3Y-TZP vs 8Y-FSZ
Ceramic · grade comparison
3Y-TZP and 8Y-FSZ are both ceramic grades. 3Y-TZP is the stronger of the two: tensile strength 400 MPa (58 ksi) against 150 MPa (21.8 ksi) for 8Y-FSZ, about 167% more. 8Y-FSZ runs hotter in service (1,500°C vs 1,000°C continuous) and 3Y-TZP conducts heat better (2.5 W/m·K vs 2.2 W/m·K).
3Y-TZPChoose it when strength drives the design.
8Y-FSZChoose it when the part sees heat.
3Y-TZP vs 8Y-FSZ: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all ceramic grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all ceramic grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Compressive Strength
Flexural Strength
Shear Strength
Fracture Toughness (K_IC)
Hardness, Vickers
Hardness, Mohs
Elongation at Break
Same in both: Bulk Modulus 175 GPa25.4 Msi · Poisson's Ratio 0.3 · Hardness, Knoop 1,200 HK
Physical
Density and transition temperatures.
Density
Refractive Index
Light Transmission
Porosity
Same in both: Melting Point (Solidus) 2,700°C4,892 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Same in both: Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Dielectric Strength
Dielectric Constant (1 MHz)
Dissipation Factor (1 MHz)
Volume Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Corrosion Resistance 92 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Polishability
Same in both: Sintering / Firing Temperature 1,450°C2,642 °F
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 0%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 0
Strength versus weight
Yield strength against density for every ceramic grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 3Y-TZP | 8Y-FSZ |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
3Y-TZP vs 8Y-FSZ — frequently asked
Is 3Y-TZP stronger than 8Y-FSZ?
Yes. 3Y-TZP has a typical tensile strength of 400 MPa (58 ksi) against 150 MPa (21.8 ksi) for 8Y-FSZ — about 167% more.
Which is cheaper, 3Y-TZP or 8Y-FSZ?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
When should I choose 3Y-TZP over 8Y-FSZ?
Pick 3Y-TZP when strength drives the design. Pick 8Y-FSZ when the part sees heat.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 3Y-TZP and 8Y-FSZ side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.