MXD6 vs PA6
Polymer · grade comparison
MXD6 and PA6 are both polymer grades. MXD6 is the stronger of the two: tensile strength 200 MPa (29 ksi) against 80 MPa (11.6 ksi) for PA6, about 150% more. In exchange, PA6 is the more ductile: elongation 60% versus 2.5% for MXD6. PA6 is lighter (1.14 g/cm³ vs 1.48 g/cm³ for MXD6) and MXD6 is stiffer (10 GPa vs 3 GPa). On the shop floor, PA6 machines more easily (good vs fair) and PA6 sits in a lower cost tier (budget, $) than MXD6 (standard, $$).
MXD6Choose it when strength drives the design, or when the part sees heat.
PA6Choose it when the part is bent, formed or impact-loaded, or when weight is the constraint.
MXD6 vs PA6: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Elongation at Break
Compressive Strength
Flexural Strength
Flexural Modulus
Izod Impact, Notched
Hardness, Rockwell M
Shear Modulus
Bulk Modulus
Yield Strength (0.2% offset)
Compressive Modulus
Shear Strength
Fracture Toughness (K_IC)
Hardness, Shore D
Hardness, Rockwell R
Physical
Density and transition temperatures.
Density
Melting Temperature (Tm)
Glass Transition (Tg)
Water Absorption (24 h)
Water Absorption (Saturation)
Refractive Index
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Heat Deflection Temp. @ 0.45 MPa
Heat Deflection Temp. @ 1.8 MPa
Max Service Temperature (short-term)
Vicat Softening Point (B50)
Same in both: Limiting Oxygen Index 24%
Electrical
Conductivity and insulation.
Dielectric Constant (1 MHz)
Dissipation Factor (1 MHz)
Comparative Tracking Index (CTI)
Surface Resistivity
Same in both: Electrical Resistivity 1×10¹² Ω·m3.94×10¹⁹ µΩ·in · Dielectric Strength 25 kV/mm635 V/mil · Volume Resistivity 1×10¹⁴ Ω·cm
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: UV / Weathering Resistance 30 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Mold Shrinkage
Processing Melt Temperature (typ.)
Mold Temperature (typ.)
Polishability
Melt Flow Rate
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Embodied Water
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Same in both: Thermal Diffusivity 0.1 mm²/s · Thermal Shock Resistance Index 0
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | MXD6 | PA6 |
|---|---|---|
| CNC machining | — | Yes |
| Sheet metal | — | Yes |
| Default condition | GF30 | Unfilled |
| Relative cost | $$ Standard | $ Budget |
| Min. machined wall | — | 0.5 mm |
| Best machined surface | — | Ra 0.8 µm |
| Painting | — | Yes |
Both are offered for Injection molding. They share 5 finishes: Chrome Plating (Plastic), EMI Shielding Coating, Soft Touch Coating, Spray Painting, UV Coating.
MXD6 vs PA6 — frequently asked
Is MXD6 stronger than PA6?
Yes. MXD6 has a typical tensile strength of 200 MPa (29 ksi) against 80 MPa (11.6 ksi) for PA6 — about 150% more.
Which is cheaper, MXD6 or PA6?
PA6 is the lower-cost material: it sits in the budget tier ($) while MXD6 is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, MXD6 or PA6?
PA6. Its machinability rates good (68/100) against fair (40/100) for MXD6; for welding the order is PA6 first (good, 62/100) then MXD6 (good, 55/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in MXD6 and PA6 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.