Precious Metal Pd99.9 vs Pt95Co5
Precious Metal · grade comparison
Precious Metal Pd99.9 and Pt95Co5 are both precious metal grades. Pt95Co5 is the stronger of the two: yield strength 250 MPa (36.3 ksi) against 55 MPa (7.98 ksi) for Pd99.9, about 4.5 times as much; tensile strength follows at 480 MPa (69.6 ksi) vs 180 MPa (26.1 ksi). In exchange, Pd99.9 is the more ductile: elongation 35% versus 20% for Pt95Co5, and Pt95Co5 is harder (128 HB vs 40 HB). Pd99.9 is lighter (12.02 g/cm³ vs 20 g/cm³ for Pt95Co5) and Pt95Co5 is stiffer (168 GPa vs 121 GPa).
Pd99.9Choose it when the part is bent, formed or impact-loaded, or when weight is the constraint.
Pt95Co5Choose it when strength drives the design, or when the part sees heat.
Pd99.9 vs Pt95Co5: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Charpy V-Notch Impact (RT)
Hardness, Rockwell B
Same in both: Poisson's Ratio 0.39
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) 0.25 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Water 250,000 L/kg29,957 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Pd99.9 | Pt95Co5 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Pd99.9 vs Pt95Co5 — frequently asked
Is Pt95Co5 stronger than Pd99.9?
Yes. Pt95Co5 has a typical yield strength of 250 MPa (36.3 ksi) against 55 MPa (7.98 ksi) for Pd99.9 — about 4.5 times as much. Tensile strength is 480 MPa (69.6 ksi) vs 180 MPa (26.1 ksi).
Which is cheaper, Pd99.9 or Pt95Co5?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, Pd99.9 or Pt95Co5?
Pt95Co5. Its machinability rates fair (35/100) against poor (30/100) for Pd99.9; for welding the order is Pt95Co5 first (excellent, 85/100) then Pd99.9 (very good, 80/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in Pd99.9 and Pt95Co5 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.