Stainless Steel 304 vs 316L
Stainless Steel · grade comparison
Stainless Steel 304 and 316L are both stainless steel grades. 316L is the stronger of the two: yield strength 290 MPa (42.1 ksi) against 250 MPa (36.3 ksi) for 304, about 16% more. 304 runs hotter in service (870°C vs 800°C continuous). On the shop floor, 304 sits in a lower cost tier (standard, $$) than 316L (high, $$$$).
304Choose it when the part sees heat, or when cost is the deciding factor.
316LChoose it when strength drives the design.
304 vs 316L: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 193 GPa28 Msi · Shear Modulus 77 GPa11.2 Msi · Fatigue Strength (Endurance Limit) 250 MPa36.3 ksi · Hardness, Brinell 150 HB
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.05 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Castability
Same in both: Machinability Rating (AISI 1212 = 100 %) 45%
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Specific Strength (UTS / density) 73 kN·m/kg · Thermal Shock Resistance Index 3
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 304 | 316L |
|---|---|---|
| Casting & forging | Yes | — |
| 3D printing | — | Yes |
| Default condition | Annealed | Solution Annealed |
| Relative cost | $$ Standard | $$$$ High |
| Min. machined wall | 0.8 mm | 0.8 mm |
| Best machined surface | Ra 1.6 µm | Ra 1.6 µm |
| Electropolished (Metal AM) | — | Yes |
| Passivated (Metal AM) | — | Yes |
| Plated (Metal AM) | — | Yes |
Both are offered for CNC machining and Sheet metal. They share 32 finishes: AlCrN, AlTiN, Black Oxide, CVD Al2O3, CVD TiCN, CVD TiN, Cerakote, Chrome Plating, CrN, DLC, Electroless Nickel (EN), Electropolishing and 20 more.
304 vs 316L — frequently asked
Is 316L stronger than 304?
Yes. 316L has a typical yield strength of 290 MPa (42.1 ksi) against 250 MPa (36.3 ksi) for 304 — about 16% more. Tensile strength is 580 MPa (84.1 ksi) vs 585 MPa (84.8 ksi).
Which is cheaper, 304 or 316L?
304 is the lower-cost material: it sits in the standard tier ($$) while 316L is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 304 or 316L?
304, by a small margin. Both rate fair for machinability — 45/100 against 40/100 for 316L.