Steel A217 WC1 vs WC5
Steel · grade comparison
Steel A217 WC1 and WC5 are both steel grades. WC5 is the stronger of the two: yield strength 330 MPa (47.9 ksi) against 290 MPa (42.1 ksi) for A217 WC1, about 14% more; tensile strength follows at 550 MPa (79.8 ksi) vs 500 MPa (72.5 ksi). In exchange, A217 WC1 is the more ductile: elongation 28% versus 24% for WC5, and WC5 is harder (170 HB vs 150 HB). On the shop floor, A217 WC1 welds better (very good vs good) and A217 WC1 sits in a lower cost tier (standard, $$) than WC5 (premium, $$$).
A217 WC1Choose it when the part is bent, formed or impact-loaded, or when it will be welded.
WC5Choose it when strength drives the design.
A217 WC1 vs WC5: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Liquidus Temperature
Same in both: Density 7.83 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Thermal Conductivity 42 W/m·K24.3 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.2 µm/m·K6.8 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb
Electrical
Conductivity and insulation.
Electrical Resistivity
Electrical Conductivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Galvanic Potential (seawater, vs SCE)
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Same in both: Polishability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Shock Resistance Index
Same in both: Thermal Diffusivity 11.4 mm²/s
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | A217 WC1 | WC5 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$ Standard | $$$ Premium |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
A217 WC1 vs WC5 — frequently asked
Is WC5 stronger than A217 WC1?
Yes. WC5 has a typical yield strength of 330 MPa (47.9 ksi) against 290 MPa (42.1 ksi) for A217 WC1 — about 14% more. Tensile strength is 550 MPa (79.8 ksi) vs 500 MPa (72.5 ksi).
Which is cheaper, A217 WC1 or WC5?
A217 WC1 is the lower-cost material: it sits in the standard tier ($$) while WC5 is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which welds better, A217 WC1 or WC5?
A217 WC1. Its weldability rates very good (70/100) against good (60/100) for WC5.