Magnesium Alloy AZ80A vs LA141A
Magnesium Alloy · grade comparison
Magnesium Alloy AZ80A and LA141A are both magnesium alloy grades. AZ80A is the stronger of the two: yield strength 250 MPa (36.3 ksi) against 117 MPa (17 ksi) for LA141A, about 114% more; tensile strength follows at 340 MPa (49.3 ksi) vs 150 MPa (21.8 ksi). In exchange, LA141A is the more ductile: elongation 18% versus 11% for AZ80A, and AZ80A is harder (60 HB vs 55 HB). LA141A is lighter (1.35 g/cm³ vs 1.8 g/cm³ for AZ80A) and AZ80A runs hotter in service (120°C vs 65°C continuous). On the shop floor, AZ80A machines more easily (98 vs 88 out of 100) and AZ80A sits in a lower cost tier (standard, $$) than LA141A (high, $$$$).
AZ80AChoose it when strength drives the design, or when the part sees heat.
LA141AChoose it when the part is bent, formed or impact-loaded, or when weight is the constraint.
AZ80A vs LA141A: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all magnesium alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all magnesium alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Brazeability / Solderability
Polishability
Castability
Same in both: Weldability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Water 500 L/kg59.9 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every magnesium alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | AZ80A | LA141A |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | F | — |
| Relative cost | $$ Standard | $$$$ High |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 0.8 µm | — |
| Anodizing Type II | Yes | — |
| Chem Film (Alodine) | Yes | — |
| E-Coating | Yes | — |
| Hard Anodize Type III w/ PTFE | Yes | — |
| Hard Anodizing Type III | Yes | — |
| Painting | Yes | — |
| Powder Coating | Yes | — |
AZ80A vs LA141A — frequently asked
Is AZ80A stronger than LA141A?
Yes. AZ80A has a typical yield strength of 250 MPa (36.3 ksi) against 117 MPa (17 ksi) for LA141A — about 114% more. Tensile strength is 340 MPa (49.3 ksi) vs 150 MPa (21.8 ksi).
Which is cheaper, AZ80A or LA141A?
AZ80A is the lower-cost material: it sits in the standard tier ($$) while LA141A is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, AZ80A or LA141A?
AZ80A, by a small margin. Both rate excellent for machinability — 98/100 against 88/100 for LA141A.
Ready to make it?
Upload a CAD file and FabDigit prices the part in AZ80A and LA141A side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.