Phenolic XX XXXPC
Grade
ASTM D709 · also Garolite XX, Bakelite
XXXPC = nEMA XXXPC
Pick for high-volume cold blanking of thin insulation parts without pre-heating the sheet.
Values for the XXXPC condition
Other Phenolic XX grades and fills
Phenolic XX is listed in 6 conditions; see the grade overview at Phenolic XX.
Compare all 6 grades and fillsHide
| Grade · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness |
|---|---|---|---|---|---|
XXXPCThis page NEMA XXXPC | Pick for high-volume cold blanking of thin insulation parts without pre-heating the sheet. | — | 76 | 1.6 | 87 Shore D |
NEMA XXXP | Pick for thin sheet that must be blanked/punched (terminal strips, washers) while keeping good electrical loss figures. | — | 80 | 1.5 | 88 Shore D |
NEMA XXX | Pick for radio-frequency or humid-environment insulation where low loss and low moisture pickup matter more than strength. | — | 83 | 1.4 | 89 Shore D |
Flame-retardant paper phenolic | Pick where a UL 94 V-0 rating is mandated for the insulating part (appliance and switchgear insulation). | — | 85 | 1.4 | 90 Shore D |
Phenolic MatrixDefault NEMA XX cellulose-paper / phenolic laminate (default) | General-purpose paper-phenolic sheet/rod/tube for combined mechanical and low-frequency electrical duty at low cost. | — | 90 | 1.5 | 90 Shore D |
NEMA X | Pick when only mechanical strength matters (spacers, jigs, wear pads) and electrical performance is irrelevant. | — | 100 | 1.6 | 91 Shore D |
What is Phenolic XX XXXPC?
Phenolic XX XXXPC is Phenolic XX in the XXXPC grade — pick for high-volume cold blanking of thin insulation parts without pre-heating the sheet. Phenolic XX XXXPC has a tensile strength of 76 MPa (11 ksi), weaker than 78% of composite grades. Elongation at break is 1.6% and the elastic modulus is 6.2 GPa (0.899 Msi). Phenolic XX XXXPC has a density of 1.34 g/cm³ (0.0484 lb/in³), lighter than 78% of composite grades. Its glass-transition temperature is 170°C (338 °F). Phenolic Matrix is the default condition FabDigit quotes; XXXPC is available on request or by drawing note.
Advantages
- Forms and bends easily — 45/100, better than 100% of composite grades
- Easy to machine — 85/100, better than 90% of composite grades
- Low embodied carbon — 4.5 kg CO₂/kg, better than 79% of composite grades
- Lightweight — 1.34 g/cm³ (0.0484 lb/in³), better than 78% of composite grades
Limitations
- Limited service temperature — 110°C (230 °F), worse than 87% of composite grades
- Degrades in UV without stabilisers — 25/100, worse than 86% of composite grades
- Poor heat conductor — 0.24 W/m·K (0.139 BTU/hr·ft·°F), worse than 79% of composite grades
- Low stiffness — 6.2 GPa (0.899 Msi), worse than 78% of composite grades
Phenolic XX XXXPC properties
Typical room-temperature values for Phenolic XX XXXPC; 24 are specific to this condition. Other listed values are Phenolic XX reference data and may not represent this condition. Bars are the position among composite grades.
Physical4
Phenolic XX XXXPC has a density of 1.34 g/cm³ (0.0484 lb/in³), lighter than 78% of composite grades. Its glass-transition temperature is 170°C (338 °F).
Mechanical14
Phenolic XX XXXPC has a tensile strength of 76 MPa (11 ksi), weaker than 78% of composite grades. Elongation at break is 1.6% and the elastic modulus is 6.2 GPa (0.899 Msi).
Thermal10
Phenolic XX XXXPC is rated for continuous service to 110°C (230 °F). It conducts heat at 0.24 W/m·K (0.139 BTU/hr·ft·°F), worse than 79% of composite grades. Thermal expansion is 25 µm/m·K (13.9 µin/in·°F).
Electrical7
Phenolic XX XXXPC is an electrical insulator with a dielectric strength of 16 kV/mm (406.4 V/mil) and a resistivity of 1×10⁹ Ω·m.
Chemical & Environmental3
Corrosion resistance is good (66/100), worse than 70% of composite grades. UV resistance is poor.
Sustainability3
Producing a kilogram of Phenolic XX XXXPC takes about 80 MJ of energy and emits 4.5 kg of CO₂ — less than 84% of composite grades. Typical recycled content is 5%.
Manufacturability4
Phenolic XX XXXPC's machinability is excellent (85/100, better than 90% of composite grades); weldability not recommended (0/100); formability fair (45/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with Phenolic XX XXXPC
Is Phenolic XX easy to machine?
Cuts, drills and turns easily with sharp carbide tooling at high speed and no coolant; dust is abrasive and irritating, so use vacuum extraction and back up holes to avoid edge chipping and delamination.
Can Phenolic XX be welded?
Thermoset — cannot be welded or thermally reformed; join by bolting, riveting or epoxy/phenolic adhesive bonding after abrading the surface.
Can Phenolic XX be formed, bent or molded?
Supplied as fully cured sheet, rod and tube; thin sheet (P/PC grades) can be hot- or cold-punched, but thick stock must be machined to shape.
What surface finishes work on Phenolic XX?
Sand or scrape edges to remove fuzz and seal machined surfaces with varnish/epoxy to limit moisture pickup; the natural finish is brown-to-black and not platable, though it accepts primer-based paint.
Phenolic XX chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| phenol-formaldehyde resinresole/novolac, fully cured thermoset binder | 40 – 55 | 48 |
| volatiles/residual moisture | 0 – 2 | 1 |
| cellulose kraft paperreinforcement web, multiple plies | ≥ 45 (balance) | — |
Phenolic XX XXXPC — frequently asked
What is Phenolic XX XXXPC used for?
Phenolic XX XXXPC is typically used for electrical insulators and barriers, terminal boards and tag strips, punched washers, gaskets and shims, coil and transformer spacers, switch and relay bases and low-load bushings and cams. In short: classic phenolic laminate.
What is the tensile strength of Phenolic XX XXXPC?
Phenolic XX XXXPC has a typical tensile strength of 76 MPa (11 ksi) — weaker than 78% of composite grades. Strength varies by condition: see the 6 listed tempers.
Is Phenolic XX XXXPC easy to machine?
Yes — machinability is rated excellent (85/100, better than 90% of composite grades). Cuts, drills and turns easily with sharp carbide tooling at high speed and no coolant; dust is abrasive and irritating, so use vacuum extraction and back up holes to avoid edge chipping and delamination.
Can Phenolic XX XXXPC be welded?
Not readily — weldability is rated not recommended (0/100). Thermoset — cannot be welded or thermally reformed; join by bolting, riveting or epoxy/phenolic adhesive bonding after abrading the surface.
What surface finishes work on Phenolic XX XXXPC?
Sand or scrape edges to remove fuzz and seal machined surfaces with varnish/epoxy to limit moisture pickup; the natural finish is brown-to-black and not platable, though it accepts primer-based paint.
Can Phenolic XX XXXPC be formed, bent or molded?
Supplied as fully cured sheet, rod and tube; thin sheet (P/PC grades) can be hot- or cold-punched, but thick stock must be machined to shape.
What is the maximum service temperature of Phenolic XX XXXPC?
Phenolic XX XXXPC is rated for continuous use to about 110°C (230 °F), and briefly to 150°C. Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Can FabDigit make parts in Phenolic XX XXXPC?
Yes — Phenolic XX XXXPC is available for CNC machining and sheet metal with instant online pricing. Upload a STEP file to get a price and a DFM check.
Sources
- NEMA LI 1 — Industrial Laminating Thermosetting Products — NEMA (1998)
- ASTM D709 — Standard Specification for Laminated Thermosetting Materials — ASTM (2017)
- Paper-phenolic industrial laminate grades X / XX / XXX / XXXP — Norplex-Micarta (2022)
- Engineered Materials Handbook Vol. 2 — Engineering Plastics (phenolic laminates) — ASM International (1988)
- MatWeb paper-reinforced phenolic laminate property listings — MatWeb (2024)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.