3Y-TZP vs ATZ
Ceramic · grade comparison
3Y-TZP and ATZ are both ceramic grades. ATZ is harder — 1,400 HV against 1,250 HV for 3Y-TZP — which matters for wear surfaces and threads. ATZ is lighter (5.5 g/cm³ vs 6.05 g/cm³ for 3Y-TZP) and ATZ is stiffer (240 GPa vs 210 GPa).
ATZChoose it when surface hardness matters, or when weight is the constraint.
3Y-TZP vs ATZ: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all ceramic grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all ceramic grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Compressive Strength
Flexural Strength
Fracture Toughness (K_IC)
Hardness, Vickers
Hardness, Knoop
Elongation at Break
Same in both: Tensile Strength (Ultimate) 400 MPa58 ksi · Shear Strength 350 MPa50.8 ksi · Hardness, Mohs 8.5
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Refractive Index
Light Transmission
Same in both: Porosity 0.1%
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Same in both: Max Service Temperature (continuous) 1,000°C1,832 °F · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Dielectric Strength
Dielectric Constant (1 MHz)
Same in both: Electrical Resistivity 1×10⁹ Ω·m3.94×10¹⁶ µΩ·in · Dissipation Factor (1 MHz) 0.002 · Volume Resistivity 1×10¹¹ Ω·cm
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Polishability
Sintering / Firing Temperature
Same in both: Machinability 4 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Same in both: Embodied Water 300 L/kg35.9 gal/lb · Typical Recycled Content 0%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every ceramic grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 3Y-TZP | ATZ |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
3Y-TZP vs ATZ — frequently asked
What is the difference between 3Y-TZP and ATZ?
3Y-TZP and ATZ are both ceramic grades. ATZ is harder — 1,400 HV against 1,250 HV for 3Y-TZP — which matters for wear surfaces and threads. ATZ is lighter (5.5 g/cm³ vs 6.05 g/cm³ for 3Y-TZP) and ATZ is stiffer (240 GPa vs 210 GPa).
Which is cheaper, 3Y-TZP or ATZ?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
When should I choose 3Y-TZP over ATZ?
Pick ATZ when surface hardness matters, or when weight is the constraint.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 3Y-TZP and ATZ side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.