Refractory Metal TZM As Sintered
Print state
UNS R03640, R03630 · ASTM B387 Grade 363 · also Mo-Ti-Zr
Pressed-and-sintered blank before forging/rolling; residual porosity means low strength and ductility — normally an intermediate product, occasionally sold for crucibles and furnace parts.
Values for the As Sintered condition
Other TZM tempers and conditions
TZM is listed in 5 conditions; see the grade overview at TZM.
Compare all 5 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
As SinteredThis page powder-metallurgy blank, unworked | Pressed-and-sintered blank before forging/rolling; residual porosity means low strength and ductility — normally an intermediate product, occasionally sold for crucibles and furnace parts. | 350 | 450 | 4 | 170 HB | 27 % IACS |
fully recrystallized in vacuum | Choose when maximum dimensional stability and creep resistance above 1400 °C matter more than room-temperature strength; more brittle at RT because DBTT rises. | 420 | 560 | 25 | 12 HRC | 126 W/m·K |
vacuum arc cast and wrought-worked billet | Vacuum-arc-cast route giving very low interstitial content and coarse grain — preferred for large forged dies and high-temperature creep parts. | 560 | 700 | 18 | 20 HRC | 32 % IACS |
Stress RelievedDefault wrought, stress relieved below recrystallization | Standard stocked condition for rod, plate and forgings — best combination of room-temperature strength, ductility and dimensional stability up to ~1300 °C. | 760 | 900 | 15 | 26 HRC | 118 W/m·K |
as-swaged / as-rolled, unrecrystallized | Highest room-temperature strength and hardness (thin sheet, wire, small rod); limited ductility and residual stress, not for service above ~1000 °C. | 940 | 1,050 | 8 | 31 HRC | 29 % IACS |
What is TZM As Sintered?
TZM As Sintered is TZM in the As Sintered condition — pressed-and-sintered blank before forging/rolling; residual porosity means low strength and ductility — normally an intermediate product, occasionally sold for crucibles and furnace parts. TZM As Sintered has a yield strength of 350 MPa (50.8 ksi) and a tensile strength of 450 MPa (65.3 ksi) — stronger than 57% of refractory metal grades. Elongation at break is 4% and the elastic modulus is 285 GPa (41.3 Msi). TZM As Sintered has a density of 9.9 g/cm³ (0.358 lb/in³), heavier than 60% of refractory metal grades. It melts at 2,617°C (4,743 °F). Stress Relieved is the default condition FabDigit quotes; As Sintered is available on request or by drawing note.
Advantages
- Easy to machine — 55/100, better than 101% of refractory metal grades
- High electrical conductivity — 27 % IACS, better than 80% of refractory metal grades
- Conducts heat well — 105 W/m·K (60.7 BTU/hr·ft·°F), better than 77% of refractory metal grades
- Low embodied carbon — 26 kg CO₂/kg, better than 77% of refractory metal grades
Limitations
- Needs corrosion protection — 42/100, worse than 95% of refractory metal grades
- Limited formability — 10/100, worse than 86% of refractory metal grades
- Limited ductility — 4%, worse than 84% of refractory metal grades
- Low fracture toughness — 13 MPa·√m (11.8 ksi·√in), worse than 82% of refractory metal grades
TZM As Sintered properties
Typical room-temperature values for TZM As Sintered; 23 are specific to this condition. Other listed values are TZM reference data and may not represent this condition. Bars are the position among refractory metal grades.
Physical3
TZM As Sintered has a density of 9.9 g/cm³ (0.358 lb/in³), heavier than 60% of refractory metal grades. It melts at 2,617°C (4,743 °F).
Mechanical16
TZM As Sintered has a yield strength of 350 MPa (50.8 ksi) and a tensile strength of 450 MPa (65.3 ksi) — stronger than 57% of refractory metal grades. Elongation at break is 4% and the elastic modulus is 285 GPa (41.3 Msi).
Thermal6
TZM As Sintered is rated for continuous service to 1,100°C (2,012 °F). It conducts heat at 105 W/m·K (60.7 BTU/hr·ft·°F), better than 77% of refractory metal grades. Thermal expansion is 5.3 µm/m·K (2.94 µin/in·°F).
Electrical3
TZM As Sintered conducts electricity at 27 % IACS, better than 80% of refractory metal grades.
Chemical & Environmental3
Corrosion resistance is fair (42/100), worse than 95% of refractory metal grades.
Sustainability4
Producing a kilogram of TZM As Sintered takes about 380 MJ of energy and emits 26 kg of CO₂ — less than 78% of refractory metal grades. Typical recycled content is 25%.
Manufacturability7
TZM As Sintered's machinability is good (55/100, better than 101% of refractory metal grades); weldability poor (25/100); formability not recommended (10/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with TZM As Sintered
Is TZM easy to machine?
Machines like a hard, abrasive cast iron — sharp positive-rake carbide or PCD tools, rigid setup, generous coolant, avoid dull edges that cause chipping and subsurface cracks; grinding and EDM work well.
Can TZM be welded?
Fusion welding (EB, laser, GTAW in chamber) recrystallizes and embrittles the joint — prefer vacuum brazing, mechanical fastening or friction/diffusion bonding for structural parts.
Can TZM be formed, bent or molded?
Form warm (200–500 °C, higher for recrystallized stock) to stay above the DBTT; generous bend radii, no sharp cold bends, and stress relieve at 900–1100 °C after heavy work.
What surface finishes work on TZM?
Cannot be anodized; use electropolishing or mechanical polish for clean vacuum surfaces and Si-Cr-Fe silicide, aluminide or CVD coatings when the part must see air above ~500 °C.
TZM chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Ticarbide former, main strengthener | 0.4 – 0.55 | 0.5 |
| Zr | 0.06 – 0.12 | 0.08 |
| Cforms TiC/ZrC dispersoids | 0.01 – 0.04 | 0.03 |
| O | ≤ 0.03 | — |
| N | ≤ 0 | — |
| Fe | ≤ 0.01 | — |
| Ni | ≤ 0.01 | — |
| Si | ≤ 0.01 | — |
| Mobalance, ≥99.2 % with additions | balance | — |
TZM As Sintered — frequently asked
What is TZM As Sintered used for?
TZM As Sintered is typically used for rocket nozzles and thrust chamber inserts, hot-work extrusion and forging dies, furnace hot-zone structures and fixtures, die-casting core pins and shot sleeves, isothermal forging tooling and X-ray rotating anode substrates. In short: higher-strength molybdenum alloy.
What is the yield strength of TZM As Sintered?
TZM As Sintered has a typical yield strength of 350 MPa (50.8 ksi) and a tensile strength of 450 MPa (65.3 ksi) — stronger than 57% of refractory metal grades. Strength varies by condition: see the 5 listed tempers.
Is TZM As Sintered easy to machine?
Reasonably — machinability is rated good (55/100, better than 101% of refractory metal grades). Machines like a hard, abrasive cast iron — sharp positive-rake carbide or PCD tools, rigid setup, generous coolant, avoid dull edges that cause chipping and subsurface cracks; grinding and EDM work well.
Can TZM As Sintered be welded?
Not readily — weldability is rated poor (25/100). Fusion welding (EB, laser, GTAW in chamber) recrystallizes and embrittles the joint — prefer vacuum brazing, mechanical fastening or friction/diffusion bonding for structural parts.
What surface finishes work on TZM As Sintered?
Cannot be anodized; use electropolishing or mechanical polish for clean vacuum surfaces and Si-Cr-Fe silicide, aluminide or CVD coatings when the part must see air above ~500 °C.
Can TZM As Sintered be formed, bent or molded?
Form warm (200–500 °C, higher for recrystallized stock) to stay above the DBTT; generous bend radii, no sharp cold bends, and stress relieve at 900–1100 °C after heavy work.
What is the maximum service temperature of TZM As Sintered?
TZM As Sintered is rated for continuous use to about 1,100°C (2,012 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Sources
- ASTM B387 — Molybdenum and Molybdenum Alloy Bar, Rod, and Wire (Type 364 TZM) — ASTM International (2018)
- ASTM B386 — Molybdenum and Molybdenum Alloy Plate, Sheet, Strip, Foil — ASTM International (2018)
- TZM molybdenum alloy material properties — Plansee SE (2023)
- ASM Handbook Vol. 2 — Properties of Refractory Metals and Alloys — ASM International (1990)
- Molybdenum and TZM technical data — H.C. Starck Solutions / Ed Fagan Inc. (2022)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.