G-3 vs LE
Composite · grade comparison
G-3 and LE are both composite grades. G-3 is the stronger of the two: tensile strength 250 MPa (36.3 ksi) against 95 MPa (13.8 ksi) for LE, about 163% more. LE is lighter (1.36 g/cm³ vs 1.85 g/cm³ for G-3) and G-3 is stiffer (18 GPa vs 7.5 GPa). On the shop floor, LE machines more easily (excellent vs fair).
G-3Choose it when strength drives the design.
LEChoose it when weight is the constraint, or when the part is machined in volume.
G-3 vs LE: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all composite grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all composite grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Compressive Strength
Compressive Modulus
Flexural Strength
Flexural Modulus
Shear Strength
Izod Impact, Notched
Hardness, Rockwell M
Same in both: Elongation at Break 1.5%
Physical
Density and transition temperatures.
Density
Glass Transition (Tg)
Water Absorption (24 h)
Water Absorption (Saturation)
Thermal
How each material carries heat and how hot it can run.
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Limiting Oxygen Index
Max Service Temperature (short-term)
Heat Deflection Temp. @ 1.8 MPa
Same in both: Thermal Conductivity 0.3 W/m·K0.17 BTU/hr·ft·°F · Min Service Temperature -50°C-58 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Dielectric Strength
Dielectric Constant (1 MHz)
Dissipation Factor (1 MHz)
Volume Resistivity
Same in both: Surface Resistivity 1×10¹¹ Ω · Comparative Tracking Index (CTI) 125 V
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
UV / Weathering Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Water
Same in both: Embodied Energy (primary production) 78 MJ/kg33,534 BTU/lb · Embodied Carbon (primary production) 4.5 kg CO₂/kg · Typical Recycled Content 0%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 0
Strength versus weight
Yield strength against density for every composite grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | G-3 | LE |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$ Premium | $$$ Premium |
| Min. machined wall | — | — |
| Best machined surface | — | — |
G-3 vs LE — frequently asked
Is G-3 stronger than LE?
Yes. G-3 has a typical tensile strength of 250 MPa (36.3 ksi) against 95 MPa (13.8 ksi) for LE — about 163% more.
Which is cheaper, G-3 or LE?
Both sit in the same relative cost tier ($$$, premium); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, G-3 or LE?
LE. Its machinability rates excellent (88/100) against fair (42/100) for G-3.
Ready to make it?
Upload a CAD file and FabDigit prices the part in G-3 and LE side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.