Stainless Steel 304 vs 310S
Stainless Steel · grade comparison
Stainless Steel 304 and 310S are both stainless steel grades. Both yield at about 250 MPa — strength does not separate them. 304 is the more ductile: elongation 55% versus 45% for 310S, and 310S is harder (160 HB vs 150 HB). 310S runs hotter in service (1,050°C vs 870°C continuous) and 304 conducts heat better (16.2 W/m·K vs 14.2 W/m·K). On the shop floor, 304 machines more easily (fair vs poor), 304 welds better (excellent vs very good), and 304 sits in a lower cost tier (standard, $$) than 310S (premium, $$$).
304Choose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
310SChoose it when the part sees heat.
304 vs 310S: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 152 GPa22 Msi · Hardness, Rockwell B 82 HRB
Physical
Density and transition temperatures.
Density
Same in both: Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,450°C2,642 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.05 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Castability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 3
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 304 | 310S |
|---|---|---|
| Casting & forging | Yes | — |
| Default condition | Annealed | Solution Annealed |
| Relative cost | $$ Standard | $$$ Premium |
| Min. machined wall | 0.8 mm | 0.8 mm |
| Best machined surface | Ra 1.6 µm | Ra 1.6 µm |
Both are offered for CNC machining and Sheet metal. Both take the same 32 finishes: AlCrN, AlTiN, Black Oxide, CVD Al2O3, CVD TiCN, CVD TiN, Cerakote, Chrome Plating, CrN, DLC, Electroless Nickel (EN), Electropolishing and 20 more.
304 vs 310S — frequently asked
What is the difference between 304 and 310S?
Stainless Steel 304 and 310S are both stainless steel grades. Both yield at about 250 MPa — strength does not separate them. 304 is the more ductile: elongation 55% versus 45% for 310S, and 310S is harder (160 HB vs 150 HB).
Which is cheaper, 304 or 310S?
304 is the lower-cost material: it sits in the standard tier ($$) while 310S is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 304 or 310S?
304. Its machinability rates fair (45/100) against poor (32/100) for 310S; for welding the order is 304 first (excellent, 88/100) then 310S (very good, 75/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 304 and 310S side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.