Precious Metal BAu-6 vs BVAu-5
Precious Metal · grade comparison
Precious Metal BAu-6 and BVAu-5 are both precious metal grades. BAu-6 is the stronger of the two: tensile strength 500 MPa (72.5 ksi) against 340 MPa (49.3 ksi) for BVAu-5, about 47% more. In exchange, BVAu-5 is the more ductile: elongation 28% versus 15% for BAu-6, and BAu-6 is harder (190 HV vs 100 HV). BVAu-5 is lighter (11.3 g/cm³ vs 14.8 g/cm³ for BAu-6) and BAu-6 is stiffer (105 GPa vs 95 GPa). On the shop floor, BVAu-5 machines more easily (45 vs 35 out of 100).
BAu-6Choose it when strength drives the design, or when the part sees heat.
BVAu-5Choose it when the part is bent, formed or impact-loaded, or when weight is the constraint.
BAu-6 vs BVAu-5: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Elongation at Break
Shear Strength
Hardness, Vickers
Shear Modulus
Bulk Modulus
Yield Strength (0.2% offset)
Hardness, Brinell
Same in both: Poisson's Ratio 0.36
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Min Service Temperature -269°C-452 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Electrical Conductivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Same in both: Weldability 40 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | BAu-6 | BVAu-5 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
BAu-6 vs BVAu-5 — frequently asked
Is BAu-6 stronger than BVAu-5?
Yes. BAu-6 has a typical tensile strength of 500 MPa (72.5 ksi) against 340 MPa (49.3 ksi) for BVAu-5 — about 47% more.
Which is cheaper, BAu-6 or BVAu-5?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, BAu-6 or BVAu-5?
BVAu-5, by a small margin. Both rate fair for machinability — 45/100 against 35/100 for BAu-6.
Ready to make it?
Upload a CAD file and FabDigit prices the part in BAu-6 and BVAu-5 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.