Copper Alloy C70600 vs C73200
Copper Alloy · grade comparison
Copper Alloy C70600 and C73200 are both copper alloy grades. C73200 is the stronger of the two: yield strength 380 MPa (55.1 ksi) against 120 MPa (17.4 ksi) for C70600, about 3.2 times as much; tensile strength follows at 470 MPa (68.2 ksi) vs 310 MPa (45 ksi). In exchange, C70600 is the more ductile: elongation 40% versus 12% for C73200, and C73200 is harder (130 HB vs 65 HB). C70600 runs hotter in service (300°C vs 200°C continuous) and C73200 conducts heat better (45 W/m·K vs 40 W/m·K). On the shop floor, C70600 welds better (excellent vs good).
C70600Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C73200Choose it when strength drives the design.
C70600 vs C73200: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Compressive Strength
Charpy V-Notch Impact (RT)
Same in both: Shear Modulus 47 GPa6.8 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Latent Heat of Fusion 200 J/g86 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Same in both: Machinability Rating (AISI 1212 = 100 %) 20%
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C70600 | C73200 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 4 finishes: Copper Plating, Electroless Nickel (EN), Gold Plating, Silver Plating.
C70600 vs C73200 — frequently asked
Is C73200 stronger than C70600?
Yes. C73200 has a typical yield strength of 380 MPa (55.1 ksi) against 120 MPa (17.4 ksi) for C70600 — about 3.2 times as much. Tensile strength is 470 MPa (68.2 ksi) vs 310 MPa (45 ksi).
Which is cheaper, C70600 or C73200?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which welds better, C70600 or C73200?
C70600. Its weldability rates excellent (92/100) against good (55/100) for C73200.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C70600 and C73200 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.