Nickel 205 vs Nickel 211
Nickel Alloy · grade comparison
Nickel 205 and Nickel 211 are both nickel alloy grades. Nickel 211 is the stronger of the two: yield strength 210 MPa (30.5 ksi) against 145 MPa (21 ksi) for Nickel 205, about 45% more; tensile strength follows at 480 MPa (69.6 ksi) vs 440 MPa (63.8 ksi). In exchange, Nickel 205 is the more ductile: elongation 45% versus 40% for Nickel 211, and Nickel 211 is harder (110 HB vs 95 HB). Nickel 205 conducts heat better (70 W/m·K vs 42 W/m·K).
Nickel 205Choose it when the part is bent, formed or impact-loaded.
Nickel 211Choose it when strength drives the design.
Nickel 205 vs Nickel 211: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Bulk Modulus 180 GPa26.1 Msi · Poisson's Ratio 0.31 · Charpy V-Notch Impact (RT) 200 J148 ft·lbf
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Min Service Temperature
Same in both: Specific Heat Capacity 456 J/kg·K0.11 BTU/lb·°F · Max Service Temperature (continuous) 315°C599 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Same in both: Corrosion Resistance 70 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Water
Typical Recycled Content
Same in both: Embodied Carbon (primary production) 13 kg CO₂/kg
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every nickel alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Nickel 205 | Nickel 211 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 3 finishes: Gold Plating, Plasma Spray, Silver Plating.
Nickel 205 vs Nickel 211 — frequently asked
Is Nickel 211 stronger than Nickel 205?
Yes. Nickel 211 has a typical yield strength of 210 MPa (30.5 ksi) against 145 MPa (21 ksi) for Nickel 205 — about 45% more. Tensile strength is 480 MPa (69.6 ksi) vs 440 MPa (63.8 ksi).
Which is cheaper, Nickel 205 or Nickel 211?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which welds better, Nickel 205 or Nickel 211?
Nickel 205. Its weldability rates very good (80/100) against very good (72/100) for Nickel 211.