ETFE vs PTFE
Polymer · grade comparison
ETFE and PTFE are both polymer grades. ETFE is the stronger of the two: yield strength 22 MPa (3.19 ksi) against 12 MPa (1.74 ksi) for PTFE, about 83% more; tensile strength follows at 45 MPa (6.53 ksi) vs 30 MPa (4.35 ksi). ETFE is harder — 73 Shore D against 56 Shore D for PTFE — which matters for wear surfaces and threads. ETFE is lighter (1.73 g/cm³ vs 2.17 g/cm³ for PTFE) and ETFE is stiffer (0.85 GPa vs 0.5 GPa). On the shop floor, PTFE machines more easily (very good vs good), ETFE welds better (very good vs not recommended), and PTFE sits in a lower cost tier (premium, $$$) than ETFE (high, $$$$).
ETFEChoose it when strength drives the design, or when surface hardness matters.
PTFEChoose it when the part sees heat, or when the part is machined in volume.
ETFE vs PTFE: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Flexural Modulus
Izod Impact, Notched
Hardness, Shore D
Hardness, Rockwell R
Shear Modulus
Compressive Modulus
Flexural Strength
Shear Strength
Hardness, Shore A
Physical
Density and transition temperatures.
Density
Melting Temperature (Tm)
Glass Transition (Tg)
Water Absorption (24 h)
Water Absorption (Saturation)
Refractive Index
Light Transmission
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Heat Deflection Temp. @ 0.45 MPa
Heat Deflection Temp. @ 1.8 MPa
Vicat Softening Point (B50)
Limiting Oxygen Index
Max Service Temperature (short-term)
Electrical
Conductivity and insulation.
Electrical Resistivity
Dielectric Strength
Dielectric Constant (1 MHz)
Dissipation Factor (1 MHz)
Volume Resistivity
Surface Resistivity
Same in both: Comparative Tracking Index (CTI) 600 V
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
UV / Weathering Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Polishability
Mold Shrinkage
Melt Flow Rate
Processing Melt Temperature (typ.)
Mold Temperature (typ.)
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 0%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Same in both: Thermal Diffusivity 0.1 mm²/s · Thermal Shock Resistance Index 0
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | ETFE | PTFE |
|---|---|---|
| CNC machining | — | Yes |
| Sheet metal | — | Yes |
| Injection molding | — | Yes |
| Default condition | — | Virgin |
| Relative cost | $$$$ High | $$$ Premium |
| Min. machined wall | — | 0.5 mm |
| Best machined surface | — | Ra 0.8 µm |
| Chrome Plating (Plastic) | — | Yes |
| EMI Shielding Coating | — | Yes |
| Painting | — | Yes |
| Soft Touch Coating | — | Yes |
| Spray Painting | — | Yes |
| UV Coating | — | Yes |
ETFE vs PTFE — frequently asked
Is ETFE stronger than PTFE?
Yes. ETFE has a typical yield strength of 22 MPa (3.19 ksi) against 12 MPa (1.74 ksi) for PTFE — about 83% more. Tensile strength is 45 MPa (6.53 ksi) vs 30 MPa (4.35 ksi).
Which is cheaper, ETFE or PTFE?
PTFE is the lower-cost material: it sits in the premium tier ($$$) while ETFE is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, ETFE or PTFE?
PTFE. Its machinability rates very good (80/100) against good (62/100) for ETFE; for welding the order is ETFE first (very good, 80/100) then PTFE (not recommended, 10/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in ETFE and PTFE side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.