usually acceptable in wear service.
What surface finishes work on Stellite 20 OAW-DEP?
Grind and lap for sealing faces (Ra <0.4 µm achievable); no plating or anodizing needed — the alloy itself is the wear/corrosion surface.
Can Stellite 20 OAW-DEP be formed, bent or molded?
No cold or hot forming possible; parts are cast to shape or produced as weld overlays/coatings.
What is the maximum service temperature of Stellite 20 OAW-DEP?
Stellite 20 OAW-DEP is rated for continuous use to about 700°C (1,292 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between Stellite 20 AS-CAST and Stellite 20 OAW-DEP?
AS-CAST is the default condition — standard supply form: chill-cast bare rod for oxy-acetylene or GTAW hardfacing, and small cast wear parts. OAW-DEP: choose for hand-applied hardfacing of valve seats and tool edges where a thin, low-dilution layer of maximum hardness is wanted. Yield strength is 450 MPa in AS-CAST versus 420 MPa in OAW-DEP.
Sources
- Stellite 20 alloy data sheet — Kennametal Stellite (2020)
- Cobalt-base hardfacing alloys — properties and application guide — Deloro Wear Solutions (2019)
- ASM Handbook Vol. 2 — Properties and Selection: Nonferrous Alloys and Special-Purpose Materials (Cobalt wear alloys) — ASM International (1990)
- AWS A5.21 / A5.13 — Bare and covered hardfacing electrodes and rods (CoCr class) — AWS (2021)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.