Nickel Alloy CW-12MW vs M30C
Nickel Alloy · grade comparison
Nickel Alloy CW-12MW and M30C are both nickel alloy grades. CW-12MW is the stronger of the two: yield strength 350 MPa (50.8 ksi) against 270 MPa (39.2 ksi) for M30C, about 30% more; tensile strength follows at 550 MPa (79.8 ksi) vs 500 MPa (72.5 ksi). In exchange, M30C is the more ductile: elongation 30% versus 10% for CW-12MW, and CW-12MW is harder (200 HB vs 140 HB). CW-12MW is stiffer (205 GPa vs 150 GPa) and CW-12MW runs hotter in service (650°C vs 480°C continuous). On the shop floor, M30C machines more easily (fair vs poor) and M30C welds better (68 vs 55 out of 100).
CW-12MWChoose it when strength drives the design, or when the part sees heat.
M30CChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
CW-12MW vs M30C: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Rockwell C
Compressive Strength
Fracture Toughness (K_IC)
Hardness, Vickers
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Same in both: Latent Heat of Fusion 290 J/g125 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Castability
Polishability
Same in both: Formability (cold) 15 / 100 · Brazeability / Solderability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Carbon (primary production)
Same in both: Embodied Energy (primary production) 150 MJ/kg64,488 BTU/lb · Embodied Water 300 L/kg35.9 gal/lb · Typical Recycled Content 40%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every nickel alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | CW-12MW | M30C |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 3 finishes: Gold Plating, Plasma Spray, Silver Plating.
CW-12MW vs M30C — frequently asked
Is CW-12MW stronger than M30C?
Yes. CW-12MW has a typical yield strength of 350 MPa (50.8 ksi) against 270 MPa (39.2 ksi) for M30C — about 30% more. Tensile strength is 550 MPa (79.8 ksi) vs 500 MPa (72.5 ksi).
Which is cheaper, CW-12MW or M30C?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, CW-12MW or M30C?
M30C. Its machinability rates fair (35/100) against poor (22/100) for CW-12MW; for welding the order is M30C first (good, 68/100) then CW-12MW (good, 55/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in CW-12MW and M30C side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.