Digital ABS vs PA6
Polymer · grade comparison
Digital ABS and PA6 are both polymer grades, both engineering plastic. PA6 is the stronger of the two: tensile strength 80 MPa (11.6 ksi) against 57 MPa (8.27 ksi) for Digital ABS, about 40% more. PA6 is the more ductile: elongation 60% versus 30% for Digital ABS, and Digital ABS is harder (86 Shore D vs 81 Shore D). PA6 is stiffer (3 GPa vs 2.8 GPa) and PA6 runs hotter in service (90°C vs 50°C continuous). On the shop floor, PA6 machines more easily (68 vs 55 out of 100), PA6 welds better (good vs poor), and PA6 sits in a lower cost tier (budget, $) than Digital ABS (specialty, $$$$$).
PA6Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
Digital ABS vs PA6: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Elongation at Break
Flexural Strength
Flexural Modulus
Izod Impact, Notched
Hardness, Shore D
Hardness, Rockwell M
Shear Modulus
Bulk Modulus
Yield Strength (0.2% offset)
Compressive Strength
Compressive Modulus
Shear Strength
Fracture Toughness (K_IC)
Hardness, Rockwell R
Physical
Density and transition temperatures.
Density
Glass Transition (Tg)
Melting Temperature (Tm)
Water Absorption (Saturation)
Refractive Index
Same in both: Water Absorption (24 h) 1.7%
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Min Service Temperature
Heat Deflection Temp. @ 0.45 MPa
Heat Deflection Temp. @ 1.8 MPa
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Vicat Softening Point (B50)
Limiting Oxygen Index
Max Service Temperature (short-term)
Electrical
Conductivity and insulation.
Electrical Resistivity
Dielectric Strength
Dielectric Constant (1 MHz)
Dissipation Factor (1 MHz)
Volume Resistivity
Surface Resistivity
Comparative Tracking Index (CTI)
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
UV / Weathering Resistance
Same in both: Corrosion Resistance 70 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Polishability
Formability (cold)
Mold Shrinkage
Melt Flow Rate
Processing Melt Temperature (typ.)
Mold Temperature (typ.)
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Digital ABS | PA6 |
|---|---|---|
| 3D printing | Yes | — |
| CNC machining | — | Yes |
| Sheet metal | — | Yes |
| Injection molding | — | Yes |
| Default condition | Standard | Unfilled |
| Relative cost | $$$$$ Specialty | $ Budget |
| Min. machined wall | — | 0.5 mm |
| Best machined surface | — | Ra 0.8 µm |
| Chrome Plating (Plastic) | — | Yes |
| Conductive Coating | Yes | — |
| Dyeing (Nylon) | Yes | — |
| Primer Coating | Yes | — |
| Spray Painting | — | Yes |
| Tinted Coating | Yes | — |
| Vacuum Metallization | Yes | — |
| Waterproof Coating | Yes | — |
They share 4 finishes: EMI Shielding Coating, Painting, Soft Touch Coating, UV Coating.
Digital ABS vs PA6 — frequently asked
Is PA6 stronger than Digital ABS?
Yes. PA6 has a typical tensile strength of 80 MPa (11.6 ksi) against 57 MPa (8.27 ksi) for Digital ABS — about 40% more.
Which is cheaper, Digital ABS or PA6?
PA6 is the lower-cost material: it sits in the budget tier ($) while Digital ABS is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, Digital ABS or PA6?
PA6, by a small margin. Both rate good for machinability — 68/100 against 55/100 for Digital ABS; for welding the order is PA6 first (good, 62/100) then Digital ABS (poor, 15/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in Digital ABS and PA6 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.