G10-ESD vs G11
Composite · grade comparison
G10-ESD and G11 are both composite grades. G11 is the stronger of the two: tensile strength 340 MPa (49.3 ksi) against 300 MPa (43.5 ksi) for G10-ESD, about 13% more. G11 is stiffer (22 GPa vs 20 GPa) and G11 runs hotter in service (180°C vs 130°C continuous).
G11Choose it when strength drives the design, or when the part sees heat.
G10-ESD vs G11: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all composite grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all composite grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Elongation at Break
Compressive Modulus
Flexural Strength
Flexural Modulus
Shear Strength
Fracture Toughness (K_IC)
Izod Impact, Notched
Hardness, Rockwell R
Hardness, Shore D
Same in both: Shear Modulus 5.5 GPa0.8 Msi · Compressive Strength 450 MPa65.3 ksi · Hardness, Rockwell M 110 HRM
Physical
Density and transition temperatures.
Glass Transition (Tg)
Water Absorption (24 h)
Water Absorption (Saturation)
Same in both: Density 1.85 g/cm³0.07 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Min Service Temperature
Heat Deflection Temp. @ 0.45 MPa
Limiting Oxygen Index
Max Service Temperature (short-term)
Same in both: Specific Heat Capacity 1,100 J/kg·K0.26 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 14 µm/m·K7.8 µin/in·°F · Heat Deflection Temp. @ 1.8 MPa 200°C392 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Volume Resistivity
Surface Resistivity
Dielectric Strength
Dielectric Constant (1 MHz)
Dissipation Factor (1 MHz)
Comparative Tracking Index (CTI)
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
UV / Weathering Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Polishability
Same in both: Weldability 0 / 100 · Formability (cold) 3 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Same in both: Embodied Carbon (primary production) 7 kg CO₂/kg · Embodied Water 200 L/kg24 gal/lb · Typical Recycled Content 0%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 0
Strength versus weight
Yield strength against density for every composite grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | G10-ESD | G11 |
|---|---|---|
| Default condition | Epoxy Matrix | Epoxy Matrix |
| Relative cost | $$$ Premium | $$$ Premium |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both are offered for CNC machining and Sheet metal. Both take the same 1 finish: Painting.
G10-ESD vs G11 — frequently asked
Is G11 stronger than G10-ESD?
Yes. G11 has a typical tensile strength of 340 MPa (49.3 ksi) against 300 MPa (43.5 ksi) for G10-ESD — about 13% more.
Which is cheaper, G10-ESD or G11?
Both sit in the same relative cost tier ($$$, premium); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, G10-ESD or G11?
G11, by a small margin. Both rate fair for machinability — 45/100 against 38/100 for G10-ESD.
Ready to make it?
Upload a CAD file and FabDigit prices the part in G10-ESD and G11 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.