Steel WC4 vs WC5
Steel · grade comparison
Steel WC4 and WC5 are both steel grades. Both yield at about 335 MPa — strength does not separate them. On the shop floor, WC4 sits in a lower cost tier (standard, $$) than WC5 (premium, $$$).
WC4Choose it when cost is the deciding factor.
WC4 vs WC5: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Reduction in Area
Compressive Strength
Shear Strength
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 78 GPa11.3 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Elongation at Break 24% · Fatigue Strength (Endurance Limit) 235 MPa34.1 ksi
Physical
Density and transition temperatures.
Liquidus Temperature
Same in both: Density 7.83 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Expansion (CTE, 20–100 °C)
Min Service Temperature
Same in both: Thermal Conductivity 42 W/m·K24.3 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Max Service Temperature (continuous) 540°C1,004 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 7.8 % IACS · Electrical Resistivity 2.2×10⁻⁷ Ω·m8.66 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 70 / 100 · Brazeability / Solderability 45 / 100 · Polishability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Typical Recycled Content
Same in both: Embodied Energy (primary production) 26 MJ/kg11,178 BTU/lb · Embodied Carbon (primary production) 2 kg CO₂/kg · Embodied Water 55 L/kg6.6 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Stiffness (E / density)
Modulus of Resilience
Same in both: Specific Strength (UTS / density) 70 kN·m/kg · Thermal Diffusivity 11.4 mm²/s · Thermal Shock Resistance Index 9
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | WC4 | WC5 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$ Standard | $$$ Premium |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
WC4 vs WC5 — frequently asked
What is the difference between WC4 and WC5?
Steel WC4 and WC5 are both steel grades. Both yield at about 335 MPa — strength does not separate them. On the shop floor, WC4 sits in a lower cost tier (standard, $$) than WC5 (premium, $$$).
Which is cheaper, WC4 or WC5?
WC4 is the lower-cost material: it sits in the standard tier ($$) while WC5 is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which welds better, WC4 or WC5?
WC5. Its weldability rates good (60/100) against good (55/100) for WC4.